Strain-rate dependent fatigue behavior of T91 steel at 550 °C of liquid lead-bismuth eutectic

被引：0
|
作者：
Xue, Baoquan [1 ,2 ]
Tan, Jibo [1 ]
Wu, Xinqiang [1 ]
Zhang, Ziyu [1 ]
Wang, Xiang [1 ]
Ke, Wei [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Steel; Fatigue; Oxidation; Embrittlement; LOW-CYCLE FATIGUE; FERRITIC-MARTENSITIC STEEL; METAL EMBRITTLEMENT; SUSCEPTIBILITY; ENVIRONMENT;
D O I：
10.1016/j.corsci.2024.112433
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Low cycle fatigue behavior of T91 steel was investigated in oxygen saturated liquid lead-bismuth eutectic (LBE) at 550 degrees C with different strain rates. The fatigue life of T91 steel decreases by about 85 % with decreasing strain rate from 0.4 % to 0.004 %/s. The crack tip was carefully analyzed by advanced characterization. The intergranular oxidation resistance of T91 steel decreases at lower strain rates, leading to fatigue failure mode changes from quasi-cleavage to cleavage cracking. Notably, the cracks (>200 mu m) propagate along the recrystallization grain boundaries with Pb/Bi segregation but without oxides detected at 0.004 %/s.
引用
收藏
页数：16
相关论文
共 50 条
  • [41] New insight of the enhanced oxidation resistance of T91 steel in 450 °C liquid lead-bismuth eutectic by adding Al and Si element
    Feng, Shaowu
    Dai, Hailong
    Sun, Xingyue
    Jiang, Kejian
    Qiu, Zhi
    Chen, Xu
    Chen, Gang
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2025, 204 : 29 - 46
  • [42] Creep-to-rupture of T91 steel in static liquid lead-bismuth eutectic: Effects of cyclic temperature and oxygen environment
    Zhou, Zhikun
    Tian, Chenwen
    Zhang, Qun
    Du, Juan
    Zhang, Chuang
    Liu, Hengjie
    Gong, Xing
    Wahab, Magd Abdel
    Chen, Ziguang
    ENGINEERING FRACTURE MECHANICS, 2024, 311
  • [43] Corrosion behavior of 410 stainless steel in flowing lead-bismuth eutectic alloy at 550 °C
    Chen, Gang
    Ju, Na
    Lei, Yucheng
    Wang, Dan
    Zhu, Qiang
    Li, Tianqing
    JOURNAL OF NUCLEAR MATERIALS, 2019, 522 : 168 - 183
  • [44] ToF-SIMS investigation of absorption of lead and bismuth in T91 steel deformed in liquid lead bismuth eutectic
    Serre, Ingrid Proriol
    Vogt, Jean-Bernard
    Nuns, Nicolas
    APPLIED SURFACE SCIENCE, 2019, 471 : 36 - 42
  • [45] Effects of pre-exposure and simulated corrosion pits on liquid metal embrittlement of T91 steel exposed to liquid lead-bismuth eutectic at 350 °C
    Gong, Xing
    Chen, Haitao
    Wang, Zhaohui
    Peng, Xuhao
    Chen, Ziguang
    Li, Yongchun
    Du, Juan
    Yu, Xiaofei
    Yin, Yuan
    Journal of Nuclear Materials, 2022, 563
  • [46] Effects of pre-exposure and simulated corrosion "pits" on liquid metal embrittlement of T91 steel exposed to liquid lead-bismuth eutectic at 350 °C
    Gong, Xing
    Chen, Haitao
    Wang, Zhaohui
    Peng, Xuhao
    Chen, Ziguang
    Li, Yongchun
    Du, Juan
    Yu, Xiaofei
    Yin, Yuan
    JOURNAL OF NUCLEAR MATERIALS, 2022, 563
  • [47] Liquid metal embrittlement of the T91 steel in lead bismuth eutectic: The role of loading rate and of the oxygen content in the liquid metal
    Ye, Changqing
    Vogt, Jean-Bernard
    Serre, Ingrid Proriol
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 608 : 242 - 248
  • [48] Crevice corrosion behavior of 316L austenitic steel in static liquid lead-bismuth eutectic at 550°C
    Huang, Yuji
    Meng, Fanqiang
    Shi, Jiajian
    Zhang, Lijun
    Yuan, Rui
    Chen, Yingxue
    Zhang, Feifei
    JOURNAL OF NUCLEAR MATERIALS, 2025, 603
  • [49] A comparative study on the compatibility of liquid lead-gold eutectic and liquid lead-bismuth eutectic with T91 and SS 316LN steels
    Dai, Y.
    Gao, W.
    Zhang, T.
    Platacis, E.
    Heinitz, S.
    Thomsen, K.
    JOURNAL OF NUCLEAR MATERIALS, 2012, 431 (1-3) : 113 - 119
  • [50] Compatibility of ferritic-martensitic steel T91 welds with liquid lead-bismuth eutectic: Comparison between TIG and EB welds
    Van den Bosch, J.
    Coen, G.
    Van Renterghem, W.
    Almazouzi, A.
    JOURNAL OF NUCLEAR MATERIALS, 2010, 396 (01) : 57 - 64
12345