Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

被引：1

作者：

PENG H.-L. ^{[1
,2
]}

ZHANG Y.-X. ^{[3
]}

CHEN X. ^{[1
,2
]}

ZHANG H.-Q. ^{[3
]}

XUE J.-L. ^{[3
]}

GUO W. ^{[3
]}

机构：

[1] Shanghai Spaceflight Precision Machinery Institute, Shanghai

[2] Shanghai Engineering Technology Research Center of Near-net Shape Forming for Metallic Materials, Shanghai

[3] School of Mechanical Engineering and Automation, Beihang University, Beijing

来源：

Transactions of Nonferrous Metals Society of China (English Edition) | 2022年 / 32卷 / 03期

基金：

中国国家自然科学基金;

关键词：

brazing; C/C composites; microstructure; shear strength;

D O I：

10.1016/S1003-6326(22)65843-6

中图分类号：

学科分类号：

摘要：

The novel Ni-based brazing filler was used to join C/C composites. When brazing temperature increased from 1080 to 1100 °C, the wetting angle decreased from 23° to 14°, and the brazing filler had good wettability on the surface of C/C composites. The brazing seam of the brazed joint consisted of Ni(s,s) and Cr3C2 phases. As brazing temperature increased, lots of Cr3C2 phases were generated at the bonding interface, and the thick reaction layer was formed. When brazing temperature was 1120 °C, the shear strength of C/C joint reached the maximum value of 31.5 MPa. The fracture path extended in the C/C matrix close to the bonding interface. © 2022 The Nonferrous Metals Society of China

引用

页码：927 / 934

页数：7

共 50 条

[21] Microstructural evolution and mechanical property of a SiCf/SiC composite/Ni-based superalloy joint brazed with an Au-Cu-Ti filler
Yang, Jia
Zhang, Xunye
Ma, Guanglu
Lin, Panpan
Xu, Yanqiang
Lin, Tiesong
He, Peng
Long, Weimin
Li, Jian
JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2021, 41 (04) : 2312 - 2322
[22] Microstructure and properties of W-Cu/1Cr18Ni9 steel brazed joint with different Ni-based filler metals
Zhou, Yi
Xia, Chunzhi
Yang, Jun
Xu, Xiangping
Zou, Jiasheng
SCIENCE AND ENGINEERING OF COMPOSITE MATERIALS, 2018, 25 (03) : 463 - 472
[23] Microstructure evolution and mechanical properties of vacuum-brazed C/C composite with AgCuTi foil
Guo, Wei
Zhu, Ying
Wang, Lin
Qu, Ping
Kang, Hui
Chu, Paul K.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 564 : 192 - 198
[24] Microstructures and mechanical properties of TiAl/Ni-based superalloy joints brazed with Fe-based filler metal
Ren, H. S.
Xiong, H. P.
Ye, L.
Ren, X. Y.
Li, W. W.
Qin, R. Y.
WELDING IN THE WORLD, 2021, 65 (01) : 79 - 85
[25] Microstructure and mechanical properties of TiAl/Ni-based superalloy joints vacuum brazed with Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal
Bao Wan
Xiao-Qiang Li
Cun-Liang Pan
Dong-Yu Li
Sheng-Guan Qu
Chao Yang
RareMetals, 2021, 40 (08) : 2134 - 2142
[26] Microstructures and mechanical properties of TiAl/Ni-based superalloy joints brazed with Fe-based filler metal
H. S. Ren
H. P. Xiong
L. Ye
X. Y. Ren
W. W. Li
R. Y. Qin
Welding in the World, 2021, 65 : 79 - 85
[27] Microstructure and mechanical properties of TiAl/Ni-based superalloy joints vacuum brazed with Ti–Zr–Fe–Cu–Ni–Co–Mo filler metal
Bao Wan
Xiao-Qiang Li
Cun-Liang Pan
Dong-Yu Li
Sheng-Guan Qu
Chao Yang
Rare Metals, 2021, 40 : 2134 - 2142
[28] Effect of CNTs on microstructure and mechanical properties of TC4 and C/C composites brazed joint
Liu D.
Li X.
Zhao K.
Song Y.
Zhong S.
Song X.
1600, Harbin Research Institute of Welding (41): : 1 - 5
[29] Correlation between microstructure and mechanical properties of welding joint in 9% Ni steel with two types of Ni-based superalloy filler metals
Ji Yong Hwang
Kwangsu Choi
Hyo Yun Jung
The International Journal of Advanced Manufacturing Technology, 2022, 122 : 2761 - 2773
[30] Correlation between microstructure and mechanical properties of welding joint in 9% Ni steel with two types of Ni-based superalloy filler metals
Hwang, Ji Yong
Choi, Kwangsu
Jung, Hyo Yun
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2022, 122 (5-6): : 2761 - 2773

← 1 2 3 4 5 →