RADIATION-INDUCED CRYSTALLINITY CHANGES AND MELTING BEHAVIOR OF DRAWN ISOTACTIC POLYPROPYLENE

被引：33
|
作者：
KOSTOSKI, D
STOJANOVIC, Z
机构：
[1] The Institute of Nuclear Sciences, Vinča, P.O. Box 522
来源：
POLYMER DEGRADATION AND STABILITY | 1995年 / 47卷 / 03期
关键词：
D O I：
10.1016/0141-3910(94)00126-X
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
Wide-angle X-ray diffraction (WAXD) and differential scanning calorimetry (DSC) measurements were used to study the effect of low absorbed doses of gamma radiation, up to 200kGy, on oriented isotactic polypropylene (iPP). The WAXD and DSC measurements on the irradiated samples were performed after an aging of only 16 h at room temperature. The crystallinity of irradiated samples was found to increase, while the peak melting temperature decreased with absorbed dose. The results of WAXD and DSC measurements are explained in terms of the scission of tie molecules followed by the growth of new thin crystal lamellae.
引用
收藏
页码：353 / 356
页数：4
相关论文
共 50 条
  • [31] DOUBLE-MELTING BEHAVIOR OF BETA PHASE OF ISOTACTIC POLYPROPYLENE
    FUJIWARA, Y
    COLLOID AND POLYMER SCIENCE, 1975, 253 (04) : 273 - 282
  • [32] Melting behavior in blends of isotactic polypropylene and a liquid crystalline polymer
    Torre, J
    Cortázar, M
    Gómez, M
    Ellis, G
    Marco, C
    JOURNAL OF POLYMER SCIENCE PART B-POLYMER PHYSICS, 2004, 42 (10) : 1949 - 1959
  • [33] Effect of β-nucleating agents on crystallization and melting behavior of isotactic polypropylene
    Xiao, Wenchang
    Wu, Peiyi
    Feng, Jiachun
    Journal of Applied Polymer Science, 2008, 108 (05): : 3370 - 3379
  • [34] MELTING BEHAVIOR OF ISOTACTIC POLYPROPYLENE ISOTHERMALLY CRYSTALLIZED FROM THE MELT
    YADAV, YS
    JAIN, PC
    POLYMER, 1986, 27 (05) : 721 - 727
  • [35] Stress-strain behavior of cold-drawn isotactic polypropylene subjected to various drawn histories
    Nitta, Koh-Hei
    Nomura, Hitomi
    POLYMER, 2014, 55 (25) : 6614 - 6622
  • [36] Radiation-induced craft copolymerization of 2-vinylpyridine and styrene onto isotactic polypropylene fiber
    Kaur, I
    Kumar, S
    Chauhan, GS
    Misra, BN
    JOURNAL OF APPLIED POLYMER SCIENCE, 1999, 73 (14) : 2959 - 2969
  • [37] Radiation-induced graft copolymerization of 2-vinylpyridine and styrene onto isotactic polypropylene fiber
    Department of Chemistry, Himachal Pradesh University, Summer Hill, Shimla-171005, India
    不详
    J. Appl. Polym. Sci., 14 (2959-2969):
  • [38] Changes of crystallinity and spherulite morphology in isotactic polypropylene after rolling and heat treatment
    Jia, Juan
    Mao, Weimin
    Raabe, Dierk
    JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEIJING, 2008, 15 (04): : 514 - 520
  • [39] Crystallization and multiple melting behavior of oriented thick lamellae in isotactic polypropylene
    Yang, Shu-Gui
    Zhang, Liang-Qing
    Zhang, Zheng-Yang
    Lei, Jun
    POLYMER, 2025, 317
  • [40] UNUSUAL RECRYSTALLIZATION AND MELTING BEHAVIOR IN DSC SCANS OF ISOTACTIC POLYPROPYLENE SAMPLES
    GUERRA, G
    DEROSA, C
    PETRACCONE, V
    TUZI, A
    JOURNAL OF THERMAL ANALYSIS, 1985, 30 (06): : 1337 - 1342
12345