INFLUENCE OF SOLIDIFICATION KINETICS ON ALUMINUM WELD GRAIN-REFINEMENT

被引:0
|
作者
DVORNAK, MJ
FROST, RH
OLSON, DL
机构
关键词
D O I
暂无
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
Aluminum alloy welds are often plagued by their susceptibility to hot tearing. The addition of titanium or zirconium is known to reduce the susceptibility through grain refinement. Previous models have suggested that these elements need merely to be contained as an alloy addition without concern for the form of the addition in the consumable prior to welding. The form of the titanium or zirconium addition was found to have a bearing on the effectiveness of the grain refinement addition. Results from this research revealed the intermetallic phase of the addition (TiAl3 or ZrAl3) must be present prior to welding to achieve the desired grain refinement. The solidification kinetics were also found to have a significant effect on the grain refinement achieved with the intermetallic additions.
引用
收藏
页码:S271 / S276
页数:6
相关论文
共 50 条
  • [31] EFFECT OF GRAVITY LEVEL ON GRAIN-REFINEMENT IN ALUMINUM-ALLOYS
    CAHOON, JR
    TANDON, KN
    CHATURVEDI, MC
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (12): : 3399 - 3404
  • [32] GRAIN-REFINEMENT OF ALUMINUM-ALLOY INGOT CASTINGS BY MEANS OF MELT AGITATION DURING SOLIDIFICATION USING NAPHTHALINE
    KISAKUREK, SE
    JOURNAL OF METALS, 1982, 34 (08): : 8 - 8
  • [33] INVESTIGATION OF THE INFLUENCE OF SILICON ON GRAIN-REFINEMENT OF ALUMINUM WITH ALUMINIUM-TI-TANIUM-BORON PREALLOYS
    REIF, W
    SCHNEIDER, W
    ZEITSCHRIFT FUR METALLKUNDE, 1979, 70 (06): : 396 - 399
  • [34] GRAIN-REFINEMENT OF AUSTENITIC STAINLESS-STEEL WELD BY PULSED TIG WELDING
    WATANABE, T
    NAKAMURA, H
    EI, K
    TRANSACTIONS OF NATIONAL RESEARCH INSTITUTE FOR METALS, 1987, 29 (04): : 204 - 211
  • [35] GRAIN-REFINEMENT IN UNDERCOOLED NICKEL
    LEUNG, KK
    CHIU, CP
    KUI, HW
    SCRIPTA METALLURGICA ET MATERIALIA, 1995, 32 (10): : 1559 - 1563
  • [36] NUCLEATION ASPECTS OF GRAIN-REFINEMENT
    ANDERSON, IE
    PEREPEZKO, JH
    JOURNAL OF METALS, 1982, 34 (08): : 17 - 17
  • [37] GRAIN-REFINEMENT DEPENDENCE ON THE SOLIDIFICATION AND SOLID-STATE REACTION IN ELECTROSLAG WELDS
    VENKATARAMAN, S
    DEVLETIAN, JH
    WOOD, WE
    ATTERIDGE, DG
    JOURNAL OF METALS, 1982, 34 (08): : 27 - 27
  • [38] APPLICATION OF A THERMOMECHANICAL PROCESS FOR THE GRAIN-REFINEMENT OF ALUMINUM ALLOY-7475
    LEE, EW
    MCNELLEY, TR
    MATERIALS SCIENCE AND ENGINEERING, 1987, 96 : 253 - 258
  • [39] GRAIN-REFINEMENT IN MAGNETICALLY STIRRED GTA WELDS OF ALUMINUM-ALLOYS
    PEARCE, BP
    KERR, HW
    METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1981, 12 (03): : 479 - 486
  • [40] BERYLLIUM-ENHANCED GRAIN-REFINEMENT OF ALUMINUM-TITANIUM ALLOYS
    YOUDELIS, WV
    YANG, CS
    METAL SCIENCE, 1982, 16 (06): : 275 - 281