Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler

被引：1
|
作者：
PENG H.-L. [1 ,2 ]
ZHANG Y.-X. [3 ]
CHEN X. [1 ,2 ]
ZHANG H.-Q. [3 ]
XUE J.-L. [3 ]
GUO W. [3 ]
机构：
[1] Shanghai Spaceflight Precision Machinery Institute, Shanghai
[2] Shanghai Engineering Technology Research Center of Near-net Shape Forming for Metallic Materials, Shanghai
[3] School of Mechanical Engineering and Automation, Beihang University, Beijing
来源：
Transactions of Nonferrous Metals Society of China (English Edition) | 2022年 / 32卷 / 03期
基金：
中国国家自然科学基金;
关键词：
brazing; C/C composites; microstructure; shear strength;
D O I：
10.1016/S1003-6326(22)65843-6
中图分类号：
学科分类号：
摘要：
The novel Ni-based brazing filler was used to join C/C composites. When brazing temperature increased from 1080 to 1100 °C, the wetting angle decreased from 23° to 14°, and the brazing filler had good wettability on the surface of C/C composites. The brazing seam of the brazed joint consisted of Ni(s,s) and Cr3C2 phases. As brazing temperature increased, lots of Cr3C2 phases were generated at the bonding interface, and the thick reaction layer was formed. When brazing temperature was 1120 °C, the shear strength of C/C joint reached the maximum value of 31.5 MPa. The fracture path extended in the C/C matrix close to the bonding interface. © 2022 The Nonferrous Metals Society of China
引用
收藏
页码：927 / 934
页数：7
相关论文
共 50 条
  • [1] Microstructure and mechanical properties of C/C composite joint brazed with Ni-based filler
    Peng, He-li
    Zhang, Yong-xin
    Chen, Xu
    Zhang, Hong-qiang
    Xue, Jun-liang
    Guo, Wei
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2022, 32 (03) : 927 - 934
  • [2] Microstructure and properties of the C/C-superalloy brazed joint by Ni-based filler
    Xue, Junliang
    Zhang, Hongqiang
    Guo, Wei
    Zhu, Ying
    Cheng, Zhan
    Zhang, Lei
    Sun, Huawei
    Zhong, Sujuan
    Long, Weimin
    CERAMICS INTERNATIONAL, 2022, 48 (09) : 12549 - 12558
  • [3] Microstructure and properties of tungsten/steel joint brazed with Ni-based foil-type filler
    Liu, Wen-Sheng
    Liu, Shu-Hua
    Ma, Yun-Zhu
    Cai, Qing-Shan
    Liu, Hao-Yang
    Yu, Qiang
    Wu, Lei
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2014, 24 (12): : 3051 - 3058
  • [4] Mechanical properties and microstructure of SUS304 brazed joint with Ni-based filler metals added Cr powder
    Shohji, I
    Takayama, S
    Nakazawa, T
    Matsumoto, K
    Hikita, M
    ADVANCES IN FRACTURE AND STRENGTH, PTS 1- 4, 2005, 297-300 : 2767 - 2771
  • [5] Microstructure and Properties of Brazed Joint Between SiCf/SiC Composite and Ni-based Superalloy
    Yang J.
    Zhang X.
    Ma G.
    Lin P.
    Xu Y.
    Lin T.
    He P.
    Jixie Gongcheng Xuebao/Journal of Mechanical Engineering, 2021, 57 (12): : 161 - 168
  • [6] Microstructure and mechanical properties of the C/C composite and Nb joints brazed with an active Ag-based filler metal
    Zheng, K.
    Yang, Z. W.
    Wang, Y.
    Wang, D. P.
    CERAMICS INTERNATIONAL, 2022, 48 (07) : 9621 - 9630
  • [7] Microstructure and mechanical properties of Ni foam/stainless steel joint brazed using Ni-based alloy
    Heo, Hoejun
    Kim, Gyulin
    Kim, Dae Yeon
    Moon, Chanhee
    Kim, Kyung Chun
    Jung, Keeyoung
    Kang, Chung-Yun
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 740 : 63 - 70
  • [8] A study of the SiCf/SiC composite/Ni-based superalloy dissimilar joint brazed with a composite filler
    Yang, Jia
    Zhang, Xunye
    Ma, Guanglu
    Lin, Panpan
    Xu, Yanqiang
    Liu, Zhanguo
    Lin, Tiesong
    He, Peng
    Song, Kuijing
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 11 : 2114 - 2126
  • [9] Microstructure and mechanical properties of the SiC/Nb joint brazed using AgCuTi + B4C composite filler metal
    Li, Chun
    Huang, Caiyan
    Chen, Lei
    Si, Xiaoqing
    Chen, Zhe
    Qi, Junlei
    Huang, Yongxian
    Feng, Jicai
    Cao, Jian
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2019, 85
  • [10] Microstructure and Mechanical Properties of Vacuum Brazed NbSS/Nb5Si3 Composite Joints Using Ni-Based Filler Alloys
    Ren, X. Y.
    Xiong, H. P.
    Kang, Y. W.
    Pei, C.
    Chen, B.
    Cheng, Y. Y.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2019, 50A (11): : 5181 - 5190
12345