THE FORMATION OF BRAZING SEAMS AND THE TENSILE-STRENGTH OF HIGH-TEMPERATURE BRAZING JOINTS BRAZED WITH PHOSPHORUS LOW-ALLOYED NICKEL-BASE SOLDERS

被引：0
|
作者：
LUGSCHEIDER, E
COSACK, T
机构：
[1] RWTH, Aachen, West Ger, RWTH, Aachen, West Ger
来源：
METALL | 1987年 / 41卷 / 10期
关键词：
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The silicide-phosphide nickel base high temperature brazing alloys 20. 3Cr 11. 5Si 0. 5P bal. Ni, 26. 3Cr 5. 1Si 3. 0P bal. Ni and 14. 8Cr 8. 1Si 3. 0Fe 3. 0P bal. Ni were developed from investigations in the ternary system Ni-Cr-Si. In experiments the brazeability with the base material 1. 4541 was investigated. Main topics of the investigation have been the formation of brazing seams and its effect on tensile strength.
引用
收藏
页码：998 / 1002
页数：5
相关论文
共 20 条
  • [11] Advanced Braze Alloys for Fast Epitaxial High-Temperature Brazing of Single-Crystalline Nickel-Base Superalloys
    Laux, Britta
    Piegert, Sebastian
    Roesler, Joachim
    JOURNAL OF ENGINEERING FOR GAS TURBINES AND POWER-TRANSACTIONS OF THE ASME, 2010, 132 (03): : 1 - 7
  • [12] HIGH-TEMPERATURE BRAZING OF STAINLESS-STEEL WITH LOW-PHOSPHORUS NICKEL-BASED FILLER METAL
    LUGSCHEIDER, E
    COSACK, T
    WELDING JOURNAL, 1988, 67 (10) : S215 - S221
  • [13] THERMAL AND METALLURGICAL INFLUENCES ON AISI-316 AND INCONEL-625 BY HIGH-TEMPERATURE BRAZING WITH NICKEL-BASE FILLER METALS
    LUGSCHEIDER, E
    PARTZ, KD
    LISON, R
    WELDING JOURNAL, 1982, 61 (10) : S329 - S333
  • [14] Enhancement of the high-temperature tensile creep strength of monocrystalline nickel-base superalloys by pre-rafting in compression
    Tetzlaff, U
    Mughrabi, H
    SUPERALLOYS 2000, 2000, : 273 - 282
  • [15] Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy
    Zhang, Z. P.
    Liu, J. D.
    Qiu, K. Q.
    Huang, Y. Y.
    Li, J. G.
    Wang, X. G.
    Liu, J. L.
    Wang, M.
    Zou, M. K.
    Zhou, Y. Z.
    METALS AND MATERIALS INTERNATIONAL, 2023, 29 (02) : 444 - 456
  • [16] Effects of Brazing Temperature on Microstructure and High-Temperature Strength of Joints Using a Novel Fourth-Generation Nickel-Based Single Crystal Superalloy
    Z. P. Zhang
    J. D. Liu
    K. Q. Qiu
    Y. Y. Huang
    J. G. Li
    X. G. Wang
    J. L. Liu
    M. Wang
    M. K. Zou
    Y. Z. Zhou
    Metals and Materials International, 2023, 29 : 444 - 456
  • [17] HIGH-TEMPERATURE BRAZING OF STAINLESS-STEEL WITH NICKEL-BASE FILLER METALS BNI-2, BNI-5 AND BNI-7
    LUGSCHEIDER, E
    PARTZ, KD
    WELDING JOURNAL, 1983, 62 (06) : S160 - S164
  • [18] THE EFFECT OF TENSILE-STRENGTH AND DUCTILITY ON HIGH-TEMPERATURE LOW-CYCLE FATIGUE OF CAST NI-BASE SUPERALLOYS
    ONODERA, H
    RO, Y
    YAMAGATA, T
    YAMAZAKI, M
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 (01): : 85 - 91
  • [19] THE EFFECT OF TENSILE-STRENGTH AND DUCTILITY ON HIGH-TEMPERATURE LOW-CYCLE FATIGUE OF CAST NI-BASE SUPERALLOYS
    ONODERA, H
    RO, Y
    YAMAGATA, T
    YAMAZAKI, M
    TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1986, 28 (02): : 112 - 120
  • [20] HIGH-TEMPERATURE LOW-CYCLE FATIGUE OF FRICTION WELDED JOINTS-TYPE-304-304 STAINLESS-STEEL AND ALLOY-718-718 NICKEL-BASE SUPERALLOY
    WAKAI, T
    SAKANE, M
    OHNAMI, M
    OKITA, K
    FUKUCHI, Y
    JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1993, 115 (01): : 109 - 115
12