High-temperature oxidation behavior of the Co-base superalloy DZ40M in air

被引：0
|
作者：
Liu, P.S. [1 ,2 ]
Liang, K.M. [1 ]
机构：
[1] Dept. of Mat. Sci. and Engineering, Tsinghua University, Beijing 100084, China
[2] Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China
来源：
| 2000年 / Kluwer Academic/Plenum Publ Corp, New York卷 / 53期
关键词：
Cracking (chemical) - High temperature properties - Morphology - Oxidation resistance - Precipitation (chemical) - Reaction kinetics - Spalling - Superalloys;
D O I：
10.1023/a:1004597405809
中图分类号：
学科分类号：
摘要：
The oxidation behavior of the Co-base superalloy DZ40M was studied in air at 900-1100 °C for times of up to 2000 hr. The results indicated that this alloy can grow a protective oxide scale at 900 and 1000 °C during isothermal oxidation, but not at 1100 °C because of serious cracking and spalling of the oxide scales. Moreover, an internal-precipitate zone formed in the subsurface region of the alloy at all temperatures and times. The precipitates were rich in Cr in the vicinity of the alloy-scale interface and rich in Al deep in the alloy. The internal-precipitate morphology changed from a granular to needlelike shape with increasing oxidation temperature.
引用
收藏
相关论文
共 50 条
  • [1] High-temperature oxidation behavior of the Co-base superalloy DZ40M in air
    Liu, PS
    Liang, KM
    OXIDATION OF METALS, 2000, 53 (3-4): : 351 - 360
  • [2] High-Temperature Oxidation Behavior of the Co-Base Superalloy DZ40M in Air
    P. S. Liu
    K. M. Liang
    Oxidation of Metals, 2000, 53 : 351 - 360
  • [3] Cyclic oxidation behavior of the aluminide coatings on the co-base superalloy DZ40M
    Liu, Peisheng
    Liang, Kaiming
    Gu, Shouren
    Guan, Hengrong
    Sun, Xiaofeng
    Jin, Tao
    Yang, Kenu
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2000, 29 (04): : 231 - 234
  • [4] Carbide Behavior during High Temperature Creep in DZ40M Co-base Superalloy
    Wenhui JIANG
    Xiangdong YAO
    Hengrong GUAN and Zhuangqi HU(Institute of Metal Research
    Journal of Materials Science & Technology, 1999, (06) : 515 - 518
  • [5] Carbide behavior during high temperature creep in DZ40M Co-base superalloy
    Jiang, Wenhui
    Yao, Xiangdong
    Guan, Hengrong
    Hu, Zhuangqi
    Journal of Materials Science and Technology, 1999, 15 (06): : 515 - 518
  • [6] Carbide behavior during high temperature creep in DZ40M co-base superalloy
    Jiang, WH
    Yao, XD
    Guan, HR
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 1999, 15 (06) : 515 - 518
  • [7] Cyclic oxidation behavior of aluminide coatings on the Co-base superalloy DZ40M
    Liu, PS
    Liang, KM
    Zhou, HY
    Gu, SR
    Sun, XF
    Guan, HR
    Jin, T
    Yang, KN
    SURFACE & COATINGS TECHNOLOGY, 2001, 145 (1-3): : 75 - 79
  • [8] Cyclic oxidation behavior of the aluminide coatings on the Co-base superalloy DZ40M
    Liu, PS
    Liang, KM
    Gu, SR
    Guan, HG
    Sun, XF
    Kin, T
    Yang, KN
    RARE METAL MATERIALS AND ENGINEERING, 2000, 29 (04) : 231 - 234
  • [9] Phase transformation of aluminide coatings on the Co-base superalloy DZ40M during high temperature oxidation
    Liu, PS
    Guan, HR
    Sun, XF
    Jin, T
    Hu, ZQ
    Yang, K
    RARE METAL MATERIALS AND ENGINEERING, 1999, 28 (06) : 357 - 362
  • [10] Phase transformation of Al-Ti coatings on Co-base superalloy DZ40M during high temperature oxidation
    Liu, PS
    Sun, XF
    Jin, T
    Guan, HR
    Hu, ZQ
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 1998, 8 (04) : 582 - 587
12345