THE FATIGUE CRACK-GROWTH RATE IN L-72 AL-ALLOY PLATE SPECIMENS WITH COLD-WORKED HOLES

被引：11
|
作者：
ARORA, PR [1 ]
DATTAGURU, B [1 ]
HANDE, HSS [1 ]
机构：
[1] INDIAN INST SCI,DEPT AEROSP ENGN,BANGALORE 560012,KARNATAKA,INDIA
来源：
ENGINEERING FRACTURE MECHANICS | 1992年 / 42卷 / 06期
关键词：
21;
D O I：
10.1016/0013-7944(92)90138-5
中图分类号：
O3 [力学];
学科分类号：
08 ; 0801 ;
摘要：
A fatigue crack growth rate study has been carried out on L-72 aluminium alloy plate specimens with and without cold worked holes. The cold worked specimens showed significantly increased fatigue fife compared to unworked specimens. Computer software is developed to evaluate the stress intensity factor for non-uniform stress distributions using Green's function approach. The exponents for the Paris equation in the stable crack growth region for cold worked and unworked specimens are 1.26 and 3.15 respectively. The reduction in exponent value indicates the retardation in crack growth rate. An SEM study indicates more plastic deformation at the edge of the hole for unworked samples as compared to the worked samples during the crack initiation period.
引用
收藏
页码：989 / 1000
页数：12
相关论文
共 50 条
  • [21] ACOUSTIC-EMISSION BEHAVIOR DURING CRACK-GROWTH OF 7075-T651 AL-ALLOY
    BLANCHETTE, Y
    DICKSON, JI
    BASSIM, MN
    ENGINEERING FRACTURE MECHANICS, 1986, 24 (05) : 647 - 656
  • [22] CHARACTERISTICS OF SURFACE CRACK-GROWTH IN ROTATING BENDING TESTS OF AGE-HARDENED OR ANNEALED AL-ALLOY
    NISITANI, H
    KAWAGOISHI, N
    BULLETIN OF THE JSME-JAPAN SOCIETY OF MECHANICAL ENGINEERS, 1985, 28 (237): : 385 - 391
  • [23] THE FATIGUE CRACK-GROWTH BEHAVIOR OF THE AL-CU-LI ALLOY WELDALITE 049
    BLANKENSHIP, CP
    STARKE, EA
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1991, 14 (01) : 103 - 114
  • [24] Reconstitution of fatigue crack growth in Al-alloy 2024-T3 open-hole specimens using microfractographic techniques
    de Matos, PFP
    Moreira, PMGP
    Nedbal, I
    de Castro, PMST
    ENGINEERING FRACTURE MECHANICS, 2005, 72 (14) : 2232 - 2246
  • [25] MICROSTRUCTURAL INFLUENCE ON FATIGUE CRACK-GROWTH NEAR THRESHOLD IN 7075-AL ALLOY
    RENAUD, P
    VIOLAN, P
    PETIT, J
    FERTON, D
    SCRIPTA METALLURGICA, 1982, 16 (12): : 1311 - 1316
  • [26] THE MICROMECHANISMS OF FATIGUE CRACK-GROWTH IN A COMMERCIAL AL-ZN-MG-CU ALLOY
    NIX, KJ
    FLOWER, HM
    ACTA METALLURGICA, 1982, 30 (08): : 1549 - 1559
  • [27] THE INFLUENCE OF ENVIRONMENT ON FATIGUE CRACK-GROWTH OF AN FE3AL, CR ALLOY
    CASTAGNA, A
    STOLOFF, NS
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (04): : 673 - 678
  • [28] FATIGUE CRACK-GROWTH TRANSITIONS IN TI-6AL-4V ALLOY
    RAVICHANDRAN, KS
    DWARAKADASA, ES
    SCRIPTA METALLURGICA, 1989, 23 (10): : 1685 - 1690
  • [29] FATIGUE CRACK GROWTH IN HELIUM-IMPLANTED, ANNEALED AND COLD-WORKED TYPE-316 STAINLESS-STEEL
    SERPAN, CZ
    SMITH, HH
    PIEPER, AG
    TRANSACTIONS OF THE AMERICAN NUCLEAR SOCIETY, 1972, 15 (02): : 721 - +
  • [30] TRENDS IN FATIGUE-CRACK GROWTH FOR THE 2024 Al-ALLOY AFTER A SINGLE TENSILE OVERLOAD
    Zhang, Chunguo
    Lei, Beibei
    Liu, Rongwei
    Huo, Fengfeng
    MATERIALI IN TEHNOLOGIJE, 2018, 52 (06): : 703 - 710
12345