The stress-corrosion cracking susceptibility of near-α titanium alloy IMI 834 in presence of hot salt

被引：0
|
作者：
Pustode, Mangesh D. [1 ]
Raja, V.S. [1 ]
Paulose, Neeta [2 ]
机构：
[1] Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai 400076, India
[2] Gas Turbine Research Establishment (GTRE), Bangalore 560093, India
来源：
Corrosion Science | 2014年 / 82卷
关键词：
Stress corrosion cracking;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The hot salt stress corrosion cracking (HSSCC) behaviour of a near α titanium alloy, IMI 834, was studied using slow strain rate test method in the temperature range 250-450. °C. The alloy was found to be susceptible to HSSCC at 300. °C and above; and the susceptibility increased with an increase in the test temperature. The secondary cracks grew exponentially with temperature. HSSC cracks initiated at α/β interfaces and grew across the primary α grain and along the α/β interfaces. © 2014 Elsevier Ltd.
引用
收藏
页码：191 / 196
相关论文
共 50 条
  • [41] Stress-corrosion cracking susceptibility of various product forms of aluminum alloy 2519
    Kramer, LS
    Blair, TP
    Blough, SD
    Fisher, JJ
    Pickens, JR
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2002, 11 (06) : 645 - 650
  • [42] STRESS-CORROSION CRACKING OF AN ALLOY-STEEL
    PEPI, M
    CHAMPAGNE, V
    ADVANCED MATERIALS & PROCESSES, 1992, 142 (01): : 47 - 47
  • [43] Damage Micromechanisms In IMI-834 Titanium Alloy: Stress Triaxiality Effects
    Kumar, Jalaj
    Prasad, N. Eswara
    Kumar, Vikas
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2008, 61 (05) : 415 - 417
  • [44] STRESS-CORROSION CRACKING BEHAVIOR OF AN ALLICUMG ALLOY
    DORWARD, RC
    HASSE, KR
    CORROSION, 1987, 43 (07) : 408 - 413
  • [45] STRESS CORROSION CRACKING SUSCEPTIBILITY OF A TITANIUM ALLOY IN A NON-ELECTROLYTE
    SANDOZ, G
    NATURE, 1967, 214 (5084) : 166 - &
  • [46] ELECTROCHEMICAL MODEL FOR HOT-SALT STRESS-CORROSION OF TITANIUM-ALLOYS
    GARFINKL.M
    METALLURGICAL TRANSACTIONS, 1973, 4 (07): : 1677 - 1686
  • [47] Damage micromechanisms in IMI-834 titanium alloy: Stress triaxiality effects
    Jalaj Kumar
    N. Eswara Prasad
    Vikas Kumar
    Transactions of the Indian Institute of Metals, 2008, 61 : 415 - 417
  • [48] EFFECTS OF ALLOYING ELEMENTS ON SUSCEPTIBILITY TO STRESS-CORROSION CRACKING OF MARTENSITIC STEELS IN SALT WATER
    SANDOZ, G
    METALLURGICAL TRANSACTIONS, 1971, 2 (04): : 1055 - &
  • [49] Texture studies of hot compressed near alpha titanium alloy (IMI 834) at 1000°C with different strain rates
    Kodli, B. K.
    Saxena, K. K.
    Dey, S. R.
    Pancholi, V.
    Bhattacharjee, A.
    17TH INTERNATIONAL CONFERENCE ON TEXTURES OF MATERIALS (ICOTOM 17), 2015, 82
  • [50] Effect of Oxidation and Hot Corrosion on Stress Corrosion Cracking Susceptibility of Inconel 738 Alloy
    A. R. Patil
    S. T. Vagge
    Strength of Materials, 2023, 55 : 582 - 605
12345