Evolution of the Microstructure and Mechanical Properties of Copper during the Rolling-ECAP Process

被引：6

作者：

Lezhnev, S. N. ^{[1
]}

Volokitina, I. E. ^{[1
]}

Panin, E. A. ^{[1
]}

Volokitin, A. V. ^{[1
]}

机构：

[1] Rudnyi Ind Inst, Rudnyi 111500, Kazakhstan

来源：

PHYSICS OF METALS AND METALLOGRAPHY | 2020年 / 121卷 / 07期

关键词：

pressing; rolling; mechanical properties; microstructure; copper; PRESSURE; STEEL;

D O I：

10.1134/S0031918X20070054

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The effect of the new combined rolling-pressing technique of plastic deformation on the structure and mechanical properties of copper has been investigated in this work. The deformation was performed at room temperature and there were three cycles. Rolling-pressing technique was shown to significantly refine the structure of the commercial-purity copper. The strength of the copper workpieces increased by two times after three passes. The ultimate tensile strength and the yield strength increased from 235 to 482 MPa and from 198 to 405 MPa, respectively. The relative elongation and the relative reduction decreased by 8% and 7%, respectively. The ultrafine-grained structure with an average grain size of 2 mu m was revealed to be stable to subsequent annealing up to 150 degrees C.

引用

页码：689 / 693

页数：5

共 50 条

[1] Evolution of the Microstructure and Mechanical Properties of Copper during the Rolling–ECAP Process
S. N. Lezhnev
I. E. Volokitina
E. A. Panin
A. V. Volokitin
Physics of Metals and Metallography, 2020, 121 : 689 - 693
[2] Evolution of the Microstructure and Mechanical Properties of Copper under ECAP with Intense Cooling
Volokitina, I. E.
METAL SCIENCE AND HEAT TREATMENT, 2020, 62 (3-4) : 253 - 258
[3] Evolution of the Microstructure and Mechanical Properties of Copper under ECAP with Intense Cooling
I. E. Volokitina
Metal Science and Heat Treatment, 2020, 62 : 253 - 258
[4] Effects on the Microstructure Evolution and Properties of Graphene/Copper Composite during Rolling Process
Yang, Ziyue
Deng, Fan
Tao, Zhang
Yan, Shuai
Ma, Heng
Qian, Miao
He, Wei
Zhang, Zhifeng
Liu, Yanqiang
Wang, Lidong
MATERIALS, 2023, 16 (16)
[5] Microstructure, texture and mechanical properties of pure copper processed by ECAP and subsequent cold rolling
Bahadori, Sh. Ranjbar
Dehghani, K.
Bakhshandeh, F.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 583 : 36 - 42
[6] Evolution of the Microstructure and Mechanical Properties of Copper during the Pressing–Drawing Process
I. E. Volokitina
A. V. Volokitin
Physics of Metals and Metallography, 2018, 119 : 917 - 921
[7] Mechanical properties, microstructure, and texture evolution of copper sheets subjected to differential speed rolling process
Lee, Jongbeom
Jeong, Haguk
Lee, Gunha
Jung, Taekkyun
MATERIALS RESEARCH EXPRESS, 2022, 9 (10)
[8] Effect of cold rolling on microstructure and mechanical properties of copper subjected to ECAP with various numbers of passes
Stepanov, N. D.
Kuznetsov, A. V.
Salishchev, G. A.
Raab, G. I.
Valiev, R. Z.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2012, 554 : 105 - 115
[9] Evolution of the Microstructure and Mechanical Properties of Copper during the Pressing-Drawing Process
Volokitina, I. E.
Volokitin, A. V.
PHYSICS OF METALS AND METALLOGRAPHY, 2018, 119 (09): : 917 - 921
[10] Simulation of microstructure evolution on Copper, Aluminum and alloy during ECAP
Guo Tingbiao
Zhao Junyuan
Ding Yutian
Li Hailong
Liu Bo
ADVANCES IN MATERIALS AND MATERIALS PROCESSING, PTS 1-3, 2013, 652-654 : 1927 - 1931

← 1 2 3 4 5 →