THE FATIGUE CRACK-GROWTH RATE IN L-72 AL-ALLOY PLATE SPECIMENS WITH COLD-WORKED HOLES

被引：11

作者：

ARORA, PR ^{[1
]}

DATTAGURU, B ^{[1
]}

HANDE, HSS ^{[1
]}

机构：

[1] INDIAN INST SCI,DEPT AEROSP ENGN,BANGALORE 560012,KARNATAKA,INDIA

来源：

ENGINEERING FRACTURE MECHANICS | 1992年 / 42卷 / 06期

关键词：

21;

D O I：

10.1016/0013-7944(92)90138-5

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

A fatigue crack growth rate study has been carried out on L-72 aluminium alloy plate specimens with and without cold worked holes. The cold worked specimens showed significantly increased fatigue fife compared to unworked specimens. Computer software is developed to evaluate the stress intensity factor for non-uniform stress distributions using Green's function approach. The exponents for the Paris equation in the stable crack growth region for cold worked and unworked specimens are 1.26 and 3.15 respectively. The reduction in exponent value indicates the retardation in crack growth rate. An SEM study indicates more plastic deformation at the edge of the hole for unworked samples as compared to the worked samples during the crack initiation period.

引用

页码：989 / 1000

页数：12

共 50 条

[31] Short fatigue crack growth in an aircraft Al-alloy of a 7075 type after shot peening
Cerny, Ivo
Sis, Jiri
Mikulova, Dagmar
SURFACE & COATINGS TECHNOLOGY, 2014, 243 : 20 - 27
[32] Fatigue behaviour and crack growth rate of cryorolled Al 7075 alloy
Das, Prosenjit
Jayaganthan, R.
Chowdhury, T.
Singh, I. V.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (24): : 7124 - 7132
[33] Fatigue Crack Growth Rate of an Al-Cu-Mg Alloy
He, Jun
Liu, Yilun
Liu, Chi
Wang, Qing
Ma, Liyong
4TH INTERNATIONAL CONFERENCE ON ADVANCES IN ENERGY RESOURCES AND ENVIRONMENT ENGINEERING, 2019, 237
[34] EFFECTS OF STRESS WAVE FORM AND SUPERPOSITION OF VIBRATORY STRESSES ON CYCLIC SCC CRACK-GROWTH BEHAVIOR IN AN AL-ALLOY
KOMAI, K
MINOSHIMA, K
BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1985, 28 (244): : 2211 - 2218
[35] Evaluation of Overloading and Crack Closure Effects on Fatigue Crack Growth in an Aircraft 7075-T7351 Al-Alloy
Cerny, Ivo
Mikulova, Dagmar
ADVANCES IN FRACTURE AND DAMAGE MECHANICS XII, 2014, 577-578 : 325 - 328
[36] FATIGUE CRACK-GROWTH AND FRACTURE-TOUGHNESS BEHAVIOR OF AN AL-LI-CU ALLOY
JATA, KV
STARKE, EA
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (06): : 1011 - 1026
[37] EFFECT OF TEMPERATURE AND COLD WORK ON THE CRACK-GROWTH RATE OF ALLOY-600 IN PRIMARY WATER
REBAK, RB
XIA, Z
SZKLARSKASMIALOWSKA, Z
CORROSION, 1995, 51 (09) : 689 - 697
[38] SLOW CRACK-GROWTH IN 18MN-4CR COLD-WORKED AUSTENITIC STEEL UNDER STATIC LOAD IN GASEOUS-HYDROGEN
AKHURST, KN
BAKER, TJ
MATERIALS SCIENCE AND TECHNOLOGY, 1985, 1 (05) : 373 - 379
[39] THE EFFECTS OF FREQUENCY AND R-RATIO ON FATIGUE CRACK-GROWTH BEHAVIOR IN AL-LI-CU-MG ALLOY (8090) PLATE
KEMP, RMJ
WILSON, RN
GREGSON, PJ
FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1992, 15 (03) : 291 - 308
[40] Fatigue crack growth of composite patch repaired Al-alloy plates under variable amplitude loading
Seriari, Fatima Zohra
Benachour, Mustapha
Benguediab, Mohamed
FRATTURA ED INTEGRITA STRUTTURALE, 2018, (43): : 43 - 56

← 1 2 3 4 5 →