Mechanisms of La2Ce2O7/YSZ Double-Ceramic-Layer Thermal Barrier Coatings against Volcanic Ash Corrosion

被引：0
|
作者：
Xia, Jie [1 ]
Du, Xuelin [1 ]
Xiao, Yiqi [2 ]
Zhang, Ling [3 ]
Wu, Rudder Tse [4 ]
Matsushita, Yoshitaka [5 ]
机构：
[1] Hunan Inst Technol, Dept Mech Engn, Hengyang 421002, Peoples R China
[2] Hunan Inst Engn, Dept Mech Engn, Xiangtan 411104, Peoples R China
[3] Chongqing Univ, Coll Mat Sci & Engn, Int Joint Lab Light Alloys MOE, Chongqing 400044, Peoples R China
[4] Natl Inst Mat Sci, High Temp Mat Grp, 1 2 1 Sengen, Tsukuba, Ibaraki 3050044, Japan
[5] Natl Inst Mat Sci, Chem Anal & Xray Diffract Grp, 1 2 1 Sengen, Tsukuba, Ibaraki 3050044, Japan
来源：
COATINGS | 2024年 / 14卷 / 07期
关键词：
thermal barrier coating; calcium-magnesium-alumina-silicate (CMAS); volcanic ash; La2Ce2O7; high-temperature corrosion; corrosion mechanism; DEGRADATION; RESISTANCE; BEHAVIOR; PROGRESS; YSZ;
D O I：
10.3390/coatings14070877
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
To tackle the ever-increasing operating temperature of aero-engines, a La2Ce2O7 (LCO)/yttria partially stabilized zirconia (YSZ) double-layer thermal barrier coating (TBC) was investigated. The LCO/YSZ double-layer samples were annealed with volcanic ash (VA) at 1250 degrees C to assess their stability in comparison with that of standard single-layer YSZ. The findings showed that the double-layer system exhibited greater resistance to VA damage than the single-layer YSZ coating. The corrosion mechanism was characterized by a rapid crystallization reaction between LCO and VA, where the kinetics of the solution's reprecipitation reaction outpaced the penetration rate into the coating's open pores.
引用
收藏
页数：17
相关论文
共 50 条
  • [1] Solid Particle Erosion Behavior of La2Ce2O7/YSZ Double-Ceramic-Layer and Traditional YSZ Thermal Barrier Coatings at High Temperature
    Zhao, Xianli
    Liu, Wei
    Li, Cong
    Yan, Gang
    Wang, Qianwen
    Yang, Li
    Zhou, Yichun
    COATINGS, 2022, 12 (11)
  • [2] Thermal cycling behavior of La2Ce2O7/8YSZ double-ceramic-layer thermal barrier coatings prepared by atmospheric plasma spraying
    Ma, Wen
    Dong, Hongying
    Guo, Hongbo
    Gong, Shengkai
    Zheng, Xuebin
    SURFACE & COATINGS TECHNOLOGY, 2010, 204 (21-22): : 3366 - 3370
  • [3] Investigating Hot corrosion, CMAS, and Thermal Shock Behaviour of Double-layer YSZ/La2Ce2O7 + YSZ Thermal Barrier Coatings
    Pakseresht, Amirhossein
    Ariharan, S.
    Sekar, Anusha
    Parchoviansky, Milan
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2024, : 809 - 822
  • [4] Effect of Ceramic Layer Thickness Ratio on Thermal Shock Resistance of La2Ce2O7/YSZ Thermal Barrier Coatings
    Ren Xiaoxue
    Jiang Peng
    Fan Xueling
    Wang Tiejun
    RARE METAL MATERIALS AND ENGINEERING, 2018, 47 (12) : 3703 - 3709
  • [5] Novel thermal barrier coatings based on La2Ce2O7/8YSZ double-ceramic-layer systems deposited by electron beam physical vapor deposition
    Ma, Wen
    Gong, Shengkai
    Li, Hefei
    Xu, Huibin
    SURFACE & COATINGS TECHNOLOGY, 2008, 202 (12): : 2704 - 2708
  • [6] Mechanical Properties and CMAS Corrosion Resistance of La2Ce2O7/YSZ Composite Thermal Barrier Coatings
    Kang, Y. X.
    Bai, Y.
    Bao, C. G.
    Fan, W.
    Zhang, L.
    INTERNATIONAL THERMAL SPRAY CONFERENCE AND EXPOSITION (ITSC 2018), 2018, : 75 - 78
  • [7] Biaxial stress in La2Ce2O7/YSZ thermal barrier coatings for oxidation evolution
    Zhao, Xianli
    Wang, Qianwen
    Liu, Wei
    Yan, Gang
    Li, Cong
    Yang, Li
    Zhou, Yichun
    SURFACE & COATINGS TECHNOLOGY, 2022, 447
  • [8] Biaxial stress in La2Ce2O7/YSZ thermal barrier coatings for oxidation evolution
    Zhao, Xianli
    Wang, Qianwen
    Liu, Wei
    Yan, Gang
    Li, Cong
    Yang, Li
    Zhou, Yichun
    Surface and Coatings Technology, 2022, 447
  • [9] Hot corrosion properties of plasma sprayed La2Ce2O7/YSZ vis-a-vis La2Ce2O7/cluster paired zirconia thermal barrier coatings
    Lashmi, P. G.
    Balaji, N.
    Kumar, S. Senthil
    Aruna, S. T.
    SURFACE & COATINGS TECHNOLOGY, 2021, 409
  • [10] Double-ceramic-layer thermal barrier coatings based on La2(Zr0.7Ce0.3)2O7/La2Ce2O7 deposited by electron beam-physical vapor deposition
    Xu, Z. H.
    He, L. M.
    Mu, R. D.
    He, S. M.
    Huang, G. H.
    Cao, X. Q.
    APPLIED SURFACE SCIENCE, 2010, 256 (11) : 3661 - 3668
12345