Formation of Mg-Cu-Zn-Y bulk metallic glasses with compressive strength over gigapascal

被引：0
|
作者：
Li, Z.G. [1 ]
Hui, X. [1 ]
Zhang, C.M. [1 ]
Chen, G.L. [1 ]
机构：
[1] State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, China
来源：
Journal of Alloys and Compounds | 2008年 / 454卷 / 1-2期
关键词：
The Mg55+xCu30-xZn5Y10 bulk metallic glasses (BMGs) with diameter of at least 3 mm were successfully fabricated in compositional range at x = 3-15 by conventional Cu-mold casting method. This kind of BMG alloys have supercooled liquid region (SLR) from 40 to 65 K; γ-value from 0.390 to 0.417; and the reduced glass transformation temperature from 0.543 to 0.576. By increasing the Zn content to 7%; the compressive strength of Mg-based BMG alloy reaches about 1.1 GPa. Vein pattern morphology has been observed in fractured surface of the Mg58Cu25Zn7Y10 alloy. The thermal; mechanical; and acoustic measurements indicate that Mg-Zn-Cu-Y BMGs are intrinsically brittle and are of good GFA. It is suggested that the correlation of elastic constants and mechanical properties of alloys could guide the Mg-based BMGs design. © 2007 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：168 / 173
相关论文
共 50 条
  • [21] Formation of ternary Mg-Cu-Dy bulk metallic glasses
    X. F. Wu
    Y. Kang
    F. F. Wu
    K. Q. Qiu
    L. K. Meng
    Bulletin of Materials Science, 2011, 34 : 1507 - 1510
  • [22] Formation of ternary Mg-Cu-Dy bulk metallic glasses
    Wu, X. F.
    Kang, Y.
    Wu, F. F.
    Qiu, K. Q.
    Meng, L. K.
    BULLETIN OF MATERIALS SCIENCE, 2011, 34 (07) : 1507 - 1510
  • [23] Development and characterization of Ca-Mg-Zn-Cu bulk metallic glasses
    Senkov, O. N.
    Miracle, D. B.
    Scott, J. M.
    INTERMETALLICS, 2006, 14 (8-9) : 1055 - 1060
  • [24] STRUCTURE AND PROPERTIES OF Mg-Cu-(Y,Ca) BULK METALLIC GLASSES
    Babilas, R.
    Cesarz-Andraczke, K.
    Nowosielski, R.
    ARCHIVES OF METALLURGY AND MATERIALS, 2015, 60 (04) : 2645 - 2650
  • [25] Mg-Cu-Zn-Y块体金属玻璃的形成
    门华
    徐坚
    金属学报, 2001, (12) : 1243 - 1246
  • [26] Bulk metallic glass formation in the Mg-Cu-Y system
    Katz-Demyanetz, A.
    Rosenson, H.
    Koren, Z.
    Regev, M.
    MATERIALS SCIENCE AND TECHNOLOGY, 2009, 25 (10) : 1227 - 1233
  • [27] Mg-Ca-Zn bulk metallic glasses with high strength and significant ductility
    Gu, X
    Shiflet, GJ
    Guo, FQ
    Poon, SJ
    JOURNAL OF MATERIALS RESEARCH, 2005, 20 (08) : 1935 - 1938
  • [28] Motion of crystal particles by the electromagnetic vibrations in Mg-Cu-Y bulk metallic glasses
    Tamura, Takuya
    Maehara, Yuuki
    Omura, Naoki
    Miwa, Kenji
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2008, 39A (08): : 1917 - 1921
  • [29] Strengthening and toughening of Mg-Cu-(Y, Gd) bulk metallic glasses by minor addition of Be
    Li, Z. G.
    Hui, X.
    Zhang, C. M.
    Wang, M. L.
    Chen, G. L.
    MATERIALS LETTERS, 2007, 61 (28) : 5018 - 5021
  • [30] Motion of Crystal Particles by the Electromagnetic Vibrations in Mg-Cu-Y Bulk Metallic Glasses
    Takuya Tamura
    Yuuki Maehara
    Naoki Omura
    Kenji Miwa
    Metallurgical and Materials Transactions A, 2008, 39 : 1917 - 1921
12345