Failure behavior of an aluminide coating on a Co-base superalloy during high-temperature oxidation in air

被引：1
|
作者：
Liu, P.S. [1 ,2 ]
Liang, K.M. [1 ]
Gu, S.R. [1 ]
机构：
[1] Dept. of Mat. Sci. and Engineering, Tsinghua University, Beijing 100084, China
[2] Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China
来源：
Oxidation of Metals | 2000年 / 54卷 / 03期
关键词：
D O I：
10.1023/a:1004650328779
中图分类号：
学科分类号：
摘要：
9
引用
收藏
页码：277 / 283
相关论文
共 50 条
  • [1] Failure Behavior of an Aluminide Coating on a Co-Base Superalloy during High-Temperature Oxidation in Air
    P. S. Liu
    K. M. Liang
    S. R. Gu
    Oxidation of Metals, 2000, 54 : 277 - 283
  • [2] Failure behavior of an aluminide coating on a co-base superalloy during high-temperature oxidation in air
    Liu, PS
    Liang, KM
    Gu, SR
    OXIDATION OF METALS, 2000, 54 (3-4): : 277 - 283
  • [3] The main degradation modes of an aluminide coating on a Co-base superalloy during high-temperature oxidation in air
    Liu, PS
    OXIDATION OF METALS, 2002, 58 (3-4): : 331 - 336
  • [4] The Main Degradation Modes of an Aluminide Coating on a Co-Base Superalloy During High-Temperature Oxidation in Air
    P.S. Liu
    Oxidation of Metals, 2002, 58 : 331 - 336
  • [5] High-Temperature Oxidation Behavior of a Novel Co-Base Superalloy
    Forsik, Stephane A. J.
    Rosas, Alberto O. Polar
    Wang, Tao
    Colombo, Gian A.
    Zhou, Ning
    Kernion, Samuel J.
    Epler, Mario E.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2018, 49A (09): : 4058 - 4069
  • [6] High-Temperature Oxidation Behavior of a Novel Co-Base Superalloy
    Stéphane A. J. Forsik
    Alberto O. Polar Rosas
    Tao Wang
    Gian A. Colombo
    Ning Zhou
    Samuel J. Kernion
    Mario E. Epler
    Metallurgical and Materials Transactions A, 2018, 49 : 4058 - 4069
  • [7] High-temperature oxidation behavior of the Co-base superalloy DZ40M in air
    Liu, P.S.
    Liang, K.M.
    2000, Kluwer Academic/Plenum Publ Corp, New York (53):
  • [8] High-Temperature Oxidation Behavior of the Co-Base Superalloy DZ40M in Air
    P. S. Liu
    K. M. Liang
    Oxidation of Metals, 2000, 53 : 351 - 360
  • [9] High-temperature oxidation behavior of the Co-base superalloy DZ40M in air
    Liu, PS
    Liang, KM
    OXIDATION OF METALS, 2000, 53 (3-4): : 351 - 360
  • [10] Cyclic oxidation behavior of a cobalt aluminide coating on Co-base superalloy AMS 5608
    Lee, JW
    Kuo, YC
    SURFACE & COATINGS TECHNOLOGY, 2005, 200 (5-6): : 1225 - 1230
12345