NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION IN ULTRAHIGH STRENGTH STEEL - INFLUENCE OF LOAD RATIO AND CYCLIC STRENGTH

被引：104

作者：

RITCHIE, RO ^{[1
]}

机构：

[1] MIT, DEPT MECH ENGN, CAMBRIDGE, MA 02139 USA

来源：

JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME | 1977年 / 99卷 / 03期

关键词：

D O I：

10.1115/1.3443519

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

引用

下载

页码：195 / 204

页数：10

共 50 条

[31] NEAR-THRESHOLD CHARACTERISTICS IN FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL UNDER HYDROGEN SUPPLY.
Nakajima, Masaki
Kato, Yozo
Nakamura, Kazushi
Zairyo/Journal of the Society of Materials Science, Japan, 1986, 35 (389) : 190 - 195
[32] Mechanisms and modeling of near-threshold fatigue crack propagation
Petit, J
Henaff, G
Sarrazin-Baudoux, C
FATIGUE CRACK GROWTH THRESHOLDS, ENDURANCE LIMITS, AND DESIGN, 2000, 1372 : 3 - 30
[33] INFLUENCE OF STRENGTH ON NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION IN AIR AND HYDROGEN GAS IN QUENCHED AND TEMPERED 2 1/4CR-1MO STEEL(SA542-2)
ZAMISKI, GF
RITCHIE, RO
JOURNAL OF METALS, 1979, 31 (08): : F61 - F61
[34] NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION OF HY80 AND HY130 STEELS
HORNG, JL
FINE, ME
JOURNAL OF METALS, 1983, 35 (08): : A35 - A36
[35] MICRO CLEAVAGE CRACKING DURING FATIGUE CRACK-PROPAGATION IN LOW STRENGTH STEEL
RITCHIE, RO
KNOTT, JF
MATERIALS SCIENCE AND ENGINEERING, 1974, 14 (01): : 7 - 14
[36] MICROSTRUCTURAL EFFECTS AND CRACK CLOSURE DURING NEAR THRESHOLD FATIGUE CRACK PROPAGATION IN A HIGH STRENGTH STEEL.
Ravichandran, K.S.
Venkata Rao, H.C.
Dwarakadasa, E.S.
Nair, C.G.Krishnadas
Metallurgical transactions. A, Physical metallurgy and materials science, 1987, 18 A (05): : 865 - 876
[37] THE EFFECT OF SHEET THICKNESS ON NEAR-THRESHOLD FATIGUE CRACK-PROPAGATION AND OXIDE AND ROUGHNESS-INDUCED CRACK CLOSURE
TOKAJI, K
ANDO, Z
NAGAE, K
JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY-TRANSACTIONS OF THE ASME, 1987, 109 (01): : 86 - 91
[38] FATIGUE CRACK-PROPAGATION IN UNPLASTICIZED POLYVINYL-CHLORIDE) (UPVC) .2. NEAR-THRESHOLD FATIGUE CRACK-GROWTH
KIM, HS
MAI, YW
COTTERELL, B
POLYMER, 1988, 29 (02) : 277 - 285
[39] INFLUENCE OF GASEOUS ENVIRONMENT ON FATIGUE CRACK GROWTH IN AN ULTRAHIGH STRENGTH STEEL
TOPLOSKY, J
RITCHIE, RO
JOURNAL OF METALS, 1980, 32 (12): : 29 - 29
[40] Fatigue crack closure in the near-threshold level in a high-strength low-alloy structural steel
Dhar, S., 1600, (11):

← 1 2 3 4 5 →