A DAMAGE MECHANICS MODEL OF FATIGUE CRACK INITIATION IN NOTCHED PLATES

被引：32
|
作者：
CHOW, CL [1 ]
WEI, Y [1 ]
机构：
[1] UNIV HONG KONG,DEPT MECH ENGN,HONG KONG,HONG KONG
来源：
THEORETICAL AND APPLIED FRACTURE MECHANICS | 1991年 / 16卷 / 02期
关键词：
D O I：
10.1016/0167-8442(91)90029-J
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A damage model is proposed to characterize fatigue crack initiation in notched plates. This is accomplished by assuming a damage fracture criterion and effective instantaneous tangent moduli matrix which accounts for damage accumulation. A finite element package is used to perform the numerical analyses for an edge-notched plate specimen made of Al alloy 2024-T3 under cyclic loading of varying constant amplitudes. The estimated fatigue crack initiation life agrees satisfactorily with those determined experimentally. An important observation from the results of the proposed damage model is its ability to identify the phenomenon of stress redistribution due to material degradation in two-dimension specimens during fatigue loading.
引用
下载
收藏
页码：123 / 133
页数：11
相关论文
共 50 条
  • [1] FATIGUE LIMITS OF CRACK INITIATION AND PROPAGATION AT NOTCHED PLATES
    LEE, KY
    LEE, TS
    ENGINEERING FRACTURE MECHANICS, 1986, 25 (01) : 111 - 114
  • [2] Influence of laser peening on fatigue crack initiation of notched aluminum plates
    Granados-Alejo, Vignaud
    Rubio-Gonzalez, Carlos
    Parra-Torres, Yazmin
    Antonio Banderas, J.
    Gomez-Rosas, Gilberto
    STRUCTURAL ENGINEERING AND MECHANICS, 2017, 62 (06) : 739 - 748
  • [3] Effects of initial overload on the fatigue crack initiation and growth in notched plates
    Seifi, Rahman
    Mohammadi, Mohammad R.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2024, 131
  • [4] Continuum damage mechanics analysis of fatigue crack initiation
    Johns Hopkins Univ, Baltimore, United States
    Int J Fatigue, 9 (631-639):
  • [5] Continuum damage mechanics analysis of fatigue crack initiation
    Bhattacharya, B
    Ellingwood, B
    INTERNATIONAL JOURNAL OF FATIGUE, 1998, 20 (09) : 631 - 639
  • [6] FATIGUE CRACK INITIATION IN NOTCHED SPECIMENS
    JACK, AR
    SCRIPTA METALLURGICA, 1971, 5 (08): : 721 - &
  • [7] Fatigue strength and fatigue crack initiation of steel notched plates under cyclic and random loading
    Tchankov, DS
    Ohta, A
    Suzuki, N
    Maeda, Y
    ECF 12: FRACTURE FROM DEFECTS, VOLS. I-III, 1998, : 277 - 282
  • [8] Method for Predicting Crack Initiation Life of Notched Specimen Based on Damage Mechanics
    Liu J.
    Wei Y.
    Yan C.
    Lang S.
    Journal of Shanghai Jiaotong University (Science), 2018, 23 (2) : 286 - 290
  • [9] Stochastic fatigue crack initiation based on continuum damage mechanics
    Bhattacharya, B
    Ellingwood, BR
    STRUCTURAL SAFETY AND RELIABILITY, VOLS. 1-3, 1998, : 1235 - 1242
  • [10] Fatigue Crack Initiation and Extension Regularity Based on Damage Mechanics
    Sun Z.
    Chai X.
    Liu X.
    Wang J.
    Cailiao Daobao/Materials Review, 2017, 31 (04): : 130 - 134
12345