Preparation of melting-free poly(lactic acid) by amorphous and crystal crosslinking under UV irradiation

被引：0
|
作者：
机构：
[1] Koo, Gwang-Hoe
[2] Jang, Jinho
来源：
Jang, J. (jh.jang@kumoh.ac.kr) | 1600年 / John Wiley and Sons Inc卷 / 127期
关键词：
The poly(lactic acid) (PLA) with 3.6% mol of benzophenone (BP) per repeat unit of PLA can be crosslinked to a gel fraction of 98.5% at UV energy of 160 J/cm2. From NMR analysis; the photocrosslinking of PLA was attributed to the recombination of primary and tertiary carbon radicals in the repeating units which were generated by the hydrogen abstraction of BP. With increasing crosslinking; melting peak disappeared and glass transition temperature elevated with loss of crystallinity; indicating that the crosslinking occurred in the crystalline region as well as in the amorphous region. The thermal stability of the crosslinked PLA also improved as shown by higher onset temperature as much as 56°C and higher maximum decomposition temperature compared with the pristine PLA. The higher toughness of the crosslinked PLA film was obtained together with the improvement in tensile strength and modulus with increasing crosslinking density. In addition to photocrosslinking of amorphous region; the crosslinking of crystalline region can have significant influence in the improvement of thermal and mechanical properties. © 2012 Wiley Periodicals; Inc; J; Appl; Polym; Sci; 2013 Copyright © 2012 Wiley Periodicals;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [21] Preparation, Melting Behavior and Thermal Stability of Poly (lactic acid)/Poly (propylene carbonate) Blends Processed by Vane Extruder
    Zou, Wei
    Chen, Rongyuan
    Zhang, Haichen
    Qu, Jinping
    PROCEEDINGS OF PPS-31: THE 31ST INTERNATIONAL CONFERENCE OF THE POLYMER PROCESSING SOCIETY, 2016, 1713
  • [22] Preparation of toughened poly(lactic acid)-poly(ε-caprolactone)-lignin nanocomposites with good heat- and UV-resistance
    Yang, Weijun
    Zhu, Yanlin
    He, Yongbin
    Xiao, Liqiang
    Xu, Pengwu
    Puglia, Debora
    Ma, Piming
    INDUSTRIAL CROPS AND PRODUCTS, 2022, 183
  • [23] Effect of poly(2-ethyl-2-oxazoline) and UV irradiation on the melt rheology and mechanical properties of poly(lactic acid)
    Zhao, Guoqing
    Thompson, Michael R.
    Zhu, Zhirong
    JOURNAL OF APPLIED POLYMER SCIENCE, 2019, 136 (40)
  • [24] Crosslinking of cotton cellulose with succinic acid in the presence of titanium dioxide nano-catalyst under UV irradiation
    Cheng-Chi Chen
    Chyung-Chyung Wang
    Journal of Sol-Gel Science and Technology, 2006, 40 : 31 - 38
  • [25] Crosslinking of cotton cellulose with succinic acid in the presence of titanium dioxide nano-catalyst under UV irradiation
    Chen, Cheng-Chi
    Wang, Chyung-Chyung
    JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY, 2006, 40 (01) : 31 - 38
  • [26] EPR STUDY OF FREE RADICALS FORMED IN FUSIDIC ACID AND NEOMYCIN UNDER UV IRRADIATION
    Pierzchala, Ewa
    Ramos, Pawel
    Pilawa, Barbara
    ACTA POLONIAE PHARMACEUTICA, 2019, 76 (02): : 215 - 223
  • [27] Amorphous calcium phosphate/poly(D,L-lactic acid) composite nanofibers: Electrospinning preparation and biomineralization
    Ma, Zhao
    Chen, Feng
    Zhu, Ying-Jie
    Cui, Ting
    Liu, Xuan-Yong
    JOURNAL OF COLLOID AND INTERFACE SCIENCE, 2011, 359 (02) : 371 - 379
  • [28] Crystal Evolution of Amorphous Poly(lactic acid) During Simultaneous Multi-step Tensile Deformation and Annealing
    Kajornprai, Todsapol
    Sringam, Jiradet
    Seejuntuek, Anucha
    Kaewsuwan, Dechmongkhon
    Kamonsutthipaijit, Nuntaporn
    Chio-Srichan, Sirinart
    Suppakarn, Nitinat
    Trongsatitkul, Tatiya
    JOURNAL OF POLYMER SCIENCE, 2025, 63 (01) : 192 - 203
  • [29] Direct synthesis of poly(l-lactic acid) by melt polycondensation under continuous microwave irradiation
    Zhang, Ying-Min
    Li, Kai-Ming
    Wang, Peng
    Jiao, Chun-Yan
    Han, Ning
    Gaofenzi Cailiao Kexue Yu Gongcheng/Polymeric Materials Science and Engineering, 2009, 25 (10): : 27 - 30
  • [30] Green oxidation of bio-lactic acid with H2O2 into tartronic acid under UV irradiation
    Tian, Xuxia
    Wang, Zhijian
    Yang, Pengju
    Hao, Ruipeng
    Jia, Suping
    Li, Na
    Li, Li
    Zhu, Zhenping
    RSC ADVANCES, 2016, 6 (47): : 41007 - 41010
12345