Preparation and microstructure analysis of CaO-MgO-SiO2 steel-slag ceramics

被引：0
|
作者：
Zhao, Li-Hua [1 ,2 ]
Cang, Da-Qiang [1 ,2 ]
Liu, Pu [1 ]
Bai, Hao [1 ,2 ]
Tang, Qi [3 ]
机构：
[1] State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China
[2] School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
[3] Foshan Oceano Ceramic Co. Ltd., Foshan 528000, China
来源：
Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing | 2011年 / 33卷 / 08期
关键词：
Bending strength - Scanning electron microscopy - X ray diffraction analysis - Electron probe microanalysis - Magnesia - Silica - Slags - Microstructure;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
A ceramic with stable and good performances was synthesized by designing the composition of the CaO-MgO-SiO2 system with steel slag as one of ceramic raw materials. Its bending strength can reach up to 99.84 MPa. The ceramic samples were tested and analyzed by scanning electron microscopy (SEM), electron probe microanalysis (EPMA) and X-ray diffraction analysis (XRD). The results show that when the content of steel slag is 40% the dominated crystal phase in the ceramic is a solid solution of diopside and ferric diopside, but when the content of steel slag is higher than 65% the dominated crystal phases are akermanite and diopside. It is indicated that synthesizing a ceramic with steel slag is a promising technology for the utilization of steel slag with high added values.
引用
收藏
页码：995 / 1000
相关论文
共 50 条
  • [21] Effects of CaO and Fe2O3 on the Microstructure and Mechanical Properties of SiO2-CaO-MgO-Fe2O3 Ceramics from Steel Slag
    Zhao, Lihua
    Li, Yu
    Zhang, Lingling
    Cang, Daqiang
    ISIJ INTERNATIONAL, 2017, 57 (01) : 15 - 22
  • [22] SOLUBILITY OF CAO IN MGO AND ITS EFFECT ON CAO-MGO-SIO2 SYSTEM AT 1800 DEGREES C
    SPENCER, DRF
    BEAMOND, TW
    COLEMAN, DS
    TRANSACTIONS AND JOURNAL OF THE BRITISH CERAMIC SOCIETY, 1971, 70 (01): : 31 - &
  • [23] Synthesis and characterization of novel multiphase bioactive glass-ceramics in the CaO-MgO-SiO2 system
    Chen, Xianchun
    Liao, Xiaoming
    Huang, Zhongbing
    You, Panli
    Chen, Chun
    Kang, Yunqing
    Yin, Guangfu
    JOURNAL OF BIOMEDICAL MATERIALS RESEARCH PART B-APPLIED BIOMATERIALS, 2010, 93B (01) : 194 - 202
  • [24] CaO-MgO-SiO2 glass ceramics: Transferred arc plasma (TAP) synthesis and microstructural characterization
    Yoganand, C. P.
    Selvarajan, V.
    Lusvarghi, Luca
    CURRENT APPLIED PHYSICS, 2009, 9 (04) : 839 - 846
  • [25] Effects of CaO/MgO Ratios on Crystallization Behavior of CaO-MgO-SiO2 System Ceramic Fibers
    Liu Hao
    Wang Xitang
    Zhang Baoguo
    Wang Zhoufu
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 1200 - 1202
  • [26] Silver diffusion and mechanism of CaO-MgO-SiO2 glass ceramics in millimeter-wave properties
    Feng, Kuei-Chih
    Chu, Ming-Wei
    Lu, Chun-An
    Iizuka, Yoshiyuki
    Chen, Pin-Yi
    Tu, Chi-Shun
    Chen, Cheng-Sao
    Chien, R. R.
    Tsao, Chung-Ya
    CERAMICS INTERNATIONAL, 2020, 46 (05) : 5634 - 5640
  • [27] ADDITIONAL PHASE EQUILIBRIUM DATA FOR THE SYSTEM CAO-MGO-SIO2
    RICKER, RW
    OSBORN, EF
    JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1954, 37 (03) : 133 - 139
  • [28] THE SOLUBILITY OF WATER-VAPOR IN CAO-MGO-SIO2 SLAGS
    MAEDA, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1984, 70 (12): : S881 - S881
  • [29] THE CATIONIC EFFECT ON PROPERTIES AND STRUCTURE OF CaO-MgO-SiO2 MELTS
    Han, Yong-Uk
    Min, Dong Joon
    ADVANCES IN MOLTEN SLAGS, FLUXES, AND SALTS, 2016, : 501 - 509
  • [30] TEPLOTNE ROZTAZNOSTI MINERALOV V SUSTAVE CAO-MGO-SIO2
    KANCLIR, E
    AMBRUZ, V
    CHEMICKE ZVESTI, 1965, 19 (01): : 51 - &
12345