Cavitation erosion of the AA7050 aluminum alloy in 3.5 wt% NaCl solution-Part 1: mitigating effect by corrosion

被引：7
|
作者：
Pan, Cheng-Cheng [1 ]
Xia, Da -Hai [1 ]
Hou, Meng -Yang [1 ]
Qin, Zhenbo [1 ]
Xu, Yunze [2 ]
Behnamian, Yashar [3 ]
Hu, Wenbin [1 ]
机构：
[1] Tianjin Univ, Sch Mat Sci & Engn, Tianjin 300350, Peoples R China
[2] Dalian Univ Technol, Sch Naval Architecture & Ocean Engn, Dalian 116024, Peoples R China
[3] Univ Alberta, Dept Chem & Mat Engn, Edmonton, AB T6G 1H9, Canada
来源：
CORROSION SCIENCE | 2024年 / 232卷
基金：
中国国家自然科学基金;
关键词：
Negative synergistic effect; Cavitation erosion -corrosion; Stress concentration; AA7050; EBSD; TEM; OXIDE-FILM; BEHAVIOR; BRONZE; STEEL; COATINGS; COLLAPSE;
D O I：
10.1016/j.corsci.2024.112012
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion in 3.5 wt% NaCl solution caused a mitigated weight loss of the aluminum alloy 7050 (AA7050) under cavitation erosion condition. The mechanism was observed using high-resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), electro back-scattered diffraction (EBSD), and potentiodynamic polarization. Both in deionized water and in 3.5 wt% NaCl solution, the cavitation erosion degradation of the AA7050 was mainly attributed to fatigue fracture like peeling off of surface layer materials. The corrosion significantly mitigated the weight loss of AA7050 under cavitation erosion condition because the loose surface oxide film (generated by corrosion) dissipated the cavitation impact energy and therefore alleviated the stress concentration on the alloy surface.
引用
下载
收藏
页数：15
相关论文
共 50 条
  • [21] The coupling effect of cavitation-erosion and corrosion for HVOF sprayed Cu-based medium-entropy alloy coating in 3.5 wt.% NaCl solution
    Cheng, Jie
    Wu, Yuping
    Zhu, Shuaishuai
    Hong, Sheng
    Cheng, Jiangbo
    Wang, Yujun
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 25 : 2936 - 2947
  • [22] Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution
    Venugopal, A.
    Sreekumar, K.
    Raja, V. S.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2012, 43A (09): : 3135 - 3148
  • [23] Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution
    A. Venugopal
    K. Sreekumar
    V. S. Raja
    Metallurgical and Materials Transactions A, 2012, 43 : 3135 - 3148
  • [24] Effect of Microstructure on the Localized Corrosion and Stress Corrosion Behaviours of Plasma-Electrolytic-Oxidation-Treated AA7075 Aluminum Alloy Forging in 3.5wt.% NaCl Solution
    Venugopal, A.
    Panda, Rajiv
    Manwatkar, Sushant
    Sreekumar, K.
    Ramakrishna, L.
    Sundararajan, G.
    INTERNATIONAL JOURNAL OF CORROSION, 2012, 2012
  • [25] Effect of micro arc oxidation treatment on localized corrosion behaviour of AA7075 aluminum alloy in 3.5% NaCl solution
    Venugopal, A.
    Panda, Rajiv
    Manwatkar, Sushant
    Sreekumar, K.
    Krishna, L. Rama
    Sundararajan, G.
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (03) : 700 - 710
  • [26] Corrosion and cavitation erosion behaviors of the manganese-aluminum-bronze cladding layer prepared by MIG in 3.5% NaCl solution
    Song, Q. N.
    Zhang, H. N.
    Li, H. L.
    Hong, H.
    Sun, S. Y.
    Xu, N.
    Zhang, G. Y.
    Bao, Y. F.
    Qiao, Y. X.
    MATERIALS TODAY COMMUNICATIONS, 2022, 31
  • [27] Corrosion Wear Properties of 7055 Aluminum Alloy in 3.5% NaCl Solution
    Song X.
    Wang Y.
    Zhang P.
    Cao L.
    Xie Y.
    Zhao J.
    Wang, Youqiang (wyq1970301@126.com), 1600, Science Press (40): : 73 - 81
  • [28] Galvanic corrosion behavior between ADC12 aluminum alloy and copper in 3.5 wt% NaCl solution
    Cheng, Tiancai
    Huang, Hualiang
    Huang, Gangliang
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2022, 927
  • [29] Effects of Ce, Sm and Yb on cavitation erosion of NAB alloy in 3.5% NaCl solution
    Li, D. G.
    Song, S. L.
    Chen, D. R.
    Liang, P.
    ULTRASONICS SONOCHEMISTRY, 2022, 88
  • [30] The crystallographic orientation dependent anisotropic corrosion behavior of aluminum in 3.5 wt% NaCl solution
    Jin, Haini
    Sui, Yudong
    Yu, Xiaohua
    Feng, Jing
    Jiang, Yehua
    Wang, Qudong
    Sun, Wenwen
    JOURNAL OF ELECTROANALYTICAL CHEMISTRY, 2023, 946
12345