The Effect of Homogenization Parameters on the Structure of EN AW-6082 Alloy

被引：0
|
作者：
Luštinec J. [1 ]
Očenášek V. [1 ]
Jelínek M., jr. [2 ]
机构：
[1] SVÚM a.s., Tovární 2053, Čelákovice
[2] Constellium Extrusions Děčín s.r.o., Ústecká 751/37, Děčín V-Rozbělesy
来源：
Manufacturing Technology | 2017年 / 17卷 / 05期
关键词：
EN AW-6082 aluminium alloy; Extrusion; Homogenization; Phases; Structure;
D O I：
10.21062/ujep/x.2017/a/1213-2489/MT/17/5/766
中图分类号：
学科分类号：
摘要：
High temperature homogenization annealing of DC cast billets from aluminium alloys used for extrusion pressing is considered as one of substantial technological operations during extrusion processing. The structure of DC cast billets consists of dendrite cell structure and contains coarse and inhomogeneously distributed intermetallic phases of β-AlFeSi and α-Al(Fe,Mn)Si type.Structure after a homogenization annealing is quite decisive for both the final properties of extrusions and the extrudability of the cast structure. The present paper deals with the medium strength heat-treatable EN AW-6082 alloy. It is investigated the effect of heating rate, time at the annealing temperature and the cooling rate of continually cast billets during the homogenization annealing on the changes of electrical conductivity, structure and intermetallic phases. Copyright © 2017. Published by Manufacturing Technology. All rights reserved.
引用
收藏
相关论文
共 50 条
  • [31] Spray cooling of extruded EN AW-6082 aluminium alloy sheets: spatial heat transfer coefficients [Abkühlen stranggepresster Platten aus der Aluminiumlegierung EN AW-6082 mittels Spraykühlung – örtliche Wärmeübergangskoeffizienten]
    Golovko O.
    Frolov I.
    Rodman D.
    Nürnberger F.
    Grydin O.
    Schaper M.
    Forschung im Ingenieurwesen, 2014, 78 (3-4) : 131 - 137
  • [32] Effect of temperature and strain rate on friction factor during microforming of AW-6082 AL-alloy
    Behrens Bernd-Arno
    Conrads Hans
    Petrov Pavel
    International Journal of Material Forming, 2009, 2 : 613 - 616
  • [33] Water Quenching of Hot-Rolled Aluminum Strips: Process Integrated Heat Treatment of the Alloy EN AW-6082
    Olexandr Grydin
    Anatolii Andreiev
    Nikolay Sotirov
    Mykhailo Stolbchenko
    Teresa M. Behr
    Anton Ashkelianets
    Iaroslav Frolov
    Mirko Schaper
    JOM, 2019, 71 : 407 - 418
  • [34] Water-Air Spray Cooling of Extruded Profiles: Process Integrated Heat Treatment of the Alloy EN AW-6082
    M. Nowak
    O. Golovko
    F. Nürnberger
    I. Frolov
    M. Schaper
    Journal of Materials Engineering and Performance, 2013, 22 : 2580 - 2587
  • [35] Influence of Hot Deformation on Mechanical Properties and Microstructure of a Twin-Roll Cast Aluminium Alloy EN AW-6082
    Grydin, O.
    Stolbchenko, M.
    Nuernberger, F.
    Schaper, M.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2014, 23 (03) : 937 - 943
  • [36] Water-Air Spray Cooling of Extruded Profiles: Process Integrated Heat Treatment of the Alloy EN AW-6082
    Nowak, M.
    Golovko, O.
    Nuernberger, F.
    Frolov, I.
    Schaper, M.
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2013, 22 (09) : 2580 - 2587
  • [37] Water Quenching of Hot-Rolled Aluminum Strips: Process Integrated Heat Treatment of the Alloy EN AW-6082
    Grydin, Olexandr
    Andreiev, Anatolii
    Sotirov, Nikolay
    Stolbchenko, Mykhailo
    Behr, Teresa M.
    Ashkelianets, Anton
    Frolov, Iaroslav
    Schaper, Mirko
    JOM, 2019, 71 (01) : 407 - 418
  • [38] Effect of extrusion press exit temperature and chromium on grain structure of EN AW 6082 alloy forgings
    Birol, Y.
    MATERIALS SCIENCE AND TECHNOLOGY, 2015, 31 (02) : 207 - 211
  • [39] The origin of weld seam defects related to metal flow in the hot extrusion of aluminium alloys en AW-6060 and en AW-6082
    Den Bakker, A.J. (andrewdenbakker@nedal.nl), 1600, Elsevier Ltd (214):
  • [40] Investigations on the Cyclic Crack Growth Behaviour of Spring Steel Wire Reinforced EN AW-6082
    Merzkirch, Matthias
    Weidenmann, Kay Andre
    Schulze, Volker
    EPD CONGRESS 2011, 2011, : 135 - 142
12345