Lamellar Disintegration Mechanism of TC11 Titanium Alloy during Hot Compression

被引：0
|
作者：
郑佩琦 [1 ]
黄陆军 [1 ]
机构：
[1] School of Materials Science & Engineering,Harbin Institute of Technology
来源：
Journal of Wuhan University of Technology(Materials Science) | 2009年 / S1期
关键词：
TC11 titanium alloy; hot compression; lamellar microstructure; lamellar disintegration;
D O I：
暂无
中图分类号：
TG146.23 [];
学科分类号：
080502 ;
摘要：
TC11 titanium alloy samples with lamellar microstructrue were compressed on a Gleeble 1500D Simulator.Compression tests were carried out at 950 ℃ and a strain rate of 0.1 s-1 with height reduction of 20%,40% and 60%,respectively.Microstruture of the compressed TC11 alloy was obeserved and analyzed by optical microscopy(OM),transmission electron microscope(TEM),electron back-scattered diffraction(EBSD).The lamellar disintegration mechanism of the TC11 titanium alloy was deduced.The results indicated that the compressive deformation promoted the phase transformation in bi-phase area.βphase layers were formed along the gliding planes inα phase,and α slivers were disintegrated into many small flakes through theα/βinterface slipping.
引用
收藏
页码：44 / 46
页数：3
相关论文
共 50 条
  • [1] Hot deformation globularization kinetic processes of TC11 titanium alloy with lamellar structure
    Chen, Hui-Qin
    Cao, Chun-Xiao
    Guo, Ling
    Lin, Hai
    Hangkong Cailiao Xuebao/Journal of Aeronautical Materials, 2009, 29 (01): : 37 - 42
  • [2] Hot deformation mechanism and microstructure evolution of TC11 titanium alloy in β field
    陈慧琴
    曹春晓
    郭灵
    林海
    Transactions of Nonferrous Metals Society of China, 2008, (05) : 1021 - 1027
  • [3] Hot deformation mechanism and microstructure evolution of TC11 titanium alloy in β field
    Chen Hui-qin
    Cao Chun-xiao
    Guo Ling
    Lin Hai
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (05) : 1021 - 1027
  • [4] Globularization Mechanisms during Hot Deformation Processes of TC11 Alloy with Lamellar Structure
    Chen Huiqin
    Cao Chunxiao
    Guo Lingo
    Lin Hai
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 (03) : 421 - 425
  • [5] Globularization mechanisms during hot deformation processes of TC11 alloy with lamellar structure
    Chen, Huiqin
    Cao, Chunxiao
    Guo, Ling
    Lin, Hai
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2009, 38 (03): : 421 - 425
  • [6] Subtransus deformation mechanisms of TC11 titanium alloy with lamellar structure
    宋鸿武
    张士宏
    程明
    Transactions of Nonferrous Metals Society of China, 2010, 20 (11) : 2168 - 2173
  • [7] Deformation behavior in isothermal compression of the TC11 titanium alloy
    Zhang, X. Y.
    Li, M. Q.
    Li, H.
    Luo, J.
    Su, S. B.
    Wang, H.
    MATERIALS & DESIGN, 2010, 31 (06) : 2851 - 2857
  • [8] Subtransus deformation mechanisms of TC11 titanium alloy with lamellar structure
    Song Hong-wu
    Zhang Shi-hong
    Cheng Ming
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 (11) : 2168 - 2173
  • [9] High temperature deformation behavior and optimization of hot compression process parameters in TC11 titanium alloy with coarse lamellar original microstructure
    Lu, Shi-qiang
    Li, Xin
    Wang, Ke-lu
    Dong, Xian-juan
    Fu, M. W.
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2013, 23 (02) : 353 - 360
  • [10] Flow softening and microstructural evolution of TC11 titanium alloy during hot deformation
    Zong, Y. Y.
    Shan, D. B.
    Xu, M.
    Lv, Y.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2009, 209 (04) : 1988 - 1994
12345