Mechanisms of La2Ce2O7/YSZ Double-Ceramic-Layer Thermal Barrier Coatings against Volcanic Ash Corrosion

被引：0
|
作者：
Xia, Jie [1 ]
Du, Xuelin [1 ]
Xiao, Yiqi [2 ]
Zhang, Ling [3 ]
Wu, Rudder Tse [4 ]
Matsushita, Yoshitaka [5 ]
机构：
[1] Hunan Inst Technol, Dept Mech Engn, Hengyang 421002, Peoples R China
[2] Hunan Inst Engn, Dept Mech Engn, Xiangtan 411104, Peoples R China
[3] Chongqing Univ, Coll Mat Sci & Engn, Int Joint Lab Light Alloys MOE, Chongqing 400044, Peoples R China
[4] Natl Inst Mat Sci, High Temp Mat Grp, 1 2 1 Sengen, Tsukuba, Ibaraki 3050044, Japan
[5] Natl Inst Mat Sci, Chem Anal & Xray Diffract Grp, 1 2 1 Sengen, Tsukuba, Ibaraki 3050044, Japan
来源：
COATINGS | 2024年 / 14卷 / 07期
关键词：
thermal barrier coating; calcium-magnesium-alumina-silicate (CMAS); volcanic ash; La2Ce2O7; high-temperature corrosion; corrosion mechanism; DEGRADATION; RESISTANCE; BEHAVIOR; PROGRESS; YSZ;
D O I：
10.3390/coatings14070877
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
To tackle the ever-increasing operating temperature of aero-engines, a La2Ce2O7 (LCO)/yttria partially stabilized zirconia (YSZ) double-layer thermal barrier coating (TBC) was investigated. The LCO/YSZ double-layer samples were annealed with volcanic ash (VA) at 1250 degrees C to assess their stability in comparison with that of standard single-layer YSZ. The findings showed that the double-layer system exhibited greater resistance to VA damage than the single-layer YSZ coating. The corrosion mechanism was characterized by a rapid crystallization reaction between LCO and VA, where the kinetics of the solution's reprecipitation reaction outpaced the penetration rate into the coating's open pores.
引用
收藏
页数：17
相关论文
共 50 条
  • [41] Thermophysical properties of solution precursor plasma-sprayed La2Ce2O7 thermal barrier coatings
    Feng, Bei-Bei
    Wang, Yi
    Jia, Qiang
    Huang, Wei
    Suo, Hong-Li
    Ma, Wen
    RARE METALS, 2019, 38 (07) : 689 - 694
  • [42] Preparation of 8YSZ and Double-ceramic-layer La2Zr2O7/8YSZ Thermal Barrier Coatings on GH4169 Superalloy Substrates and Their Static High Temperature Oxidation Behaviour
    Wang, Liang
    Wang, You
    Sun, Xiaoguang
    MATERIALS PERFORMANCE, MODELING AND SIMULATION, 2013, 749 : 617 - +
  • [43] Thermophysical properties of solution precursor plasma-sprayed La2Ce2O7 thermal barrier coatings
    Bei-Bei Feng
    Yi Wang
    Qiang Jia
    Wei Huang
    Hong-Li Suo
    Wen Ma
    Rare Metals, 2019, 38 (07) : 689 - 694
  • [44] Thermal stability of plasma-sprayed La2Ce2O7/YSZ composite coating
    State Key Laboratory for Mechanical Behavior of Materials, School of Materials Science and Engineering, Xi'An Jiaotong University, Xi'an, Shaanxi Province
    710049, China
    Ceram Int, 1600, 7 (7950-7961):
  • [45] Thermal stability of plasma-sprayed La2Ce2O7/YSZ composite coating
    Xu, Ya-Xin
    Liu, Tao
    Yang, Guan-Jun
    Li, Chang-Jiu
    CERAMICS INTERNATIONAL, 2016, 42 (07) : 7950 - 7961
  • [46] Thermal cycling behavior of YSZ and La2(Zr0.7Ce0.3)2O7 as double-ceramic-layer systems EB-PVD TBCs
    Xu, Zhenhua
    He, Limin
    Mu, Rende
    Lu, Feng
    He, Shimei
    Cao, Xueqiang
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 525 : 87 - 96
  • [47] Plasma-sprayed La2Ce2O7 thermal barrier coatings against calcium-magnesium-alumina-silicate penetration
    Gao, Lihua
    Guo, Hongbo
    Gong, Shengkai
    Xu, Huibin
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2014, 34 (10) : 2553 - 2561
  • [48] Hot corrosion behavior of plasma sprayed La2Ce2O7/YSZ thermal barrier composite coating in the presence of Sulfate and Vanadate molten Salts
    Dehkharghani, Amir Mohammad Fathi
    Rahimipour, Mohammad Reza
    Zakeri, Mohammad
    CORROSION SCIENCE, 2021, 183 (183)
  • [49] Thermal cycling behavior and bonding strength of single-ceramic-layer Sm2Zr2O7 and double-ceramic-layer Sm2Zr2O7/8YSZ thermal barrier coatings deposited by atmospheric plasma spraying
    Wu, H. X.
    Ma, Z.
    Liu, L.
    Liu, Y. B.
    Wang, D. Y.
    CERAMICS INTERNATIONAL, 2016, 42 (11) : 12922 - 12927
  • [50] Influence of Gd2O3 addition on thermophysical properties of La2Ce2O7 ceramics for thermal barrier coatings
    Zhang Hong-song
    Chen Xiao-ge
    Li Gang
    Wang Xin-li
    Dang Xu-dan
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2012, 32 (14) : 3693 - 3700
12345