Effect of hot plastic deformation and heat treatment on microstructure and properties of TC11 titanium alloy

被引：0
|
作者：
Cui, Xi-Ping [1 ]
Geng, Lin [1 ]
Song, Yi-Biao [1 ]
Feng, Yi-Cheng [1 ]
Wang, Qing-Wei [1 ]
机构：
[1] School of Materials Science and Engineering, Harbin Institute of Technology, Harbin 150001, China
来源：
Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment | 2009年 / 30卷 / 02期
关键词：
Effect of heat treatments - Elongated grains - Equi-axed grains - Equiaxed microstructures - Microstructure and properties - Microstructure observation - TC11 titanium alloys - Ultimate tensile strength;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Effect of heat treatment after compression at 1000°C on microstructure and tensile properties of TC11 titanium alloy was investigated by means of optical microscope, scanning electron microscopy and tensile tests. Microstructure observation of the compressed and water-quenched samples indicates that the elongated equiaxed grains tend to recover to equiaxed shape, and the tendency of the elongated grains to recover to equiaxed shape is more obviously and the volume fraction of equiaxed alpha phase increases after water quenching plus aging and duplex annealing, and meanwhile acicular alpha phases are precipitated from beta phases (β). The ultimate tensile strength and yield strength of the specimens treated by water quenching plus aging increase to 1300MPa and to 1152MPa, respectively. That is to say, σband σ0.2increase by 14.8% and 16.8% compared with that the water-quenched alloy, respectively. The deformed and water-quenched TC11 titanium alloy after duplex annealing exhibits excellent mechanical properties with tensile strength of 1176MPa and elongation of 15.95%.
引用
收藏
页码：89 / 92
相关论文
共 50 条
  • [41] Surface ionic bombarding treatment of TC11 titanium alloy
    Tang, Guangxin
    Zhu, Zhangxiao
    Ding, Lianzhen
    Shen, Wanci
    2002, Press of Tsinghua University (42):
  • [42] Evolution of Microstructure and Hardness of TC11 Titanium Alloy under Different Electroshocking Treatment Directions
    Liu, Chang
    Wu, Yongjian
    Wang, Haoxing
    Yin, Fei
    Qian, Dongsheng
    Wang, Liqiang
    Xie, Lechun
    Hua, Lin
    METALS, 2023, 13 (08)
  • [43] Microstructure evolution and mechanical property response of TC11 titanium alloy under electroshock treatment
    Liu, Chang
    Xie, Lechun
    Qian, Dongsheng
    Hua, Lin
    Wang, Liqiang
    Zhang, Lai-Chang
    MATERIALS & DESIGN, 2021, 198
  • [44] Study on the microstructure and impact toughness of TC11 titanium alloy by a novel electromagnetic shocking treatment
    Li, Yunfeng
    Wang, Fanglei
    Sun, Qian
    Qian, Dongsheng
    Song, Yanli
    Hua, Lin
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2023, 876
  • [45] Effect of Heat Treatment on Microstructure and Mechanical Properties of Titanium Recycled by Severe Plastic Deformation
    McDonald, D. T.
    Davies, A. J.
    Luo, P.
    Zhu, S. M.
    Palanisamy, S.
    Dargusch, M. S.
    Xia, K.
    TI-2011: PROCEEDINGS OF THE 12TH WORLD CONFERENCE ON TITANIUM, VOL I, 2012, : 497 - 501
  • [46] Microstructure simulation of TC11 titanium alloy during disk forging processes
    Taiyuan University of Science and Technology, Taiyuan 030024, China
    不详
    Cailiao Gongcheng, 2009, 12 (30-33):
  • [47] Lamellar Disintegration Mechanism of TC11 Titanium Alloy during Hot Compression
    郑佩琦
    黄陆军
    Journal of Wuhan University of Technology(Materials Science), 2009, (S1) : 44 - 46
  • [48] Mechanical behaviors and microstructural characteristics of TC11 alloy during hot deformation
    Sun, XJ
    Bai, BZ
    Gu, JL
    Chen, NP
    RARE METALS, 2000, 19 (02) : 101 - 109
  • [49] Superplastic deformation mechanism of titanium alloy TC11 at maximum m value
    School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063, China
    不详
    Hangkong Xuebao, 2009, 2 (357-361): : 357 - 361
  • [50] Effect of gas pressure on microstructure and mechanical properties of TC11 titanium alloy during supersonic fine particle bombardment
    Wu, Yong-li
    Xiong, Yi
    Chen, Zheng-ge
    Liu, Wei
    Zhang, Xin
    Wang, Shu-bo
    Cao, Wei
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2023, 33 (08) : 2379 - 2394
12345