Study on erosion-corrosion property of metal material

被引：0
|
作者：
Liu, Guo-Yu [1 ]
Bao, Chong-Gao [2 ]
Zhang, An-Feng [2 ]
机构：
[1] Yunnan Tin Group Co. Ltd., Gejiu 661000, China
[2] Xi'an Jiaotong Univ., Xi'an 710049, China
来源：
Cailiao Gongcheng/Journal of Materials Engineering | 2004年 / 11期
关键词：
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The two-phase flow of liquid and solid erosion-corrosion tester was used to simulate different erosion-corrosion conditions. The erosion-corrosion behavior of 1Cr18Ni9Ti and T8 was studied. The damage of material was accelerated as increasing erosion speed and slurry temperature. The erosion-corrosion mass loss rate of T8 was much higher than that of 1Cr18Ni9Ti. In order to increase the resistance of the erosion-corrosion of material in acid slurry, first, the materials must have good corrosion resistance, and the second, they must have good wear resistance. The erosion-corrosion mass loss rates of 18-8 and T8 appears maximum value, when the erosion angle is at 45 degree, so that the erosion angle of 45 degree in the pipeline structure should be avoided.
引用
收藏
页码：37 / 40
相关论文
共 50 条
  • [21] FLOW EFFECTS ON EROSION-CORROSION
    DAWSON, JL
    SHIH, CC
    GEAREY, D
    MILLER, RG
    MATERIALS PERFORMANCE, 1991, 30 (04) : 57 - 60
  • [22] Piehl factor for erosion-corrosion
    不详
    MATERIALS PERFORMANCE, 2000, 39 (03) : 13 - 13
  • [23] Experimental study of erosion-corrosion wear of materials: A review
    Prozhega, M. V.
    Tatus, N. A.
    Samsonov, S. V.
    Kolyuzhni, O. Yu
    Smirnov, N. N.
    JOURNAL OF FRICTION AND WEAR, 2014, 35 (02) : 155 - 160
  • [24] Experimental study of erosion-corrosion wear of materials: A review
    M. V. Prozhega
    N. A. Tatus
    S. V. Samsonov
    O. Yu. Kolyuzhni
    N. N. Smirnov
    Journal of Friction and Wear, 2014, 35 : 155 - 160
  • [25] Optimizing material selection: A study of erosion-corrosion performance in homogeneous and carbide-containing materials
    Islam, Md. Aminul
    Jiang, Jiaren
    Xie, Yongsong
    WEAR, 2024, 536
  • [26] Study of Erosion-Corrosion and Corrosion Behavior of Commercially Pure-Ti During Slurry Erosion
    Khayatan, N.
    Ghasemi, H. M.
    Abedini, M.
    JOURNAL OF TRIBOLOGY-TRANSACTIONS OF THE ASME, 2018, 140 (06):
  • [27] Assessing metal matrix composites for corrosion and erosion-corrosion applications in the oil sands industry
    Neville, A.
    Reza, F.
    Chiovelli, S.
    Revega, T.
    CORROSION, 2006, 62 (08) : 657 - 675
  • [28] Particulate erosion-corrosion of Al in aqueous conditions: some perspectives on pH effects on the erosion-corrosion map
    Stack, MM
    Pungwiwat, N
    TRIBOLOGY INTERNATIONAL, 2002, 35 (10) : 651 - 660
  • [29] Erosion, corrosion and erosion-corrosion of EB PVD thermal barrier coatings
    Wellman, R. G.
    Nicholls, J. R.
    TRIBOLOGY INTERNATIONAL, 2008, 41 (07) : 657 - 662
  • [30] Erosion-corrosion of heat exchanger tubes
    Kuznicka, B.
    ENGINEERING FAILURE ANALYSIS, 2009, 16 (07) : 2382 - 2387
12345