FURTHER INTERPRETATION OF SINTERING DATA IN ZIRCONIA URANIA MIXED-OXIDE POWDER COMPACTS

被引：0
|
作者：
DAS, P
CHOUDHURY, R
机构：
[1] Research and Development Centre for Iron and Steel, IISCO Sub-Centre, Burnpur, Burdwan, West Bengal
来源：
JOURNAL OF NUCLEAR MATERIALS | 1990年 / 174卷 / 01期
关键词：
D O I：
10.1016/0022-3115(90)90423-K
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Sintering studies of zirconia-urania mixed oxide powder compacts (in steps of 5.0% urania up to a maximum of 20.0% addition) were carried out at temperatures of 1000-1400°C for various soaking periods. The sintering rate with respect to temperature versus temperature plot attained a maximum at the phase transformation temperature of zirconia. This temperature was independent of the amount of urania addition. Sintering data were re-analysed and it was observed that solid solution formation is not likely to occur and sintering of like particles of zirconia influences the overall densification of the mixed oxide compacts. © 1990.
引用
收藏
页码：76 / 79
页数：4
相关论文
共 50 条
  • [21] Enhancement of sintering of injection molded ferrous mixed powder compacts by silane treatment
    Takekawa, J
    MATERIALS TRANSACTIONS JIM, 1996, 37 (02): : 157 - 162
  • [22] The role of the native oxide shell on the microwave sintering of copper metal powder compacts
    Mahmoud, Morsi M.
    Link, Guido
    Thumm, Manfred
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 627 : 231 - 237
  • [23] OXYGEN-CHEMISORPTION ON TITANIA ZIRCONIA MIXED-OXIDE SUPPORTED VANADIUM-OXIDE CATALYSTS
    REDDY, BM
    MANOHAR, B
    REDDY, EP
    LANGMUIR, 1993, 9 (07) : 1781 - 1785
  • [24] Composite powder and compacts of iron/iron oxide type produced by mechanosynthesis and reactive sintering
    Marinca, T. F.
    Neamtu, B. V.
    Popa, F.
    Chicinas, I.
    Isnard, O.
    ADVANCED MATERIALS AND STRUCTURES V, 2014, 216 : 29 - 34
  • [25] RAMAN-SPECTROSCOPY CHARACTERIZATION OF MOLYBDENA SUPPORTED ON TITANIA-ZIRCONIA MIXED-OXIDE
    MICIUKIEWICZ, J
    MANG, T
    KNOZINGER, H
    APPLIED CATALYSIS A-GENERAL, 1995, 122 (02) : 151 - 159
  • [26] TRANSIENT PERFORMANCE OF MIXED-OXIDE POWDER FUEL WITH UP TO 60 PERCENT MELTING
    THOMAS, GR
    FIELD, JH
    TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1969, 12 (01): : 343 - &
  • [27] Solid state sintering (3). Experimental study on grain and pore growth, and densification of superfine zirconia powder compacts
    Shi, Jianlin
    Huaxue Gongcheng/Chemical Engineering, 26 (01): : 1 - 13
  • [28] PHASE RELATIONSHIP AND THE DENITRIDATION DURING THE SINTERING PROCESS OF THE TIN-NI MIXED POWDER COMPACTS
    FUKUHARA, M
    MITANI, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1979, 43 (03) : 169 - 174
  • [29] THE PHASE RELATIONSHIP AND DENITRIFICATION DURING THE SINTERING PROCESS OF TIN-NI MIXED POWDER COMPACTS
    FUKUHARA, M
    MITANI, H
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1980, 21 (04): : 211 - 218
  • [30] SINTERING MECHANISM IN MIXED POWDER COMPACTS OF FE-CU-C TERNARY-SYSTEM
    MAJIMA, K
    MITANI, H
    TRANSACTIONS OF THE JAPAN INSTITUTE OF METALS, 1977, 18 (10): : 663 - 672
12345