Bending Deformation and Microstructure Evolution of Bainite Rail during Cooling Process after Rolling

被引:0
|
作者
Cen, Yaodong [1 ]
Chen, Lin [1 ]
Bao, Xirong [1 ]
Li, Xiaona [1 ]
机构
[1] School of Materials and Metallurgy, Inner Mongolia University of Science and Technology, Baotou,014010, China
关键词
After-heat treatment - Bainitic transformations - Straightening;
D O I
10.3901/JME.2024.14.139
中图分类号
学科分类号
摘要
Due to the asymmetric cross-sectional characteristics of turnout rail, the rolling, heat treatment and straightening processes are very complex and the production is very difficult. In view of the flatness and residual stress of turnout bainite rail, the CCT curve was measured by Gleeble-1500, the microstructure under different cooling rates was observed by SEM, and the simulation calculation of controlled cooling before and between phase transformation was carried out by finite element software. The results show that with the increase of cooling rate, when the undeformed austenite is continuously cooled at the cooling rate of 0.05-1 ℃/s, the microstructure gradually changes from granular bainite to martensite. When the deformed austenite is continuously cooled at the cooling rate of 0.2-2 ℃/s, the microstructure gradually changes from granular bainite to a large amount of martensite + a little of lath bainite; Controlled cooling in phase change section adopts cooling the center of rail head surface to 500 ℃, then cooling from 500 ℃ to 300 ℃ (cooling rate of rail surface is 0.4 ℃/s), and then air cooling to room temperature to obtain bainite volume of 35.6 %, The final maximum tensile stress, maximum compressive stress, bending deflection in Y direction and Z direction meet the requirements. Before phase transformation, the center of rail head surface is cooled to 500 ℃ (the cooling rate of rail head upper surface, non working side and rail waist is 3 ℃/s, and the working side of rail head is 3.5 ℃/s). After air cooling from 500 ℃ to room temperature, 99.3% bainite structure can be obtained. The final residual stress value and bending deflection meet the requirements. The purpose of reducing bending deformation and residual stress after straightening is realized by controlling cooling. © 2024 Chinese Mechanical Engineering Society. All rights reserved.
引用
收藏
页码:139 / 152
相关论文
共 50 条
  • [31] Evolution of the Microstructure and Mechanical Properties of Copper during the Rolling–ECAP Process
    S. N. Lezhnev
    I. E. Volokitina
    E. A. Panin
    A. V. Volokitin
    Physics of Metals and Metallography, 2020, 121 : 689 - 693
  • [32] Multi-Scale Modeling of Microstructure Evolution during Multi-Pass Hot-Rolling and Cooling Process
    Lin, Xian
    Zou, Xinyi
    An, Dong
    Krakauer, Bruce W.
    Zhu, Mingfang
    MATERIALS, 2021, 14 (11)
  • [33] CuAl alloy microstructure evolution during ordering after deformation
    Antonova, OV
    Boyarshinova, TS
    Volkov, AY
    Greenberg, BA
    Sakhanskaya, IN
    Hug, G
    IZVESTIYA AKADEMII NAUK SERIYA FIZICHESKAYA, 1999, 63 (07): : 1347 - 1351
  • [34] Influence of the annealing cooling rate on the microstructure evolution and deformation behaviours in the cold ring rolling of medium steel
    Wu, M.
    Hua, L.
    Shao, Y. C.
    Zhou, Q. J.
    MATERIALS & DESIGN, 2011, 32 (04) : 2292 - 2300
  • [35] EFFECT OF COOLING IN THE PROCESS OF DEFORMATION ON RETENTION OF THE EFFECT OF HTMT DURING HOT ROLLING.
    Podgaiskii, M.S.
    Khlestov, V.M.
    Metal Science and Heat Treatment (English translation of Metallovedenie i Termicheskaya Obrabotka Metallov), 1979, 21 (7-8): : 605 - 607
  • [36] EFFECT OF COOLING IN THE PROCESS OF DEFORMATION ON RETENTION OF THE EFFECT OF HTMT DURING HOT-ROLLING
    PODGAISKII, MS
    KHLESTOV, VM
    METAL SCIENCE AND HEAT TREATMENT, 1979, 21 (7-8) : 605 - 607
  • [37] Mechanical Properties and Microstructure Evolution During Bending–Unbending Deformation of Pure Titanium Sheet
    Daming Nie
    Zhen Lu
    Kaifeng Zhang
    Journal of Materials Engineering and Performance, 2018, 27 : 705 - 713
  • [38] EVOLUTION OF THE MICROSTRUCTURE IN THE HOT-ROLLING PROCESS
    PIETRZYK, M
    KEDZIERSKI, Z
    KUSIAK, H
    MADEJ, W
    LENARD, JG
    STEEL RESEARCH, 1993, 64 (11): : 549 - 556
  • [39] Analysis of deformation and microstructure evolution during the cogging process of Waspaloy alloy
    Kukuryk, Marcin
    Winczek, Jerzy
    Gucwa, Marek
    XXIII POLISH-SLOVAK SCIENTIFIC CONFERENCE ON MACHINE MODELLING AND SIMULATIONS (MMS 2018), 2019, 254
  • [40] Evolution of the Microstructure and Mechanical Properties of Copper during the Rolling-ECAP Process
    Lezhnev, S. N.
    Volokitina, I. E.
    Panin, E. A.
    Volokitin, A. V.
    PHYSICS OF METALS AND METALLOGRAPHY, 2020, 121 (07): : 689 - 693