FURTHER INTERPRETATION OF SINTERING DATA IN ZIRCONIA URANIA MIXED-OXIDE POWDER COMPACTS

被引：0
|
作者：
DAS, P
CHOUDHURY, R
机构：
[1] Research and Development Centre for Iron and Steel, IISCO Sub-Centre, Burnpur, Burdwan, West Bengal
来源：
JOURNAL OF NUCLEAR MATERIALS | 1990年 / 174卷 / 01期
关键词：
D O I：
10.1016/0022-3115(90)90423-K
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Sintering studies of zirconia-urania mixed oxide powder compacts (in steps of 5.0% urania up to a maximum of 20.0% addition) were carried out at temperatures of 1000-1400°C for various soaking periods. The sintering rate with respect to temperature versus temperature plot attained a maximum at the phase transformation temperature of zirconia. This temperature was independent of the amount of urania addition. Sintering data were re-analysed and it was observed that solid solution formation is not likely to occur and sintering of like particles of zirconia influences the overall densification of the mixed oxide compacts. © 1990.
引用
收藏
页码：76 / 79
页数：4
相关论文
共 50 条
  • [41] High-temperature Pressurized Sintering of Yttria-stabilized Tetragonal Zirconia Powder Compacts by 28-GHz Microwave Irradiation
    Tai K.
    Kumagai T.
    Funtai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy, 2018, 65 (09): : 566 - 571
  • [42] RADIATION-THERMAL SINTERING OF ZIRCONIA POWDER COMPACTS UNDER CONDITIONS OF BILATERAL HEATING USING BEAMS OF LOW-ENERGY ELECTRONS
    Ghyngazov, S. A.
    Frangulyan, T. S.
    Chernyavskii, A. V.
    Goreev, A. K.
    Naiden, E. P.
    RUSSIAN PHYSICS JOURNAL, 2015, 58 (02) : 188 - 191
  • [43] MIXED-OXIDE FUEL FABRICATION TECHNOLOGY AND EXPERIENCE AT THE BELGONUCLEAIRE AND CFCA PLANTS AND FURTHER DEVELOPMENTS FOR THE MELOX PLANT
    HAAS, D
    VANDERGHEYNST, A
    VANVLIET, J
    LORENZELLI, R
    NIGON, JL
    NUCLEAR TECHNOLOGY, 1994, 106 (01) : 60 - 82
  • [44] Radiation-Thermal Sintering of Zirconia Powder Compacts Under Conditions of Bilateral Heating Using Beams of Low-Energy Electrons
    S. A. Ghyngazov
    T. S. Frangulyan
    A. V. Chernyavskii
    A. K. Goreev
    E. P. Naiden
    Russian Physics Journal, 2015, 58 : 188 - 191
  • [45] MIXED-OXIDE FUEL MICROSTRUCTURAL DATA SUGGESTING MODIFICATION OF 3-REGION MODEL
    HILBERT, RF
    BLACK, TJ
    RUBIN, BF
    STEPHEN, JD
    TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1972, 15 (02): : 750 - +
  • [46] High temperature sintering of SiC with oxide additives:: IV.: Powder beds and the influence of vaporization on the behaviour of SiC compacts
    Baud, S
    Thévenot, F
    Chatillon, C
    JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2003, 23 (01) : 29 - 36
  • [47] URANIUM-PLUTONIUM REDISTRIBUTION IN MIXED-OXIDE FUELS - MODEL PREDICTIONS AND FUEL PIN DATA
    MELDE, GF
    AMERICAN CERAMIC SOCIETY BULLETIN, 1972, 51 (04): : 387 - &
  • [48] RELATION BETWEEN NICKEL PARTICLE-SIZE AND UNEQUAL INTERDIFFUSION ON SINTERING PROCESS FOR FE-NI BINARY MIXED POWDER COMPACTS
    HANATATE, Y
    MITANI, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1978, 42 (07) : 643 - 649
  • [49] INFLUENCE OF NI CONTENT ON SINTERING BEHAVIOR OF CU-14 WT-PERCENT-AL-NI TERNARY MIXED POWDER COMPACTS
    SUZUKI, K
    MITANI, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1980, 44 (01) : 37 - 43
  • [50] Behavior of oxide film at interface between particles of Al-Mg alloy powder compacts prepared by pulse electric current sintering
    Xie, GQ
    Ohashi, O
    Yamaguchi, N
    Song, MG
    Mitsuishi, K
    Furuya, K
    Noda, T
    JAPANESE JOURNAL OF APPLIED PHYSICS PART 1-REGULAR PAPERS SHORT NOTES & REVIEW PAPERS, 2003, 42 (7B): : 4725 - 4728
12345