High-temperature oxidation behavior of the Co-base superalloy DZ40M in air

被引：0
|
作者：
Liu, P.S. [1 ,2 ]
Liang, K.M. [1 ]
机构：
[1] Dept. of Mat. Sci. and Engineering, Tsinghua University, Beijing 100084, China
[2] Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China
来源：
| 2000年 / Kluwer Academic/Plenum Publ Corp, New York卷 / 53期
关键词：
Cracking (chemical) - High temperature properties - Morphology - Oxidation resistance - Precipitation (chemical) - Reaction kinetics - Spalling - Superalloys;
D O I：
10.1023/a:1004597405809
中图分类号：
学科分类号：
摘要：
The oxidation behavior of the Co-base superalloy DZ40M was studied in air at 900-1100 °C for times of up to 2000 hr. The results indicated that this alloy can grow a protective oxide scale at 900 and 1000 °C during isothermal oxidation, but not at 1100 °C because of serious cracking and spalling of the oxide scales. Moreover, an internal-precipitate zone formed in the subsurface region of the alloy at all temperatures and times. The precipitates were rich in Cr in the vicinity of the alloy-scale interface and rich in Al deep in the alloy. The internal-precipitate morphology changed from a granular to needlelike shape with increasing oxidation temperature.
引用
收藏
相关论文
共 50 条
  • [11] Effects of secondary precipitation on recrystallization in Co-base superalloy DZ40M
    赵阳
    王磊
    于腾
    宋秀
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 1944 - 1948
  • [12] Effects of secondary precipitation on recrystallization in Co-base superalloy DZ40M
    Zhao Yang
    Wang Lei
    Yu Teng
    Song Xiu
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2006, 16 : S1944 - S1948
  • [13] PHASE TRANSFORMATION OF Al-Ti COATINGS ON Co-BASE SUPERALLOY DZ40M DURING HIGH TEMPERATURE OXIDATION
    Liu Peisheng
    TransactionsofNonferrousMetalsSocietyofChina, 1998, (04) : 51 - 56
  • [14] Activation energy of oxidation of Co-base DZ40M alloy at high temperatures
    Liu, Peisheng
    Cheng, Ken
    Xiyou Jinshu / Chinese Journal of Rare Metals, 2008, 32 (05): : 543 - 547
  • [15] High-Temperature Oxidation Behavior of a Novel Co-Base Superalloy
    Forsik, Stephane A. J.
    Rosas, Alberto O. Polar
    Wang, Tao
    Colombo, Gian A.
    Zhou, Ning
    Kernion, Samuel J.
    Epler, Mario E.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (09): : 4058 - 4069
  • [16] High-Temperature Oxidation Behavior of a Novel Co-Base Superalloy
    Stéphane A. J. Forsik
    Alberto O. Polar Rosas
    Tao Wang
    Gian A. Colombo
    Ning Zhou
    Samuel J. Kernion
    Mario E. Epler
    Metallurgical and Materials Transactions A, 2018, 49 : 4058 - 4069
  • [17] Failure Behavior of an Aluminide Coating on a Co-Base Superalloy during High-Temperature Oxidation in Air
    P. S. Liu
    K. M. Liang
    S. R. Gu
    Oxidation of Metals, 2000, 54 : 277 - 283
  • [18] Failure behavior of an aluminide coating on a Co-base superalloy during high-temperature oxidation in air
    Liu, P.S.
    Liang, K.M.
    Gu, S.R.
    Oxidation of Metals, 2000, 54 (03): : 277 - 283
  • [19] Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air
    Liu, PS
    Liang, KM
    Gu, SR
    OXIDATION OF METALS, 2000, 54 (3-4): : 277 - 283
  • [20] Effect of leaching process for ceramic core on microstructure and mechanical property of investment cast co-base superalloy DZ40M
    Tong J.
    Chen J.
    Zheng Z.
    Yu Y.
    Ning L.
    Liu E.
    Cailiao Yanjiu Xuebao/Chinese Journal of Materials Research, 2016, 30 (02): : 140 - 148
12345