Analysis of brazing joints of CMCs/TC4 by Ag-Cu-Ti-Si filler

被引：0
|
作者：
Aerospace Research Institute of Material and Processing Technology, Beijing 100076, China [1 ]
机构：
来源：
Cailiao Kexue yu Gongyi | 2009年 / SUPPL. 1卷 / 40-43期
关键词：
Silver alloys - Filler metals - Fillers - Scanning electron microscopy - Silicon alloys - Titanium alloys - Brazing - Copper alloys;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
C/SiC CMCs and TC4 alloy are brazed successfully by Ag-Cu-Ti-Si filler in this research. The shear strength of the joints are tested, the interface microstructure and fracture appearance are observed by SEM method, and the microstructure is analyzed by EDS. The results show that the max. value of shear strength is 118.2 MPa, by using Ag-Cu-Ti-Si filler(Ti:Ti=1:1, wt%), while the brazing parameter is 900°C/10min.
引用
下载
收藏
相关论文
共 50 条
  • [1] Vacuum brazing ZSCf composite ceramics to TC4 alloy with Ag-Cu filler
    Wang, Wei
    Liu, Yaping
    Wang, Gang
    Tan, Caiwang
    Cao, Wei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2020, 9 (04): : 8627 - 8635
  • [2] Brazing ZTA ceramic to TC4 alloy using Ag-Cu filler metal
    Wang X.
    Cao J.
    Dai X.
    Feng J.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (03): : 47 - 51and58
  • [3] Effect of Brazing Clearance on the Microstructure and Mechanical Properties of TC4/TC4 Joints Brazed in Vacuum with Ti–Zr–Ni Filler Metal
    Min Liang
    Youqiong Qin
    Danfeng Zhang
    Feng Zhao
    Journal of Materials Engineering and Performance, 2023, 32 : 2973 - 2982
  • [4] Microstructure and mechanical properties of joints prepared by vacuum brazing on TC4 titanium alloy with Ag as filler metal
    Peng, Yu
    Li, Jinglong
    Du, Yajie
    Xiong, Jiangtao
    Shi, Junmiao
    VACUUM, 2021, 187
  • [5] Effect of Brazing Clearance on the Microstructure and Mechanical Properties of TC4/TC4 Joints Brazed in Vacuum with Ti-Zr-Ni Filler Metal
    Liang, Min
    Qin, Youqiong
    Zhang, Danfeng
    Zhao, Feng
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (07) : 2973 - 2982
  • [6] Brazing ZrO 2 ceramic and TC4 alloy using Ag-Cu+WC composite filler
    Wang Z.
    Cao J.
    Dai X.
    Feng J.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (01): : 5 - 9
  • [7] Activating brazing of Gr/2024Al composite material to TC4 titanium alloy with Ag-Cu-Sn-Ti filler
    Shi, Junmiao
    Zhang, Lixia
    Li, Hongwei
    Tian, Xiaoyu
    Feng, Jicai
    Hanjie Xuebao/Transactions of the China Welding Institution, 2014, 35 (11): : 31 - 34
  • [8] Brazing of carbon fiber reinforced SiC composite and TC4 using Ag-Cu-Ti active brazing alloy
    Xiong, Jin Hui
    Huang, Ji Hua
    Zhang, Hua
    Zhao, Xing Ke
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2010, 527 (4-5): : 1096 - 1101
  • [9] Morphology and strength of TC4/TC4 joint with 72Ag-28Cu filler metal
    Jiang, CY
    Wu, MF
    Yu, C
    Liang, C
    RARE METAL MATERIALS AND ENGINEERING, 2003, 32 (04) : 295 - 297
  • [10] Microstructure and mechanical properties of TC4 joints brazed with Ti–Zr–Cu–Sn amorphous filler alloy
    Hui-Hui Zhang
    Zhen-Duo Cui
    Sheng-Li Zhu
    Shi-Wei Guo
    Xian-Jin Yang
    Akihisa Inoue
    Rare Metals, 2021, 40 (07) : 1881 - 1889
12345