Effects of electrode wear on weld quality of hot galvanization steel with high strength in resistance spot welding

被引：0
|
作者：
Zhang, Xuqiang [1 ]
Zhang, Yansong [2 ]
Liu, Yancong [1 ]
机构：
[1] School of Mechanical Engineering, Petroleum University of China, Dongying 257061, China
[2] School of Mechanical Engineering and Power, Shanghai Jiaotong University, Shanghai 200030, China
来源：
Hanjie Xuebao/Transactions of the China Welding Institution | 2009年 / 30卷 / 10期
关键词：
Galvanizing - Welds - High strength steel - Welding electrodes - Wear resistance - Cracks;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Electrode wear characteristics were studied; the electrode life of un-coated steels was much lower and pitting changed more obviously than that of galvanization steels when welding. The effect of electrode wear on weld quality was studied; the expulsion was serious and more micro-cracks were grown at early electrode wear stage, which decreased weld quality greatly. And then based on the experiment results of effect of electrode wear on weld quality, welding technique step-current was established according to the current density that micro-crack degree was less than 0.25 mm to reduce the effect of electrode wear on weld quality.
引用
收藏
页码：5 / 8
相关论文
共 50 条
  • [31] Investigation of mechanical properties of high strength steel welded by resistance spot welding
    Aras, Sedat
    Ertan, Rukiye
    Guler Ozgul, Hande
    PAMUKKALE UNIVERSITY JOURNAL OF ENGINEERING SCIENCES-PAMUKKALE UNIVERSITESI MUHENDISLIK BILIMLERI DERGISI, 2018, 24 (01): : 63 - 68
  • [32] Macro characteristics of dissimilar high strength steel resistance spot welding joint
    Luo, Xiaomin
    Ren, Jiangwei
    Li, Dong
    Qin, Youqiong
    Xu, Peiquan
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2016, 87 (1-4): : 1105 - 1113
  • [33] Macro characteristics of dissimilar high strength steel resistance spot welding joint
    Xiaomin Luo
    Jiangwei Ren
    Dong Li
    Youqiong Qin
    Peiquan Xu
    The International Journal of Advanced Manufacturing Technology, 2016, 87 : 1105 - 1113
  • [34] Study on Intermediate Frequency Spot Welding Process of Hot Stamping High Strength Steel
    Yu, Yang
    Wang, Chao
    Chen, Shujun
    Lu, Zhenyang
    ADVANCED MANUFACTURING SYSTEMS, 2011, 339 : 375 - 378
  • [35] Weld Formation Characteristics in Resistance Spot Welding of Ultra-Thin Steel High welding current and short welding time were found to produce the best combination of strength and weld size
    Zhao, Y. Y.
    Zhang, Y. S.
    Wang, Pei-Chung
    WELDING JOURNAL, 2017, 96 (02) : 71S - 82S
  • [36] Weld formation characteristics in resistance spot welding of ultra-thin steel: High welding current and short welding time were found to produce the best combination of strength and weld size
    1600, American Welding Society (96):
  • [37] Effect of a Conically Shaped Hollow Electrode on Advanced High Strength Steel in Three-Sheet Resistance Spot Welding
    Kim, Donghyun
    Yu, Jiyoung
    Rhee, Sehun
    INTERNATIONAL JOURNAL OF PRECISION ENGINEERING AND MANUFACTURING, 2016, 17 (03) : 331 - 336
  • [38] Optimised design of electrode morphology for novel dissimilar resistance spot welding of aluminium alloy and galvanised high strength steel
    Zhang, Weihua
    Sun, Daqian
    Han, Lijun
    Li, Yongqiang
    MATERIALS & DESIGN, 2015, 85 : 461 - 470
  • [39] Effect of a conically shaped hollow electrode on advanced high strength steel in three-sheet resistance spot welding
    Donghyun Kim
    Jiyoung Yu
    Sehun Rhee
    International Journal of Precision Engineering and Manufacturing, 2016, 17 : 331 - 336
  • [40] A Novel Method Using Electromagnetic Stirring to Improve Resistance Spot Weld Quality of Advanced High Strength Steel (AHSS)
    Shen, Qi
    Li, YongBing
    Chen, GuanLong
    TRENDS IN WELDING RESEARCH: PROCEEDINGS OF THE 9TH INTERNATIONAL CONFERENCE, 2013, : 661 - 669
12345