Oxyfluorination of wood-fiber reinforced thermoplastic composites to improve adhesion

被引：0
|
作者：
Laborie, Marie-Pierre [1 ]
Gupta, Barun [2 ]
机构：
[1] Washington State University, Department of Civil and Environmental Engineering, Wood Materials and Engineering Laboratory, Pullman, WA, United States
[2] Department of Forest Resources, Pennsylvania State University, State College, PA, United States
来源：
Journal of Adhesion | 2008年 / 84卷 / 10期
关键词：
Oxyfluorination was evaluated on a series of wood-fiber reinforced thermoplastic composite (WPCs) formulations as a means to improve the adhesion of a water-based acrylic coating. The oxyfluorination increased the acrylic coating peel load to WPCs by 179%; yielding adhesion levels higher than those obtained on control maple. For oxyfluorinated surfaces; the WPC formulation had a significant impact on the acrylic coating paint. Formulations without maleic anhydride polypropylene coupling agent developed better adhesion than formulations with the coupling agent. Formulations with polypropylene also performed better than formulations with high density polyethylene and so did formulations with pine compared with those with maple. Interestingly; the adhesion improvement imparted by oxyfluorination was higher for those formulations that were least amenable to bonding with the acrylic coating; i.e; those containing the coupling agent and high density polyethylene. Contact angle measurements and ATR-FTIR spectroscopy indicated that oxyfluorination improved wettability with polar liquids by generating new oxygenated groups on the surface. A moderate positive linear relationship (r2 = 0.5) was established between the carbonyl/C-H stretch band intensity ratio I1650cm-1 /I2915cm-1 in the infrared spectra of oxyfluorinated WPCs and the coating peel strength. It is; therefore; proposed that oxyfluorination improves the adhesion properties of WPCs by oxidizing the surface; and by increasing wettability with polar liquids; thus allowing the development of stronger interfacial forces;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：830 / 846
相关论文
共 50 条
  • [31] Mechanical properties of wood-fiber reinforced polypropylene composites: Effect of a novel compatibilizer with isocyanate functional group
    Karmarkar, Ajay
    Chauhan, S. S.
    Modak, Jayant M.
    Chanda, Manas
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2007, 38 (02) : 227 - 233
  • [32] Sorption and diffusion of carbon dioxide in wood-fiber/polystyrene composites
    Doroudiani, S
    Chaffey, CE
    Kortschot, MT
    JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 2002, 40 (08) : 723 - 735
  • [33] WOOD FIBER REINFORCED COMPOSITES
    KLASON, C
    KUBAT, J
    GATENHOLM, P
    ACS SYMPOSIUM SERIES, 1992, 489 : 82 - 98
  • [34] APPROACHES TO IMPROVE THE PROPERTIES OF WOOD FIBER-REINFORCED CEMENTITIOUS COMPOSITES
    LIN, X
    SILSBEE, MR
    ROY, DM
    KESSLER, K
    BLANKENHORN, PR
    CEMENT AND CONCRETE RESEARCH, 1994, 24 (08) : 1558 - 1566
  • [35] Effect of fiber length on processing and properties of extruded wood-fiber/HDPE composites
    Migneault, Sebastien
    Koubaa, Ahmed
    Erchiqui, Fouad
    Chaala, Abdelkader
    Englund, Karl
    Krause, Cornelia
    Wolcott, Michael
    JOURNAL OF APPLIED POLYMER SCIENCE, 2008, 110 (02) : 1085 - 1092
  • [36] Morphology and properties of wood-fiber reinforced blends of recycled polystyrene and polyethylene
    Simonsen, J
    Rials, TG
    JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 1996, 9 (03) : 292 - 302
  • [37] Recycling of fiber reinforced composites with a focus on thermoplastic composites
    Bernatas, Rebecca
    Dagreou, Sylvie
    Despax-Ferreres, Auriane
    Barasinski, Anais
    CLEANER ENGINEERING AND TECHNOLOGY, 2021, 5
  • [38] Effects of impact modifiers on the properties of rigid PVC/wood-fiber composites
    Mengeloglu, F
    Matuana, LM
    King, JA
    ANTEC 2000: SOCIETY OF PLASTICS ENGINEERS TECHNICAL PAPERS, CONFERENCE PROCEEDINGS, VOLS I-III, 2000, : 3407 - 3411
  • [39] Effects of impact modifiers on the properties of rigid PVC/wood-fiber composites
    Mengeloglu, F
    Matuana, LM
    King, JA
    JOURNAL OF VINYL & ADDITIVE TECHNOLOGY, 2000, 6 (03): : 153 - 157
  • [40] Wood-Fiber/High-Density-Polyethylene composites: Compounding process
    Lu, JZ
    Wu, Q
    Negulescu, II
    JOURNAL OF APPLIED POLYMER SCIENCE, 2004, 93 (06) : 2570 - 2578
12345