DISPERSION OF ULTRASONIC DATA AS A MEASURE OF HYGROTHERMAL EFFECTS ON FIBER-REINFORCED PLASTIC LAMINATES

被引：2
|
作者：
ISHAI, O
BARCOHEN, Y
机构：
来源：
COMPOSITES | 1980年 / 11卷 / 04期
关键词：
D O I：
10.1016/0010-4361(80)90426-7
中图分类号：
TB33 [复合材料];
学科分类号：
摘要：
In the reported experiments, destructive and non-destructive tests were carried out on three fiber-reinforced plastic composites - glass, carbon and Kevlar reinforced epoxy - under hygrothermal exposure. In all cases good correlation was found between the dispersion of ultrasonic attenuation data (measured by its coefficient of variation) and corresponding average values of strength and attenuation. Accordingy, dispersion may serve as a reliable parameter in non-destructive evaluation for detection and follow-up of hygrothermal degradation in fiber-reinforced laminates.
引用
收藏
页码：205 / 208
页数：4
相关论文
共 50 条
  • [1] NONDESTRUCTIVE EVALUATION OF HYGROTHERMAL EFFECTS ON FIBER-REINFORCED PLASTIC LAMINATES
    COHEN, YB
    MERON, M
    ISHAI, O
    JOURNAL OF TESTING AND EVALUATION, 1979, 7 (05) : 291 - 296
  • [2] ULTRASONIC EVALUATION OF THIN, FIBER-REINFORCED LAMINATES
    VEIDT, M
    SACHSE, W
    JOURNAL OF COMPOSITE MATERIALS, 1994, 28 (04) : 329 - 342
  • [3] ON THE MACHINING OF FIBER-REINFORCED PLASTIC (FRP) COMPOSITE LAMINATES
    BHATNAGAR, N
    RAMAKRISHNAN, N
    NAIK, NK
    KOMANDURI, R
    INTERNATIONAL JOURNAL OF MACHINE TOOLS & MANUFACTURE, 1995, 35 (05): : 701 - 716
  • [4] Optimal Strength Design for Fiber-Metal Laminates and Fiber-reinforced Plastic Laminates
    Peng, Wenjie
    Chen, Jianqiao
    Wei, Junhong
    Tu, Wenqiong
    JOURNAL OF COMPOSITE MATERIALS, 2011, 45 (02) : 237 - 254
  • [5] Rotary ultrasonic machining of carbon fiber-reinforced plastic composites: effects of ultrasonic frequency
    Wang, Hui
    Hu, Yingbin
    Cong, Weilong
    Burks, Anthony R.
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2019, 104 (9-12): : 3759 - 3772
  • [6] FAILURE PREDICTION OF FIBER-REINFORCED LAMINATES UNDER HYGROTHERMAL AND MECHANICAL INPLANE LOADS
    PHILIPPIDIS, TP
    THEOCARIS, PS
    ADVANCES IN POLYMER TECHNOLOGY, 1993, 12 (03) : 271 - 279
  • [7] HYGROTHERMAL EFFECTS ON THE MECHANICAL-BEHAVIOR OF GRAPHITE FIBER-REINFORCED EPOXY LAMINATES BEYOND INITIAL FAILURE
    ISHAI, O
    GARG, A
    NELSON, HG
    COMPOSITES, 1986, 17 (01): : 23 - 32
  • [8] Effects of fiber orientations on fracture mechanisms in rotary ultrasonic drilling of carbon fiber reinforced plastic laminates
    Lv, Dongxi
    Shi, Pengcheng
    Chen, Mingda
    Liu, Dong
    Chen, Gang
    Zhu, Yingdan
    Ali, Imran
    JOURNAL OF MANUFACTURING PROCESSES, 2023, 105 : 199 - 212
  • [9] Review of Hygrothermal Effects on Carbon Fiber-reinforced Composite Materials
    Jin, Ping
    Wang, De
    Tan, Xiaoming
    MECHATRONICS AND INTELLIGENT MATERIALS II, PTS 1-6, 2012, 490-495 : 3611 - 3615
  • [10] EFFECT OF HYGROTHERMAL HISTORY ON RESIDUAL STRENGTH OF GLASS-FIBER REINFORCED PLASTIC LAMINATES
    ISHAI, O
    ARNON, U
    JOURNAL OF TESTING AND EVALUATION, 1977, 5 (04) : 320 - 326
12345