The stress-corrosion cracking susceptibility of near-α titanium alloy IMI 834 in presence of hot salt

被引：0
|
作者：
Pustode, Mangesh D. [1 ]
Raja, V.S. [1 ]
Paulose, Neeta [2 ]
机构：
[1] Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai 400076, India
[2] Gas Turbine Research Establishment (GTRE), Bangalore 560093, India
来源：
Corrosion Science | 2014年 / 82卷
关键词：
Stress corrosion cracking;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The hot salt stress corrosion cracking (HSSCC) behaviour of a near α titanium alloy, IMI 834, was studied using slow strain rate test method in the temperature range 250-450. °C. The alloy was found to be susceptible to HSSCC at 300. °C and above; and the susceptibility increased with an increase in the test temperature. The secondary cracks grew exponentially with temperature. HSSC cracks initiated at α/β interfaces and grew across the primary α grain and along the α/β interfaces. © 2014 Elsevier Ltd.
引用
收藏
页码：191 / 196
相关论文
共 50 条
  • [21] AgCl-induced hot salt stress corrosion cracking in a titanium alloy
    Shi, Yitong
    Joseph, Sudha
    Saunders, Edward A.
    Sandala, Rebecca S.
    Walker, Adrian
    Lindley, Trevor C.
    Dye, David
    CORROSION SCIENCE, 2021, 187
  • [22] Dynamic strain aging in the intermediate temperature regime of near-α titanium alloy, IMI 834: Experimental and modeling
    Agrawal, Priyanka
    Karthikeyan, S.
    Makineni, Surendra Kumar
    Gault, Baptiste
    Banerjee, Dipankar
    ACTA MATERIALIA, 2022, 222
  • [23] Mechanism of Degradation of Titanium Alloy IMI 834 and Its Protection Under Hot Corrosion Conditions
    I. Gurrappa
    Oxidation of Metals, 2003, 59 : 321 - 322
  • [24] MARINE CORROSION STUDIES (STRESS-CORROSION CRACKING OF A TITANIUM ALLOY WELDMENT)
    BROWN, BF
    REPORT OF NRL PROGRESS, 1965, (OCT): : 35 - &
  • [25] Mechanism of degradation of titanium alloy IMI 834 and its protection under hot corrosion conditions
    Gurrappa, I
    OXIDATION OF METALS, 2003, 59 (3-4): : 321 - 332
  • [26] Study of Hot Salt Stress Corrosion Crack Initiation of Alloy IMI 834 by using DC Potential Drop Method
    Pustode, Mangesh D.
    Dewangan, Bhupendra
    Raja, V. S.
    Paulose, Neeta
    Babu, Narendra
    CORROSION SCIENCE AND TECHNOLOGY-KOREA, 2016, 15 (05): : 203 - 208
  • [27] STRESS-CORROSION CRACKING SUSCEPTIBILITY OF BETA-TITANIUM ALLOY 38-6-44
    CZYRKLIS, WF
    LEVY, M
    CORROSION, 1976, 32 (03) : 99 - 102
  • [28] Influence of thermomechanical processing on microstructural evolution in near-α alloy IMI834
    Wanjara, P
    Jahazi, M
    Monajati, H
    Yue, S
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 416 (1-2): : 300 - 311
  • [29] Hot salt stress corrosion cracking and corrosion fatigue of titanium alloys
    Cash, M
    Nicholls, JR
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 4, PTS 1 AND 2, 1997, 251-2 : 649 - 656
  • [30] Serrated flow behavior in a near alpha titanium alloy IMI 834
    Prasad, Kartik
    Varma, Vijay. K.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 486 (1-2): : 158 - 166
12345