INFLUENCE OF STRAIN ON THE ENVIRONMENTAL HYDROGEN-ASSISTED CRACKING OF A HIGH-STRENGTH STEEL IN SODIUM-CHLORIDE SOLUTION

被引：33
|
作者：
SCULLY, JR
MORAN, PJ
机构：
[1] AMER IRON & STEEL INST,WASHINGTON,DC
[2] JOHNS HOPKINS UNIV,DEPT MAT SCI & ENGN,CORROS & ELECTROCHEM RES LAB,BALTIMORE,MD 21218
来源：
CORROSION | 1988年 / 44卷 / 03期
关键词：
D O I：
10.5006/1.3583922
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
引用
收藏
页码：176 / 185
页数：10
相关论文
共 50 条
  • [21] Effect of fatigue pre-loading on mixed-mode hydrogen-assisted cracking initiation in high-strength steel
    Toribio, J
    Ovejero, E
    Khrain, V
    FATIGUE '99: PROCEEDINGS OF THE SEVENTH INTERNATIONAL FATIGUE CONGRESS, VOLS 1-4, 1999, : 2243 - 2248
  • [22] Hydrogen-Assisted Cracking in GMA Welding of High-Strength Structural Steel-A New Look into This Issue at Narrow Groove
    Schaupp, Thomas
    Schroeder, Nina
    Schroepfer, Dirk
    Kannengiesser, Thomas
    METALS, 2021, 11 (06)
  • [23] Hydrogen-assisted cracking (HAC) of high-strength steels as a function of the hydrogen pre-charging time
    Brilz, Michael
    Hoche, Holger
    Oechsner, Matthias
    ENGINEERING FRACTURE MECHANICS, 2022, 261
  • [24] HYDROGEN-ASSISTED CRACKING IN HIGH-STRENGTH TI-6AL-4V ALLOY
    MEYN, DA
    REPORT OF NRL PROGRESS, 1971, (MAR): : 16 - &
  • [25] Microstructural and crystallographic study of hydrogen-assisted cracking in high strength PSB1080 steel
    Li, Xinfeng
    Zhang, Jin
    Akiyama, Eiji
    Wang, Yanfei
    Li, Qizhen
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2018, 43 (37) : 17898 - 17911
  • [26] FORMATION OF HYDROGEN-ASSISTED INTERGRANULAR CRACKS IN HIGH-STRENGTH STEELS
    YATABE, H
    YAMADA, K
    DELOSRIOS, ER
    MILLER, KJ
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 1995, 18 (03) : 377 - 384
  • [27] Utilizing controlled hydrogen-assisted pre-cracking to assess the fracture toughness of high-strength steels
    Brilz, Michael
    Chakamnan, Anutsara
    Szabo, Meike
    Hoche, Holger
    Damyanov, Dimitar
    Klein, Marcus
    Oechsner, Matthias
    ENGINEERING FRACTURE MECHANICS, 2025, 314
  • [28] Effect of post-weld heat treatment on hydrogen-assisted cracking behavior of high-strength process pipe steel in a sour environment
    Kim, Sung Jin
    Jung, Hwan Gyo
    Kim, Kyoo Young
    SCRIPTA MATERIALIA, 2012, 67 (11) : 895 - 898
  • [29] Hydrogen-assisted cracking of quenched and tempered AISI 4135 steel in an hydroxide solution
    Verniquet, E
    Roberge, R
    Lalonde, S
    Dickson, JI
    HYDROGEN EFFECTS ON MATERIAL BEHAVIOR AND CORROSION DEFORMATION INTERACTIONS, 2003, : 577 - 586
  • [30] The dual role of shot peening in hydrogen-assisted cracking of PSI31080 high strength steel
    Li, Xinfeng
    Zhang, Jin
    Wang, Yanfei
    Ma, Mingming
    Shen, Sicong
    Song, Xiaolong
    MATERIALS & DESIGN, 2016, 110 : 602 - 615
12345