Effects of electrode wear on weld quality of hot galvanization steel with high strength in resistance spot welding

被引：0

作者：

Zhang, Xuqiang ^{[1
]}

Zhang, Yansong ^{[2
]}

Liu, Yancong ^{[1
]}

机构：

[1] School of Mechanical Engineering, Petroleum University of China, Dongying 257061, China

[2] School of Mechanical Engineering and Power, Shanghai Jiaotong University, Shanghai 200030, China

来源：

Hanjie Xuebao/Transactions of the China Welding Institution | 2009年 / 30卷 / 10期

关键词：

Galvanizing - Welds - High strength steel - Welding electrodes - Wear resistance - Cracks;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Electrode wear characteristics were studied; the electrode life of un-coated steels was much lower and pitting changed more obviously than that of galvanization steels when welding. The effect of electrode wear on weld quality was studied; the expulsion was serious and more micro-cracks were grown at early electrode wear stage, which decreased weld quality greatly. And then based on the experiment results of effect of electrode wear on weld quality, welding technique step-current was established according to the current density that micro-crack degree was less than 0.25 mm to reduce the effect of electrode wear on weld quality.

引用

页码：5 / 8

共 50 条

[21] Spall Strength of Resistance Spot Weld for QP Steel
范春雷
马伯翰
陈大年
王焕然
马东方
Chinese Physics Letters, 2016, (03) : 77 - 81
[22] Analysis of Failure of Resistance Spot Welding for Advanced High Strength Steel
Noh, Wooram
Koh, Youngwoo
Chung, Kwansoo
Yang, Xin
NUMISHEET 2014: THE 9TH INTERNATIONAL CONFERENCE AND WORKSHOP ON NUMERICAL SIMULATION OF 3D SHEET METAL FORMING PROCESSES: PART A BENCHMARK PROBLEMS AND RESULTS AND PART B GENERAL PAPERS, 2013, 1567 : 595 - 598
[23] Effects of Steel Coatings on Electrode Life in Resistance Spot Welding of Galvannealed Steel Sheets
Hu, X.
Zou, G.
Dong, S. J.
Lee, M. Y.
Jung, J. P.
Zhou, Y.
MATERIALS TRANSACTIONS, 2010, 51 (12) : 2236 - 2242
[24] Development of next generation resistance spot welding technologies improving the weld properties of advanced high strength steel sheets
Joining and Strength Res. Dept., Steel Res. Lab., JFE Steel, Japan
JFE Tech. Rep., 20 (85-91):
[25] Microstructure and its hardness estimation of resistance spot weld of ultra-high strength steel sheets: development of resistance spot welding with pulsed current pattern for ultra-high strength steel sheets
Matsuda H.
Taniguchi K.
Ikeda R.
Oi K.
Matsuda, Hiroshi (h-matsuda@jfe-steel.co.jp), 1600, Taylor and Francis Ltd. (34): : 166 - 175
[26] Properties of resistance spot weld between high strength steel and aluminum alloy
School of Materials Science and Engineering, Shanghai Jiaotong University, Shanghai 200240, China
不详
Hanjie Xuebao, 2013, 9 (71-74+78):
[27] Resistance Spot Welding Process and Properties of Hot Dip Galvanized DP590 High Strength Steel
Liu, Ruxia
Rao, Mei
Liu, Shulong
Zhang, Jian
Luo, Guoqiang
ADVANCES IN MATERIALS PROCESSING, 2018, : 743 - 749
[28] Improvement of Cross-tension Strength Using Concave Electrode in Resistance Spot Welding of High-strength Steel Sheets
Watanabe, Goro
Amago, Tatsuyuki
Ishii, Yasuhiro
Takao, Hisaaki
Yasui, Toshiaki
Fukumoto, Masahiro
IRAGO CONFERENCE 2015: 360 DEGREE OUTLOOK ON CRITICAL SCIENTIFIC AND TECHNOLOGICAL CHALLENGES FOR A SUSTAINABLE SOCIETY, 2016, 1709
[29] Minimising electrode wear in resistance spot welding of aluminium alloys
Patil, R. R.
Tilak, C. J. K. Anurag
Srivastava, V.
De, A.
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2011, 16 (06) : 509 - 513
[30] Microstructure and its hardness estimation of resistance spot weld of ultra-high strength steel sheets-Development of resistance spot welding with pulsed current pattern for ultra-high strength steel sheets
MATSUDA H.
TANIGUCHI K.
IKEDA R.
OI K.
Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 2021, 38 (04): : 234 - 242

← 1 2 3 4 5 →