Preparation of melting-free poly(lactic acid) by amorphous and crystal crosslinking under UV irradiation

被引：0
|
作者：
机构：
[1] Koo, Gwang-Hoe
[2] Jang, Jinho
来源：
Jang, J. (jh.jang@kumoh.ac.kr) | 1600年 / John Wiley and Sons Inc卷 / 127期
关键词：
The poly(lactic acid) (PLA) with 3.6% mol of benzophenone (BP) per repeat unit of PLA can be crosslinked to a gel fraction of 98.5% at UV energy of 160 J/cm2. From NMR analysis; the photocrosslinking of PLA was attributed to the recombination of primary and tertiary carbon radicals in the repeating units which were generated by the hydrogen abstraction of BP. With increasing crosslinking; melting peak disappeared and glass transition temperature elevated with loss of crystallinity; indicating that the crosslinking occurred in the crystalline region as well as in the amorphous region. The thermal stability of the crosslinked PLA also improved as shown by higher onset temperature as much as 56°C and higher maximum decomposition temperature compared with the pristine PLA. The higher toughness of the crosslinked PLA film was obtained together with the improvement in tensile strength and modulus with increasing crosslinking density. In addition to photocrosslinking of amorphous region; the crosslinking of crystalline region can have significant influence in the improvement of thermal and mechanical properties. © 2012 Wiley Periodicals; Inc; J; Appl; Polym; Sci; 2013 Copyright © 2012 Wiley Periodicals;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Preparation of melting-free poly(lactic acid) by amorphous and crystal crosslinking under UV irradiation
    Koo, Gwang-Hoe
    Jang, Jinho
    JOURNAL OF APPLIED POLYMER SCIENCE, 2013, 127 (06) : 4515 - 4523
  • [2] Surface modification of poly(lactic acid) by UV/Ozone irradiation
    Koo, Gwang-Hoe
    Jang, Jinho
    FIBERS AND POLYMERS, 2008, 9 (06) : 674 - 678
  • [3] Photodegradation of Poly(lactic acid) Stereocomplex by UV-Irradiation
    Tsuji, Hideto
    Sugiyama, Hiroaki
    Sato, Yoshihiro
    JOURNAL OF POLYMERS AND THE ENVIRONMENT, 2012, 20 (03) : 706 - 712
  • [4] Photodegradation of Poly(lactic acid) Stereocomplex by UV-Irradiation
    Hideto Tsuji
    Hiroaki Sugiyama
    Yoshihiro Sato
    Journal of Polymers and the Environment, 2012, 20 : 706 - 712
  • [5] Surface modification of poly(lactic acid) by UV/Ozone irradiation
    Gwang-Hoe Koo
    Jinho Jang
    Fibers and Polymers, 2008, 9 : 674 - 678
  • [6] Poly (lactic acid)/titanium dioxide composites: Preparation and performance under ultraviolet irradiation
    Man, Changzhen
    Zhang, Chunmei
    Liu, Yiming
    Wang, Weiwei
    Ren, Wuyang
    Jiang, Long
    Reisdorffer, Frederic
    Thien Phap Nguyen
    Dan, Yi
    POLYMER DEGRADATION AND STABILITY, 2012, 97 (06) : 856 - 862
  • [7] Poly(lactic acid)/clarithromycin with metals dioxides nanoparticles: Preparation and performance under ultraviolet irradiation
    Adil H.
    Thamer H.
    Alsayed R.
    Bufaroosha M.
    Ahmed D.S.
    Al-Mashhadani M.H.
    Hashim H.
    Husain A.A.
    Yousif E.
    Materials Science for Energy Technologies, 2024, 7 : 73 - 84
  • [8] Enzymatic degradation of poly(L-lactic acid): Effects of UV irradiation
    Tsuji, Hideto
    Echizen, Yoshihisa
    Nishimura, Yoshiro
    JOURNAL OF POLYMERS AND THE ENVIRONMENT, 2006, 14 (03) : 239 - 248
  • [9] Enzymatic Degradation of Poly(l-Lactic Acid): Effects of UV Irradiation
    Hideto Tsuji
    Yoshihisa Echizen
    Yoshiro Nishimura
    Journal of Polymers and the Environment, 2006, 14 : 239 - 248
  • [10] Preparation and characterization of high molecular weight poly (L-lactic acid) under microwave irradiation
    Department of Materials, College of Technology, Jinan University, Guangzhou 510632, China
    Gongneng Cailiao/Journal of Functional Materials, 2007, 38 (06): : 972 - 975
12345