EVOLUTION RATES OF SIO FROM CAO-SIO2-AL2O3 SLAG MELTED IN A GRAPHITE CRUCIBLE AND DISSOLUTION RATES OF CARBON IN SLAG

被引：0
|
作者：
SHIMOO, T
SHIBATA, Y
KIMURA, H
机构：
来源：
JOURNAL OF THE JAPAN INSTITUTE OF METALS | 1980年 / 44卷 / 11期
关键词：
D O I：
10.2320/jinstmet1952.44.11_1231
中图分类号：
学科分类号：
摘要：
SiO evolution was generally controlled by the breaking of Si-O bonds but in the range of small alpha (SiO//2) value, the transport of silica also affected the rate. Dissolution of carbon proceeded slowly and its rate varied from 2 multiplied by 10** minus **5 to 5 multiplied by 10** minus **5 mol. m** minus **2. S** minus **1 at 1873 K.
引用
收藏
页码：1231 / 1238
页数：8
相关论文
共 50 条
  • [1] EVOLUTION RATES OF MG AND SIO FROM CAO-SIO2-MGO SLAG MELTED IN A GRAPHITE CRUCIBLE
    SHIMOO, T
    ANDO, S
    KIMURA, H
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1983, 47 (02) : 114 - 120
  • [2] Dissolution Behavior of Indium in CaO-SiO2-Al2O3 Slag
    Ko, Kyu Yeol
    Park, Joo Hyun
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2011, 42 (06): : 1224 - 1230
  • [3] Dissolution Behavior of Indium in CaO-SiO2-Al2O3 Slag
    Kyu Yeol Ko
    Joo Hyun Park
    Metallurgical and Materials Transactions B, 2011, 42 : 1224 - 1230
  • [4] Dissolution of Carbon-Containing Species in CaO-SiO2-Al2O3 Slag
    Li, Qiuju
    Liang, Cong
    Han, Bowen
    ISIJ INTERNATIONAL, 2024, 64 (06) : 928 - 934
  • [5] Erratum to: Dissolution Behavior of Indium in CaO-SiO2-Al2O3 Slag
    Kyu Yeol Ko
    Joo Hyun Park
    Metallurgical and Materials Transactions B, 2015, 46 : 531 - 531
  • [6] Comparative study of oxide inclusion dissolution in CaO-SiO2-Al2O3 slag
    Monaghan, BJ
    Chen, L
    Sorbe, J
    IRONMAKING & STEELMAKING, 2005, 32 (03) : 258 - 264
  • [7] Surface kinetics of nitrogen dissolution and its correlation to the slag structure in the CaO-SiO2, CaO-Al2O3, and CaO-SiO2-Al2O3 slag system
    Han, Seung-Min
    Park, Jin-Gyun
    Sohn, Il
    JOURNAL OF NON-CRYSTALLINE SOLIDS, 2011, 357 (15) : 2868 - 2875
  • [8] In-situ observation on dissolution of CaO-SiO2-Al2O3 complex inclusions in refining slag
    Gu, Yu-die
    Ren, Ying
    Zhang, Li-feng
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2025, 32 (02) : 376 - 387
  • [9] Wettability of Solid Metals by Molten CaO-SiO2-Al2O3 Slag
    Parry, G.
    Ostrovski, O.
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2008, 39 (05): : 681 - 689
  • [10] Wettability of Solid Metals by Molten CaO-SiO2-Al2O3 Slag
    G. Parry
    O. Ostrovski
    Metallurgical and Materials Transactions B, 2008, 39 : 681 - 689
12345