Preparation of melting-free poly(lactic acid) by amorphous and crystal crosslinking under UV irradiation

被引：0
|
作者：
机构：
[1] Koo, Gwang-Hoe
[2] Jang, Jinho
来源：
Jang, J. (jh.jang@kumoh.ac.kr) | 1600年 / John Wiley and Sons Inc卷 / 127期
关键词：
The poly(lactic acid) (PLA) with 3.6% mol of benzophenone (BP) per repeat unit of PLA can be crosslinked to a gel fraction of 98.5% at UV energy of 160 J/cm2. From NMR analysis; the photocrosslinking of PLA was attributed to the recombination of primary and tertiary carbon radicals in the repeating units which were generated by the hydrogen abstraction of BP. With increasing crosslinking; melting peak disappeared and glass transition temperature elevated with loss of crystallinity; indicating that the crosslinking occurred in the crystalline region as well as in the amorphous region. The thermal stability of the crosslinked PLA also improved as shown by higher onset temperature as much as 56°C and higher maximum decomposition temperature compared with the pristine PLA. The higher toughness of the crosslinked PLA film was obtained together with the improvement in tensile strength and modulus with increasing crosslinking density. In addition to photocrosslinking of amorphous region; the crosslinking of crystalline region can have significant influence in the improvement of thermal and mechanical properties. © 2012 Wiley Periodicals; Inc; J; Appl; Polym; Sci; 2013 Copyright © 2012 Wiley Periodicals;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [41] An Efficient and Simple Reaction: Solvent-Free Preparation of Rosolic Acid Under Microwave Irradiation
    K. P. Ng. Dennis
    ChemicalResearchinChineseUniversities, 2008, (03) : 385 - 388
  • [42] Preparation and characterization of poly(lactic acid)/sisal fiber bio-composites under continuous elongation flow
    Tan, Yongbin
    Zhang, Xiaoqiu
    Qu, Jin-Ping
    JOURNAL OF POLYMER ENGINEERING, 2019, 39 (01) : 76 - 84
  • [43] Preparation and structural characterization of poly-mannose synthesized by phosphoric acid catalyzation under microwave irradiation
    Wang, Haisong
    Cheng, Xiangrong
    Shi, Yonghui
    Le, Guowei
    CARBOHYDRATE POLYMERS, 2015, 121 : 355 - 361
  • [44] Synthesis of poly(lactic acid) from D, L-lactide with ring-opening polymerization under microwave irradiation
    Zhang, Ying-Min
    Wang, Peng
    Han, Ning
    Lei, Hai-Fen
    Li, Yue
    Cailiao Kexue yu Gongyi/Material Science and Technology, 2009, 17 (02): : 288 - 292
  • [45] Preparation and osteogenesis of a multiple crosslinking silk fibroin/carboxymethyl chitosan/sodium alginate composite scaffold loading with mesoporous silica/poly (lactic acid-glycolic acid) microspheres
    Shi, Yiwan
    Wang, Zhaozhen
    Xu, Weikang
    Yu, Xiaolu
    Gao, Botao
    Zhou, Xinting
    Chen, Jiwen
    Jia, Kunfeng
    Cheang, Lek Hang
    Tam, Man seng
    Wang, Huajun
    Zheng, Xiaofei
    Wu, Tingting
    JOURNAL OF BIOMATERIALS APPLICATIONS, 2025, 39 (06) : 578 - 591
  • [46] Preparation of a halogen-free flame retardant and its effect on the poly (L-lactic acid) as the flame retardant material
    Zhou, Shanshan
    Yang, Yubin
    Zhu, Zhe
    Xie, Zhanghua
    Sun, Xaioyu
    Jia, Chunfeng
    Liu, Fude
    Wang, Junsheng
    Yang, Jinjun
    POLYMER, 2021, 229
  • [47] Preparation of a halogen-free flame retardant and its effect on the poly(L-lactic acid) as the flame retardant material
    Zhou, Shanshan
    Yang, Yubin
    Zhu, Zhe
    Xie, Zhanghua
    Sun, Xaioyu
    Jia, Chunfeng
    Liu, Fude
    Wang, Junsheng
    Yang, Jinjun
    Polymer, 2021, 229
  • [48] Biodegradation behavior of amorphous polyhydroxyalkanoate-incorporated poly(L-lactic acid) under modulated home-composting conditions
    Han, Geonhee
    Yoon, Juhee
    Lee, Changsuk
    Lee, Eunhye
    Yoon, Kichull
    Kwak, Hyo Won
    Jin, Hyoung-Joon
    POLYMER TESTING, 2023, 126
  • [49] Effect of thermal annealing on crystal evolution and multiple melting behaviors of molded poly(L-lactic acid) and poly(butylene succinate) blends upon heating investigated by TMDSC
    Kajornprai, Todsapol
    Sirisinha, Kalyanee
    JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY, 2021, 146 (06) : 2471 - 2480
  • [50] Effect of thermal annealing on crystal evolution and multiple melting behaviors of molded poly(L-lactic acid) and poly(butylene succinate) blends upon heating investigated by TMDSC
    Todsapol Kajornprai
    Kalyanee Sirisinha
    Journal of Thermal Analysis and Calorimetry, 2021, 146 : 2471 - 2480
12345