Formation of Mg-Cu-Zn-Y bulk metallic glasses with compressive strength over gigapascal

被引：0
|
作者：
Li, Z.G. [1 ]
Hui, X. [1 ]
Zhang, C.M. [1 ]
Chen, G.L. [1 ]
机构：
[1] State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing, 100083, China
来源：
Journal of Alloys and Compounds | 2008年 / 454卷 / 1-2期
关键词：
The Mg55+xCu30-xZn5Y10 bulk metallic glasses (BMGs) with diameter of at least 3 mm were successfully fabricated in compositional range at x = 3-15 by conventional Cu-mold casting method. This kind of BMG alloys have supercooled liquid region (SLR) from 40 to 65 K; γ-value from 0.390 to 0.417; and the reduced glass transformation temperature from 0.543 to 0.576. By increasing the Zn content to 7%; the compressive strength of Mg-based BMG alloy reaches about 1.1 GPa. Vein pattern morphology has been observed in fractured surface of the Mg58Cu25Zn7Y10 alloy. The thermal; mechanical; and acoustic measurements indicate that Mg-Zn-Cu-Y BMGs are intrinsically brittle and are of good GFA. It is suggested that the correlation of elastic constants and mechanical properties of alloys could guide the Mg-based BMGs design. © 2007 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
页码：168 / 173
相关论文
共 50 条
  • [1] Formation of Mg-Cu-Zn-Y bulk metallic glasses with compressive strength over gigapascal
    Li, Z. G.
    Hui, X.
    Zhang, C. M.
    Chen, G. L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2008, 454 (1-2) : 168 - 173
  • [2] Formation of Mg-Cu-Zn-Y bulk metallic glass
    Men, H
    Xu, J
    ACTA METALLURGICA SINICA, 2001, 37 (12) : 1243 - 1246
  • [3] Formation of Mg-Cu-Zn-Y bulk metallic glass
    Men, Hua
    Xu, Jian
    2001, Chinese Academy of Sciences (37):
  • [4] Bulk metallic glass formation in the Mg-Cu-Zn-Y system
    Men, H
    Hu, ZQ
    Xu, J
    SCRIPTA MATERIALIA, 2002, 46 (10) : 699 - 703
  • [5] Formation of high strength Mg-Cu-Zn-Y alloys
    Zhang, C. M.
    Hui, X.
    Yao, K. F.
    Li, Z. G.
    Chen, G. L.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 491 (1-2): : 470 - 475
  • [6] Mg-Cu-Y-Ag bulk metallic glasses with enhanced compressive strength and plasticity
    Hui, X.
    Sun, G. Y.
    Zhang, C. M.
    Liu, S. N.
    Wang, E. R.
    Wang, M. L.
    Chen, G. L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 504 : S6 - S9
  • [7] Mg-Cu-Zn-Y magnesium alloy with high strength and plasticity
    Zhang, C. M.
    Hui, X.
    Li, Z. G.
    Chen, G. L.
    MATERIALS LETTERS, 2008, 62 (6-7) : 1129 - 1131
  • [8] Effects of Mg content and cooling rate on microstructure and corrosion behavior of Mg-Cu-Zn-Y bulk metallic glass composites
    Wang, Jingfeng
    Wei, Yiyun
    Wu, Xia
    Pan, Fusheng
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2011, 40 (06): : 1060 - 1064
  • [9] Structure, Properties, and Crystallization of Mg-Cu-Y-Zn Bulk Metallic Glasses
    Babilas, Rafa
    Cesarz-Andraczke, Katarzyna
    Nowosielski, Ryszard
    Burian, Andrzej
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (06) : 2241 - 2246
  • [10] Structure, Properties, and Crystallization of Mg-Cu-Y-Zn Bulk Metallic Glasses
    Rafał Babilas
    Katarzyna Cesarz-Andraczke
    Ryszard Nowosielski
    Andrzej Burian
    Journal of Materials Engineering and Performance, 2014, 23 : 2241 - 2246
12345