Depth dependence of elastic grain interaction and mechanical stress: Analysis by x-ray diffraction measurements at fixed penetration/information depths

被引：0
|
作者：
Kumar, A. [1 ]
Welzel, U. [1 ]
Mittemeijer, E.J. [1 ]
机构：
[1] Max Planck Institute for Metals Research, Heisenbergstrasse 3, D-70569 Stuttgart, Germany
来源：
Journal of Applied Physics | 2006年 / 100卷 / 11期
关键词：
Gradients of the type of elastic grain interaction and the (residual) internal state of stress were determined. This was possible by the application of x-ray diffraction stress measurements at various fixed penetration/ information depths. The analysis was applied to nickel films of thicknesses 2 and 4 μm. Surface anisotropy was considered as source of direction-dependent (anisotropic) elastic grain interaction. It was found that only a small gradient of the state of stress; but a pronounced gradient of the grain interaction constraints; prevails in the investigated specimens. Thereby the evidence for the depth dependence of the so-called surface anisotropy was obtained. © 2006 American Institute of Physics;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Depth dependence of elastic grain interaction and mechanical stress: Analysis by x-ray diffraction measurements at fixed penetration/information depths
    Kumar, A.
    Welzel, U.
    Mittemeijer, E. J.
    JOURNAL OF APPLIED PHYSICS, 2006, 100 (11)
  • [2] A method for the non-destructive analysis of gradients of mechanical stresses by X-ray diffraction measurements at fixed penetration/information depths
    Kumar, A.
    Welzel, U.
    Mittemeijer, E. J.
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2006, 39 : 633 - 646
  • [3] Mechanical stress gradients in thin films analyzed employing X-ray diffraction measurements at constant penetration/information depths
    Wohlschloegel, M.
    Baumann, W.
    Welzel, U.
    Mittemeijer, E. J.
    RESIDUAL STRESSES VII, 2006, 524-525 : 19 - 24
  • [4] An X-ray diffraction method to determine stress at constant penetration/information depth
    Kumar, A.
    Welzel, U.
    Wohlschloegel, Markus
    Baumann, W.
    Mittemeijer, E. J.
    RESIDUAL STRESSES VII, 2006, 524-525 : 13 - 18
  • [5] The dependence of X-ray elastic constants with respect to the penetration depth
    Mareau, Charles
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2023, 56 : 1446 - 1455
  • [6] Measurement of X-ray diffraction-line broadening induced by elastic mechanical grain interaction
    Koker, M. K. A.
    Welzel, U.
    Mittemeijer, E. J.
    JOURNAL OF APPLIED CRYSTALLOGRAPHY, 2014, 47 : 391 - 401
  • [7] Measurement of X-ray diffraction-line broadening induced by elastic mechanical grain interaction
    Mittemeijer, E.J. (e.j.mittemeijer@is.mpg.de), 1600, International Union of Crystallography, 5 Abbey Road, Chester, CH1 2HU, United Kingdom (47):
  • [8] X-ray measurements of the depth dependence of stress in gold films
    Brennan, S
    Munkholm, A
    Leung, OS
    Nix, WD
    PHYSICA B, 2000, 283 (1-3): : 125 - 129
  • [9] Controlled depth penetration X-ray diffraction measurement
    Bolle, B
    Tidu, A
    Jolly, L
    Valot, C
    Laruelle, C
    Heizmann, JJ
    TEXTURES OF MATERIALS, PTS 1 AND 2, 2002, 408-4 : 233 - 238
  • [10] ORIENTATION DEPENDENCE OF THE EFFECTIVE DEPTH OF X-RAY PENETRATION
    TOMOV, I
    PHYSICA STATUS SOLIDI A-APPLIED RESEARCH, 1986, 98 (01): : 43 - 50
12345