Microstructures and mechanical properties of (Ti,Cr)Al/Al2O 3 composites fabricated by reactive hot pressing from Ti, Al and Cr2O3

被引：0
|
作者：
机构：
[1] Zhu, Jianfeng
[2] Yang, Wenwen
[3] Wang, Fen
来源：
Zhu, J. (zhujf@sust.edu.cn) | 1600年 / Elsevier Ltd卷 / 567期
关键词：
Titanium aluminide composites reinforced with in situ formed Al 2O3 were fabricated by a reactive hot press method; using Cr2O3; Al and Ti powders as raw materials. The effect of Cr2O3 addition on the microstructures and mechanical properties of the (Ti; Cr)Al/Al2O3 composite was characterized. The results show that the TiAl matrix is refined gradually with increasing the amount of Cr2O3. The Vickers-hardness and densities of the (Ti; Cr)Al/Al2O3 composite increase gradually with increasing Cr2O3 content. When the Cr 2O3 content is 4.47 wt.%; the compressive strength; flexural strength and fracture toughness of the composite reach the maximum values of 1032 MPa; 634 MPa and 9.78 MPa m1/2; which are substantially higher than those of the monolithic TiAl based alloy by about 18%; 78%; and; 80.5%; respectively. The increase in mechanical properties for the (Ti; Cr)Al/Al2O3 composite is due to the toughening effect arising from the combination of Cr solid solution in TiAl matrix and in situ formed Al2O3. © 2013 Elsevier B.V. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
Journal article (JA)
引用
收藏
相关论文
共 50 条
  • [1] Microstructures and mechanical properties of (Ti,Cr)Al/Al2O3 composites fabricated by reactive hot pressing from Ti, Al and Cr2O3
    Zhu, Jianfeng
    Yang, Wenwen
    Wang, Fen
    JOURNAL OF ALLOYS AND COMPOUNDS, 2013, 567 : 15 - 20
  • [2] Microstructure formation mechanism of (Al2O3+TiB2+Al3Ti)/Al composites fabricated by reactive hot pressing
    Wang, Guisong
    Geng, Lin
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 1439 - 1442
  • [3] Microstructures and mechanical properties of Ti3SiC2/TiC-Al2O3 composites synthesized by reactive hot pressing
    Cai, Yanzhi
    Yin, Hongfeng
    Pan, Liqing
    Chen, Panjun
    Sun, Gaolei
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 571 : 137 - 143
  • [4] Synthesis, microstructure and mechanical properties of (Ti,Mo)Al/Al2O3 in situ composites by reactive hot pressing
    Zhu, Jianfeng
    Peng, Haijun
    Wang, Fen
    JOURNAL OF MATERIALS RESEARCH, 2017, 32 (06) : 1129 - 1137
  • [5] Synthesis, microstructure and mechanical properties of (Ti,Mo)Al/Al2O3in situ composites by reactive hot pressing
    Jianfeng Zhu
    Haijun Peng
    Fen Wang
    Journal of Materials Research, 2017, 32 : 1129 - 1137
  • [6] Microstructures and Mechanical Properties of In Situ Al2O3/Al-Si Composites Fabricated by Reaction Hot Pressing
    El Oualid Mokhnache
    G. S. Wang
    L. Geng
    L. J. Huang
    Metallurgical and Materials Transactions B, 2014, 45 : 1965 - 1969
  • [7] Microstructures and Mechanical Properties of In Situ Al2O3/Al-Si Composites Fabricated by Reaction Hot Pressing
    Mokhnache, El Oualid
    Wang, G. S.
    Geng, L.
    Huang, L. J.
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2014, 45 (06): : 1965 - 1969
  • [8] Effect of Al2O3 on the microstructure and mechanical properties of Ti3AlC2/Al2O3 in situ composites synthesized by reactive hot pressing
    Zhu, J. F.
    Ye, L.
    He, L. H.
    CERAMICS INTERNATIONAL, 2012, 38 (07) : 5475 - 5479
  • [9] Effect of MoO3 on microstructure and mechanical properties of (Ti,Mo)Al/Al2O3 composites by in situ reactive hot pressing
    Wang, Fen
    Zhao, Yuanbo
    Yang, Chenhui
    Fan, Ningxia
    Zhu, Jianfeng
    CERAMICS INTERNATIONAL, 2016, 42 (01) : 1 - 8
  • [10] Reaction Synthesis of TiAl-Al2O3 Composites from Ti-Al-Cr2O3
    Zhu, Jianfeng
    Yang, Wenwen
    Du, Fangni
    MECHATRONICS AND INTELLIGENT MATERIALS, PTS 1 AND 2, 2011, 211-212 : 209 - 212
12345