Preparation and microstructure analysis of CaO-MgO-SiO2 steel-slag ceramics

被引：0
|
作者：
Zhao, Li-Hua [1 ,2 ]
Cang, Da-Qiang [1 ,2 ]
Liu, Pu [1 ]
Bai, Hao [1 ,2 ]
Tang, Qi [3 ]
机构：
[1] State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China
[2] School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
[3] Foshan Oceano Ceramic Co. Ltd., Foshan 528000, China
来源：
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2011年 / 33卷 / 08期
关键词：
Bending strength - Scanning electron microscopy - X ray diffraction analysis - Electron probe microanalysis - Magnesia - Silica - Slags - Microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A ceramic with stable and good performances was synthesized by designing the composition of the CaO-MgO-SiO2 system with steel slag as one of ceramic raw materials. Its bending strength can reach up to 99.84 MPa. The ceramic samples were tested and analyzed by scanning electron microscopy (SEM), electron probe microanalysis (EPMA) and X-ray diffraction analysis (XRD). The results show that when the content of steel slag is 40% the dominated crystal phase in the ceramic is a solid solution of diopside and ferric diopside, but when the content of steel slag is higher than 65% the dominated crystal phases are akermanite and diopside. It is indicated that synthesizing a ceramic with steel slag is a promising technology for the utilization of steel slag with high added values.
引用
收藏
页码：995 / 1000
相关论文
共 50 条
  • [41] Corrosion modeling of magnesia aggregates in contact with CaO-MgO-SiO2 slags
    Zhang, Wenxuan
    Huang, Ao
    Zou, Yongshun
    Gu, Huazhi
    Fu, Lvping
    Li, Guangqiang
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2020, 103 (03) : 2128 - 2136
  • [42] THERMODYNAMICS OF WATER-VAPOR DISSOLUTION IN CAO-MGO-SIO2 SLAGS
    SOSINSKY, DJ
    MAEDA, M
    MCLEAN, A
    JOURNAL OF METALS, 1983, 35 (12): : 111 - 111
  • [43] Three routes for the synthesis of the bioceramic powder of the CaO-MgO-SiO2 system
    Yamagata, Chieko
    Leme, Daniel Rezende
    Rodrigues, Vanessa Galvao
    Eretides, Gabriel Trindade
    Rodas, Andrea Cecilia Dorion
    CERAMICS INTERNATIONAL, 2022, 48 (07) : 9681 - 9691
  • [44] Glasses and glass-ceramics in the CaO-MgO-SiO2 system: Diopside containing compositions-A brief review
    Tulyaganov, Dilshat U.
    Dimitriadis, Konstantinos
    Agathopoulos, Simeon
    Fernandes, Hugo R.
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2023, 612
  • [45] Effect of (CaO + MgO)/SiO2 ratio on crystallisation and properties of slag glass-ceramics
    Liu, Z. B.
    Zong, Y. B.
    Ma, H. Y.
    Dai, W. B.
    Li, S. H.
    ADVANCES IN APPLIED CERAMICS, 2014, 113 (07) : 411 - 418
  • [46] Oxidation-reduction equilibria of vanadium in CaO-SiO2, CaO-Al2O3-SiO2 and CaO-MgO-SiO2 melts
    H. Farah
    M. Brungs
    Journal of Materials Science, 2003, 38 : 1885 - 1894
  • [47] Oxidation-reduction equilibria of vanadium in CaO-SiO2, CaO-Al2O3-SiO2 and CaO-MgO-SiO2 melts
    Farah, H
    Brungs, M
    JOURNAL OF MATERIALS SCIENCE, 2003, 38 (09) : 1885 - 1894
  • [48] Forecast of Crystallizing Phases and Modeling of Chemical Interaction in the System CaO-MgO-SiO2
    Garkushin, I. K.
    Lavrent'eva, O. V.
    Shterenberg, A. M.
    GLASS PHYSICS AND CHEMISTRY, 2023, 49 (02) : 121 - 128
  • [49] Composite bone graft of CaO-MgO-SiO2 glass-ceramics and CaSO4 ceramics for boosting bone formation rate
    Hung, Guan-Yi
    Wang, Chi-Yun
    Hsiao, Hui-Yi
    Tu, Chi-Shun
    Mana-ay, Haidee
    Chen, Ching-Ting
    Lai, Po-Liang
    Feng, Kuei-Chih
    Chen, Pin-Yi
    JOURNAL OF MATERIALS CHEMISTRY B, 2024, 12 (26) : 6394 - 6409
  • [50] The compound merwinite (3CaO MgO2SiO(2)) and its stability relations within the system CaO-MgO-SiO2 (Preliminary report)
    Osborn, EF
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1943, 26 (10) : 321 - 332
12345