Evaluation for Weld Residual Stress and Operating Stress around Weld Region of the CRDM Nozzle in Reactor Vessel Upper Head

Primary water stress corrosion cracking (PWSCC) has been observed around the weld region of control rod drive mechanism (CRDM) nozzles in nuclear power plants overseas. The weld has a J-shaped groove and it connects the CRDM nozzle with the reactor vessel upper head (RVUH). It is a dissimilar metal weld (DMW), because the CRDM is made of alloy 600 and the RVUH is made of carbon steel. In this study, finite element analysis (FEA) was performed to estimate the stress condition around the weld region. Generally, it is known that a high tensile region is more susceptible to PWSCC. FEA was performed as for the condition of welding, hydrostatic test and normal operation successively to observe how the residual stress changes due to plant condition. The FEA results show that a high tensile stress region is formed around the weld starting point on the inner surface and around the weld stop point on the outer surface.