The stress-corrosion cracking susceptibility of near-α titanium alloy IMI 834 in presence of hot salt

被引：0
|
作者：
Pustode, Mangesh D. [1 ]
Raja, V.S. [1 ]
Paulose, Neeta [2 ]
机构：
[1] Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Mumbai 400076, India
[2] Gas Turbine Research Establishment (GTRE), Bangalore 560093, India
来源：
Corrosion Science | 2014年 / 82卷
关键词：
Stress corrosion cracking;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The hot salt stress corrosion cracking (HSSCC) behaviour of a near α titanium alloy, IMI 834, was studied using slow strain rate test method in the temperature range 250-450. °C. The alloy was found to be susceptible to HSSCC at 300. °C and above; and the susceptibility increased with an increase in the test temperature. The secondary cracks grew exponentially with temperature. HSSC cracks initiated at α/β interfaces and grew across the primary α grain and along the α/β interfaces. © 2014 Elsevier Ltd.
引用
收藏
页码：191 / 196
相关论文
共 50 条
  • [1] The stress-corrosion cracking susceptibility of near-α titanium alloy IMI 834 in presence of hot salt
    Pustode, Mangesh D.
    Raja, V. S.
    Paulose, Neeta
    CORROSION SCIENCE, 2014, 82 : 191 - 196
  • [2] Modeling the hot working behavior of near-α titanium alloy IMI 834
    Balasundar, I.
    Raghu, T.
    Kashyap, B. P.
    PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2013, 23 (06) : 598 - 607
  • [3] Modeling the hot working behavior of near-α titanium alloy IMI 834
    I.Balasundar
    T.Raghu
    B.P.Kashyap
    Progress in Natural Science:Materials International, 2013, 23 (06) : 598 - 607
  • [4] Variability in Fatigue Life of Near-α Titanium Alloy IMI 834
    Bhandari, Litton
    Kumar, Jalaj
    Balasundar, I.
    Arora, Amit
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2021, 74 (04) : 979 - 989
  • [5] Variability in Fatigue Life of Near-α Titanium Alloy IMI 834
    Litton Bhandari
    Jalaj Kumar
    I. Balasundar
    Amit Arora
    Transactions of the Indian Institute of Metals, 2021, 74 : 979 - 989
  • [6] Hot working behavior of near-α alloy IMI834
    Wanjara, P
    Jahazi, M
    Monajati, H
    Yue, S
    Immarigeon, JP
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2005, 396 (1-2): : 50 - 60
  • [7] STRESS-CORROSION CRACKING OF A TITANIUM ALLOY
    不详
    ANTI-CORROSION, 1968, 15 (01): : 23 - &
  • [8] HOT-SALT STRESS-CORROSION CRACKING OF TITANIUM-ALLOYS
    SINIGAGLIA, D
    TACCANI, G
    VICENTINI, B
    CORROSION SCIENCE, 1978, 18 (09) : 781 - 796
  • [9] EFFECT OF INITIAL HYDROGEN CONTENT OF A TITANIUM-ALLOY ON SUSCEPTIBILITY TO HOT SALT STRESS-CORROSION
    GRAY, HR
    CORROSION, 1972, 28 (05) : 186 - &
  • [10] High-temperature fatigue damage mechanisms in near-α titanium alloy IMI 834
    Hardt, S
    Maier, HJ
    Christ, HJ
    INTERNATIONAL JOURNAL OF FATIGUE, 1999, 21 (08) : 779 - 789
12345