Cavitation erosion of the AA7050 aluminum alloy in 3.5 wt% NaCl solution-Part 1: mitigating effect by corrosion

被引：7

作者：

Pan, Cheng-Cheng ^{[1
]}

Xia, Da -Hai ^{[1
]}

Hou, Meng -Yang ^{[1
]}

Qin, Zhenbo ^{[1
]}

Xu, Yunze ^{[2
]}

Behnamian, Yashar ^{[3
]}

Hu, Wenbin ^{[1
]}

机构：

[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300350, Peoples R China

[2] Dalian Univ Technol, Sch Naval Architecture & Ocean Engn, Dalian 116024, Peoples R China

[3] Univ Alberta, Dept Chem & Mat Engn, Edmonton, AB T6G 1H9, Canada

来源：

CORROSION SCIENCE | 2024年 / 232卷

基金：

中国国家自然科学基金;

关键词：

Negative synergistic effect; Cavitation erosion -corrosion; Stress concentration; AA7050; EBSD; TEM; OXIDE-FILM; BEHAVIOR; BRONZE; STEEL; COATINGS; COLLAPSE;

D O I：

10.1016/j.corsci.2024.112012

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The corrosion in 3.5 wt% NaCl solution caused a mitigated weight loss of the aluminum alloy 7050 (AA7050) under cavitation erosion condition. The mechanism was observed using high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), electro back-scattered diffraction (EBSD), and potentiodynamic polarization. Both in deionized water and in 3.5 wt% NaCl solution, the cavitation erosion degradation of the AA7050 was mainly attributed to fatigue fracture like peeling off of surface layer materials. The corrosion significantly mitigated the weight loss of AA7050 under cavitation erosion condition because the loose surface oxide film (generated by corrosion) dissipated the cavitation impact energy and therefore alleviated the stress concentration on the alloy surface.

引用

下载

页数：15

共 50 条

[1] Cavitation Corrosion of Anodized Aluminum Alloy in 3.5% NaCl Solution
Yong, X.
Hou, C.
Wu, J.
Ji, J.
Zhang, Z.
Wang, J.
CORROSION, 2011, 67 (04) : 0450031 - 0450036
[2] Synergistic effect between cavitation erosion and corrosion of Monel K500 alloy in 3.5 wt% NaCl solution
He, Zebang
Qin, Zhenbo
Gao, Zhiming
Wu, Zhong
Hu, Wenbin
MATERIALS CHARACTERIZATION, 2023, 205
[3] Synergistic Erosion and Corrosion Behavior of AA5052 Aluminum Alloy in 3.5 wt% NaCl Solution Under Various Impingement Angles
Azarian N.S.
Ghasemi H.M.
Monshi M.R.
Journal of Bio- and Tribo-Corrosion, 2015, 1 (02)
[4] Effect of pre-corrosion on the cavitation erosion performance of two aluminum bronzes in 3.5% NaCl solution
Song, Q. N.
Wang, Y.
Wu, Y. Q.
Zhu, X. Y.
Xu, N.
Zhang, G. Y.
Bao, Y. F.
Zhao, J. H.
Zhao, L. J.
Gao, Y.
Qiao, Y. X.
MATERIALS TODAY COMMUNICATIONS, 2023, 37
[5] The role of Ti in cavitation erosion and corrosion behaviours of NAB alloy in 3.5 % NaCl solution
Song, S. L.
Li, D. G.
Chen, D. R.
Liang, P.
JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 919
[6] Study on cavitation erosion-corrosion behavior of CoCrFeNiMoCu0.1 high entropy alloy in 3.5 wt% NaCl solution
Li, Liang
Nie, Sijia
Li, Chengtao
Chen, Xin
Qiao, Yanxin
Ma, Rongyao
Chen, Zhilin
Zhang, Lianmin
Cui, Jie
ULTRASONICS SONOCHEMISTRY, 2024, 110
[7] Effect of Sulfide Concentration on the Corrosion and Cavitation Erosion Behavior of a Manganese-Aluminum Bronze in 3.5% NaCl Solution
Q. N. Song
N. Xu
X. Jiang
Y. Liu
Y. Tong
J. S. Li
Y. F. Bao
Y. X. Qiao
Journal of Materials Engineering and Performance, 2019, 28 : 4053 - 4064
[8] Effect of Sulfide Concentration on the Corrosion and Cavitation Erosion Behavior of a Manganese-Aluminum Bronze in 3.5% NaCl Solution
Song, Q. N.
Xu, N.
Jiang, X.
Liu, Y.
Tong, Y.
Li, J. S.
Bao, Y. F.
Qiao, Y. X.
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2019, 28 (07) : 4053 - 4064
[9] The corrosion behavior of chromated AA2024 aluminum alloy in 3.5% NaCl solution
Zhou, Yong
Zhang, Pei
Xiong, Jinping
Yan, Fuan
ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (06) : 879 - 887
[10] EFFECT OF PH ON STRESS-CORROSION CRACKING OF 7050-T7451 ALUMINUM-ALLOY IN 3.5 WT-PERCENT NACL SOLUTION
TSAI, WT
DUH, JB
YEH, JJ
LEE, JT
CHANG, YC
CORROSION, 1990, 46 (06) : 444 - 449

← 1 2 3 4 5 →