Influence of Al5FeSi Phases on the Cracking of Castings at Al-Si Alloys

被引：6

作者：

Hren, I ^{[1
]}

Svobodova, J. ^{[1
]}

Michna, S. ^{[1
]}

机构：

[1] Univ JE Purkyne Usti Nad Labem, Fac Mech Engn, Inst Technol & Mat, Pasteurova 7, Usti Nad Labem 40096, Czech Republic

来源：

ARCHIVES OF FOUNDRY ENGINEERING | 2018年 / 18卷 / 04期

关键词：

Aluminium alloy; Intametallic phase; Low pressure casting; Structure; Iron contamination;

D O I：

10.24425/afe.2018.125180

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The research described in this contribution is focused on fractographic analysis of the fracture area of newly developed eutectic silumin type AlSi9NiCuMg0.5 (AA 4032), which was developed and patented by a team of staff of the Faculty of Mechanical Engineering. The paper presents determination of the cause of casting cracks in operating conditions. Fractographic analysis of the fracture area, identification of the structure of the casting, identification of structural components on the surface of the fracture surface and chemical analysis of the material in the area of refraction were performed within the experiment. Al-Si alloys with high specific strength, low density, and good castability are widely used in pressure-molded components for the automotive and aerospace industries. The results shown that the inter-media phases Fe-Al and Fe-Si in aluminium alloys lead to breakage across the entire casting section and a crack that crossed the entire cross section, which was confirmed by EDS analysis.

引用

页码：120 / 124

页数：5

共 50 条

[21] Fragmentation and dissolution of β-Al5FeSi phase during solution heat treatment of Al-13 wt% Si-Fe alloys
Villeneuve, C
Samuel, FH
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 1999, 12 (03) : 145 - 160
[22] Effect of pressure on solidification cracking susceptibility of Al-Si alloys
Liu, Jiangwei
Zeng, Pingwang
Li, Yuqiang
Kou, Sindo
SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2019, 24 (08) : 713 - 720
[23] Precipitation of β-Al5FeSi iron intermetallic in Al-6% Si-3.5% Cu (319) type alloys:: Role of Sr and P
Pennors, A
Samuel, AM
Samuel, FH
Doty, HW
TRANSACTIONS OF THE AMERICAN FOUNDRYMEN'S SOCIETY, VOL 106, 1998, 106 : 251 - 264
[24] Modification of eutectic silicon and β-Al5FeSi phases in as-cast ADC12 alloys by using samarium addition
饶远生
闫洪
胡志
JournalofRareEarths, 2013, 31 (09) : 916 - 922
[25] The Effect of the Connectivity of Rigid Phases on Strength of Al-Si Alloys
Requena, Guillermo
Garces, Gerardo
Asghar, Zahid
Marks, Esteban
Staron, Peter
Cloetens, Peter
ADVANCED ENGINEERING MATERIALS, 2011, 13 (08) : 674 - 684
[26] Modification of eutectic silicon and β-Al5FeSi phases in as-cast ADC12 alloys by using samarium addition
Rao Yuansheng
Yan Hong
Hu Zhi
JOURNAL OF RARE EARTHS, 2013, 31 (09) : 916 - 922
[27] Effect of stirring induced by rotating magnetic field on β-Al5FeSi intermetallic phases during directional solidification in AlSi alloys
Mikolajczak, P.
Ratke, L.
INTERNATIONAL JOURNAL OF CAST METALS RESEARCH, 2013, 26 (06) : 339 - 353
[28] The influence of strontium on porosity formation in Al-Si alloys
Dinnis, CM
Otte, MO
Dahle, AK
Taylor, JA
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2004, 35A (11): : 3531 - 3541
[29] The influence of strontium on porosity formation in Al-Si alloys
C. M. Dinnis
A. K. Dahle
J. A. Taylor
M. O. Otte
Metallurgical and Materials Transactions A, 2004, 35 : 3531 - 3541
[30] INFLUENCE OF REFINING TREATMENTS ON THE PROPERTIES OF Al-Si ALLOYS
Rzadkosz, S.
Zych, J.
Piekos, M.
Kozana, J.
Garbacz-Klempka, A.
Kolczyk, J.
Jamrozowicz, L.
METALURGIJA, 2015, 54 (01): : 35 - 38

← 1 2 3 4 5 →