Strain-rate dependent fatigue behavior of T91 steel at 550 °C of liquid lead-bismuth eutectic

被引：0
|
作者：
Xue, Baoquan [1 ,2 ]
Tan, Jibo [1 ]
Wu, Xinqiang [1 ]
Zhang, Ziyu [1 ]
Wang, Xiang [1 ]
Ke, Wei [1 ]
机构：
[1] Chinese Acad Sci, Inst Met Res, CAS Key Lab Nucl Mat & Safety Assessment, Liaoning Key Lab Safety & Assessment Tech Nucl Mat, Shenyang 110016, Peoples R China
[2] Univ Sci & Technol China, Sch Mat Sci & Engn, Hefei 230026, Peoples R China
来源：
CORROSION SCIENCE | 2024年 / 240卷
基金：
中国国家自然科学基金;
关键词：
Steel; Fatigue; Oxidation; Embrittlement; LOW-CYCLE FATIGUE; FERRITIC-MARTENSITIC STEEL; METAL EMBRITTLEMENT; SUSCEPTIBILITY; ENVIRONMENT;
D O I：
10.1016/j.corsci.2024.112433
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Low cycle fatigue behavior of T91 steel was investigated in oxygen saturated liquid lead-bismuth eutectic (LBE) at 550 degrees C with different strain rates. The fatigue life of T91 steel decreases by about 85 % with decreasing strain rate from 0.4 % to 0.004 %/s. The crack tip was carefully analyzed by advanced characterization. The intergranular oxidation resistance of T91 steel decreases at lower strain rates, leading to fatigue failure mode changes from quasi-cleavage to cleavage cracking. Notably, the cracks (>200 mu m) propagate along the recrystallization grain boundaries with Pb/Bi segregation but without oxides detected at 0.004 %/s.
引用
收藏
页数：16
相关论文
共 50 条
  • [21] Mechanical behavior of coated T91 steel in contact with lead-bismuth liquid alloy at 300 °C
    Serre, I. Proriol
    Diop, I.
    David, N.
    Vilasi, M.
    Vogt, J. -B.
    SURFACE & COATINGS TECHNOLOGY, 2011, 205 (19): : 4521 - 4527
  • [22] Liquid metal embrittlement susceptibility of T91 steel by lead-bismuth
    Auger, T
    Lorang, G
    SCRIPTA MATERIALIA, 2005, 52 (12) : 1323 - 1328
  • [23] Effect of cold rolling on the oxidation resistance of T91 steel in oxygen-saturated stagnant liquid lead-bismuth eutectic at 450 °C and 550 °C
    Dong, Hong
    Ye, Zhongfei
    Wang, Pei
    Li, Dianzhong
    Zhang, Yutuo
    Li, Yiyi
    JOURNAL OF NUCLEAR MATERIALS, 2016, 476 : 213 - 217
  • [24] CHARACTERISTICS OF OXIDES ON A PRE-STRESSED T91 STEEL EXPOSED TO LIQUID LEAD-BISMUTH EUTECTIC
    Di Gabriele, Fosca
    Lorincik, Jan
    Halodova, Patricie
    Duchon, Jan
    Hojna, Anna
    METAL 2017: 26TH INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2017, : 688 - 692
  • [25] Corrosion characteristics of T91 steel in lead-bismuth eutectic with different oxygen concentrations at 500°C
    Tian, Shujian
    Pang, Yongqiang
    Jiang, Zhizhong
    Luo, Lin
    Xiao, Zunqi
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (01): : 134 - 142
  • [26] Approach of the corrosion behaviour of T91 steel in lead or lead-bismuth liquid bath
    Maître, A
    François, M
    Podor, R
    Gachon, JC
    HIGH TEMPERATURE CORROSION AND PROTECTION OF MATERIALS 6, PRT 1 AND 2, PROCEEDINGS, 2004, 461-464 : 1141 - 1148
  • [27] Study on Liquid Metal Embrittlement Susceptibility of T91 Exposed to Liquid Lead-Bismuth Eutectic
    Zhang, Jie
    Qin, Bo
    Long, Bin
    METALS, 2025, 15 (02)
  • [28] Fracture mechanics behavior of the T91 martensitic steel in contact with liquid lead-bismuth eutectic for application in an accelerator driven system
    Auger, T.
    Gorse, D.
    Hamouche-Hadjem, Z.
    Van den Bosch, J.
    Coen, G.
    Almazouzi, A.
    Hojna, A.
    Dalikova, K.
    Di Gabriele, F.
    Serrano, M.
    Gessi, A.
    Agostini, P.
    Vogt, J. -B.
    Serre, I.
    JOURNAL OF NUCLEAR MATERIALS, 2011, 415 (03) : 293 - 301
  • [29] Cracking and exfoliation behavior of oxide scale on T91 steel under different tensile stresses in oxygen-controlled lead-bismuth eutectic at 550 °C
    Luo, Lin
    Jiang, Zhizhong
    Xiao, Zunqi
    Huang, Qunying
    CORROSION SCIENCE, 2021, 183
  • [30] The role of oxide films in preventing liquid metal embrittlement of T91 steel exposed to liquid lead-bismuth eutectic
    Gong, Xing
    Marmy, Pierre
    Yin, Yuan
    JOURNAL OF NUCLEAR MATERIALS, 2018, 509 : 401 - 407
12345