Influence of ultimate strength of wire and depth of its riffling on cyclic resistance

被引：0

作者：

Burylev, V.I. ^{[1
]}

机构：

[1] NIImetiz, Magnitogorsk, Russia

来源：

Stal' | 2001年 / 05期

关键词：

Composition effects - Mathematical models - Metal working - Regression analysis - Strength of materials;

D O I：

暂无

中图分类号：

学科分类号：

摘要：

Meshes from preliminary riffled wire of carbon steel are used in vibroshakers with the alternating load for screening the lump and loose materials. Operation of the meshes have been investigated. Results of the investigations have shown that premature destruction of the meshes is connected with abrasive wear and fatigue. One of ways for improving the resistance of the wire to wear and fatigue destruction is increase in content of carbon in the steel. However, this leads to decrease in plasticity of the steel. Riffling of the wire has been provided. Results of testing have shown that Large riffling causes premature destruction. Optimal riffling has been determined.

引用

页码：46 / 47

共 50 条

[21] STATISTICAL ANALYSIS OF CAUSES OF NON-UNIFORMITY OF ULTIMATE TENSILE STRENGTH OF CABLE WIRE
NEDOVIZII, IN
PAVLOV, AM
TRIFONOV.RG
STAL IN ENGLISH-USSR, 1968, (12): : 1087 - +
[22] Cyclic Load Testing and Ultimate Failure Strength of Suture Anchors in the Acetabular Rim
Ruiz-Suarez, Michell
Aziz-Jacobo, Jorge
Barber, F. Alan
ARTHROSCOPY-THE JOURNAL OF ARTHROSCOPIC AND RELATED SURGERY, 2010, 26 (06): : 762 - 768
[23] Evaluation of resistance at supporting pulley of messenger wire and its influence on current collection characteristics
Contact Line Structures Laboratory, Power Supply Technology Division, United States
不详
不详
Q Rep RTRI (Jpn), 2009, 3 (137-143):
[24] Ultimate strength assessment of ship hull structures subjected to cyclic bending moments
Liu, Bin
Soares, C. Guedes
OCEAN ENGINEERING, 2020, 215
[25] DETERMINATION OF FATIGUE STRENGTH OF RESISTANCE WIRE STRAIN GAUGES
KOTELNIK.YP
INDUSTRIAL LABORATORY, 1969, 35 (04): : 600 - &
[26] Failure mechanism and ultimate strength of stiffened plates under extreme cyclic load
Liu W.
Cai Q.
Jin T.
Kang Z.
Li C.
Harbin Gongcheng Daxue Xuebao/Journal of Harbin Engineering University, 2023, 44 (08): : 1275 - 1282
[27] Characterization of debonding strength in steel-wire-reinforced aluminum and its influence on material fracture
Morasch, A.
Reeb, A.
Baier, H.
Weidenmann, K. A.
Schulze, V.
ENGINEERING FRACTURE MECHANICS, 2015, 141 : 242 - 259
[28] THE INFLUENCE OF MIDDLE FRAMES ON THE ULTIMATE STRENGTH OF PRESSURE CYLINDER SHELL
Wang Lin
Li Feng
OMAE 2009, VOL 2: STRUCTURES, SAFETY AND RELIABILITY, 2009, : 583 - 588
[29] Influence on miners' physiological parameters of ultimate environment and working strength
Cui Liqin
Li Yongjun
Zhao Shijun
PROGRESS IN SAFETY SCIENCE AND TECHNOLOGY, VOL 6, PTS A AND B, 2006, 6 : 539 - 542
[30] Influence of the Temperature on Ultimate Strength of 93WNiFe Alloy
Xu, Yingge
Wang, Liangliang
Wu, Zewei
MECHATRONICS AND INTELLIGENT MATERIALS III, PTS 1-3, 2013, 706-708 : 134 - 137

← 1 2 3 4 5 →