Microstructures and mechanical properties of (Ti,Cr)Al/Al2O 3 composites fabricated by reactive hot pressing from Ti, Al and Cr2O3

被引：0
|
作者：
机构：
[1] Zhu, Jianfeng
[2] Yang, Wenwen
[3] Wang, Fen
来源：
Zhu, J. (zhujf@sust.edu.cn) | 1600年 / Elsevier Ltd卷 / 567期
关键词：
Titanium aluminide composites reinforced with in situ formed Al 2O3 were fabricated by a reactive hot press method; using Cr2O3; Al and Ti powders as raw materials. The effect of Cr2O3 addition on the microstructures and mechanical properties of the (Ti; Cr)Al/Al2O3 composite was characterized. The results show that the TiAl matrix is refined gradually with increasing the amount of Cr2O3. The Vickers-hardness and densities of the (Ti; Cr)Al/Al2O3 composite increase gradually with increasing Cr2O3 content. When the Cr 2O3 content is 4.47 wt.%; the compressive strength; flexural strength and fracture toughness of the composite reach the maximum values of 1032 MPa; 634 MPa and 9.78 MPa m1/2; which are substantially higher than those of the monolithic TiAl based alloy by about 18%; 78%; and; 80.5%; respectively. The increase in mechanical properties for the (Ti; Cr)Al/Al2O3 composite is due to the toughening effect arising from the combination of Cr solid solution in TiAl matrix and in situ formed Al2O3. © 2013 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [41] Solubilities of Cr2O3 and Al2O3 in CoO
    Mohri, T
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1997, 105 (02) : 183 - 184
  • [42] Synthesis of Al2O3/TiAl In situ Composites from Ti-Al-TiO2-Cr-V2O5
    Zhang, Kun
    Wang, Fen
    Zhu, Jianfeng
    ECO-MATERIALS PROCESSING AND DESIGN XIII, 2012, 724 : 447 - 450
  • [43] Preparation of Cr2O3-Al2O3-Cr coatings on carbon steel by aluminothermic process based on Cr2O3 and Al system
    Zhou, Hong
    Wu, Shoujun
    Liu, Shuang
    Shen, Yan
    Yang, Baoshan
    Zheng, Xu
    ADVANCED TECHNOLOGIES IN MANUFACTURING, ENGINEERING AND MATERIALS, PTS 1-3, 2013, 774-776 : 560 - 563
  • [44] Solubilities of Cr2O3 and Al2O3 in CoO
    Mohri, T.
    Nippon Seramikkusu Kyokai Gakujutsu Ronbunshi/Journal of the Ceramic Society of Japan, 1997, 105 (1218): : 183 - 184
  • [45] MAGNETOELECTRIC EFFECTS IN CR2O3 AND (CR2O3)0.8.(AL2O3)0.2
    FONER, S
    HANABUSA, M
    JOURNAL OF APPLIED PHYSICS, 1963, 34 (04) : 1246 - &
  • [46] Microstructure and mechanical properties of Ti3(AI,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing
    Yuan FANG
    Xiaohua LIU
    Yuxia FENG
    Jianfeng ZHU
    Wei JIANG
    Journal of Advanced Ceramics, 2020, 9 (06) : 782 - 790
  • [47] Low cost Ti(Al,O)/Al2O3 and TixAly/Al2O3 composites
    Zhang, DL
    Cai, ZH
    Newby, M
    MATERIALS TECHNOLOGY, 2003, 18 (02) : 94 - 98
  • [48] Effect of Ni Doping on the Microstructure and Mechanical Properties of Ti/Al2O3 Composites Developed by Hot Pressing Sintering
    Liu, Lu-hao
    Wang, Zhi
    Shi, Guo-pu
    Feng, Shu-ai
    Ma, Yan
    INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND MATERIAL ENGINEERING (MSME 2014), 2014, : 44 - 48
  • [49] NONLINEARITY AND ELASTIC PROPERTIES OF CR(3+)AL2O3 AND TI(3+)AL2O3 LASER CRYSTALS
    AMARANATH, G
    BUDDHUDU, S
    MANDELIS, A
    SOLID STATE COMMUNICATIONS, 1994, 91 (09) : 761 - 763
  • [50] Microstructure, mechanical properties and formability of Ti/Al/Ti laminated composites fabricated by hot-pressing
    Cao, Miao
    Deng, Kun-kun
    Nie, Kai-bo
    Wang, Cui-ju
    Wang, Lifei
    Liang, Wei
    JOURNAL OF MANUFACTURING PROCESSES, 2020, 58 : 322 - 334
12345