Microstructures and Mechanical Properties of Mg-4.5Gd- 2.6Nd-0.5Zn-0.5Zr New Casting Alloy

被引：0
|
作者：
Zhan, Liang [1 ,2 ]
Le, Qichi [2 ]
Feng, Zhijun [1 ]
Lou, Yanchun [1 ]
Li, Huawen [3 ]
机构：
[1] State Key Laboratory of Light Alloy Casting Technology for High-end Equipment, Shenyang Research Institute of Foundry Co. Ltd, Shenyang,110022, China
[2] Key Lab of Electromagnetic Processing of Materials, Ministry of Education, Northeastern University, Shenyang,110819, China
[3] AECC Zhong Chuan Transmission Machinery Co. Ltd, Changsha,410200, China
来源：
Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering | 2020年 / 49卷 / 08期
关键词：
The microstructure and mechanical properties of Mg-4.5Gd-2.6Nd-0.5Zn-0.5Zr; a novel magnesium cast alloy; were investigated. The microstructure of the as-cast experimental alloy is determined to be composed of near-equiaxed α-Mg; Mg12(Nd; Gd); and Mg3Gd phases. After optimizing the heat treatment parameters; the YS; UTS; and A values reach 205 MPa; 325; MPa; and 4.0% at room temperature; and; 145; 245; and 18.5% at 250 oC. The strengthening mechanism of this alloy was also investigated. The fracture surfaces of Mg-4.5Gd-2.6Nd-0.5Zn-0.5Zr during tensile tests demonstrate that brittle fracture occurs at room temperature; and ductile fracture occurs at 250 oC accompanied by appearance of many dimples and tear ridges. Copyright © 2020; Northwest Institute for Nonferrous Metal Research. Published by Science Press. All rights reserved;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
引用
收藏
页码：2644 / 2648
相关论文
共 50 条
  • [31] Microstructures and mechanical properties of a hot-extruded Mg-8Gd-3Yb-1.2Zn-0.5Zr (wt%) alloy
    Li, Baishun
    Guan, Kai
    Yang, Qiang
    Niu, Xiaodong
    Zhang, Dongdong
    Lv, Shuhui
    Meng, Fanzhi
    Huang, Yuanding
    Hort, Norbert
    Meng, Jian
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 776 : 666 - 678
  • [32] Microstructures of extruded Mg-12Gd-1Zn-0.5Zr and Mg-12Gd-4Y-1Zn-0.5Zr alloys
    Li, J. P.
    Yang, Z.
    Liu, T.
    Guo, Y. C.
    Xia, F.
    Yang, J. M.
    Liang, M. X.
    SCRIPTA MATERIALIA, 2007, 56 (02) : 137 - 140
  • [33] Microstructure and mechanical properties of Mg-5Gd-2Y-2Zn-0.5Zr alloy
    Meng, L. G.
    Fang, C. F.
    Peng, P.
    Mi, S. B.
    Zhu, Q.
    Li, N. P.
    Hao, H.
    Zhang, X. G.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 (01) : 14 - 19
  • [34] Effects of extrusion ratio and annealing treatment on the mechanical properties and microstructure of a Mg-11Gd-4.5Y-1Nd-1.5Zn-0.5Zr (wt%) alloy
    Yu, Zijian
    Huang, Yuanding
    Gan, Weimin
    Zhong, Zhengye
    Hort, Norbert
    Meng, Jian
    JOURNAL OF MATERIALS SCIENCE, 2017, 52 (11) : 6670 - 6686
  • [35] Effects of Nd on Microstructure Mechanical Properties of Mg-10Gd-3Y-0.5Zr Alloy
    Yan, Jing-long
    Li, Quan-an
    Zhang, Xing-yuan
    Zhou, Yao
    INTERNATIONAL CONFERENCE ON MATERIAL SCIENCE AND CIVIL ENGINEERING, MSCE 2016, 2016, : 294 - 300
  • [36] Effects of Extrusion Ratio on the Microstructure, Texture and Mechanical Properties of Mg-2.5Nd-0.5Zn-0.5Zr Alloy Sheets
    Wang, Songhui
    Pan, Jinqi
    Xie, Wenzhuo
    Yang, Jianlei
    Zhang, Wencong
    Chen, Wenzhen
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (11) : 4834 - 4845
  • [37] Effects of Extrusion Ratio on the Microstructure, Texture and Mechanical Properties of Mg-2.5Nd-0.5Zn-0.5Zr Alloy Sheets
    Songhui Wang
    Jinqi Pan
    Wenzhuo Xie
    Jianlei Yang
    Wencong Zhang
    Wenzhen Chen
    Journal of Materials Engineering and Performance, 2023, 32 : 4834 - 4845
  • [38] Microstructure and mechanical properties of a peak-aged Mg-5Y-2.5Nd-1.5Gd-0.5Zr casting alloy
    Tian, Zheng
    Yang, Qiang
    Guan, Kai
    Meng, Jian
    Cao, Zhanyi
    JOURNAL OF ALLOYS AND COMPOUNDS, 2018, 731 : 704 - 713
  • [39] Influence of Nd addition on microstructures and mechanical properties of a hot-extruded Mg-6.0Zn-0.5Zr (wt.%) alloy
    Lv, Shuhui
    Meng, Fanzhi
    Lu, Xiaoling
    Yang, Qiang
    Qiu, Xin
    Duan, Qian
    Meng, Jian
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 806 : 1166 - 1179
  • [40] Effect of heat treatment on the microstructures and mechanical properties of the sand-cast Mg-2.7Nd-0.6Zn-0.5Zr alloy
    Wu, D.
    Ma, Q.
    Chen, R. S.
    Ke, W.
    JOURNAL OF MAGNESIUM AND ALLOYS, 2014, 2 (01) : 20 - 26
12345